In situ melt electrospun polycaprolactone/Fe3O4 nanofibers for magnetic hyperthermia.

Magnetic fibrous membrane used to generate heat under the alternating magnetic field (AMF) has attracted wide attention due to their application in magnetic hyperthermia. However, there is not magnetic fibrous membrane prepared by melt electrospinning (e-spinning) which is a solvent-free, bio-friendly technology. In this work, polycaprolactone (PCL)/Fe3O4 fiber membrane was prepared by melt e-spinning and using homemade self-powered portable melt e-spinning apparatus. The hand-held melt e-spinning apparatus has a weight of about 450 g and a precise size of 24 cm in length, 6 cm in thickness and 13 cm in height, which is more portable for widely using in the medical field. The PCL/Fe3O4 composite fibers with diameters of 4-17 µm, are very uniform. In addition, the magnetic composite fiber membrane has excellent heating efficiency and thermal cycling characteristics. The results indicated that self-powered portable melt e-spinning apparatus and PCL/Fe3O4 fiber membrane may provide an attractive way for hyperthermia therapy.

Bubble Melt Electrospinning for Production of Polymer Microfibers.

In this paper, we report an interesting bubble melt electrospinning (e-spinning) to produce polymer microfibers. Usually, melt e-spinning for fabricating ultrafine fibers needs "Taylor cone", which is formed on the tip of the spinneret. The spinneret is also the bottleneck for mass production in melt e-spinning. In this work, a metal needle-free method was tried in the melt e-spinning process. The "Taylor cone" was formed on the surface of the broken polymer melt bubble, which was produced by an airflow. With the applied voltage ranging from 18 to 25 kV, the heating temperature was about 210⁻250 °C, and polyurethane (TPU) and polylactic acid (PLA) microfibers were successfully fabricated by this new melt e-spinning technique. During the melt e-spinning process, polymer melt jets ejected from the burst bubbles could be observed with a high-speed camera. Then, polymer microfibers could be obtained on the grounded collector. The fiber diameter ranged from 45 down to 5 µm. The results indicate that bubble melt e-spinning may be a promising method for needleless production in melt e-spinning.