ABSTRACT
As an admixture of cement-based materials, the reaction of fly ash (FA) usually takes place in the late age of curing, so FA will affect the self-healing ability of long-age cement-based materials. The self-healing potential and the characteristics of self-healing products of cementitious materials before and after crack healing were analyzed by microscopic tests, and the mechanism of the effect of fly ash on the self-healing performance of cementitious materials was revealed. The results showed that the increase in fly ash content promoted the improvement of the self-repair performance of cracked specimens at 28 d, especially when the fly ash dosage was 40%, the crack opened after 30 d of healing in water was completely closed, the UPV value after recovery was close to 3000 m/s, the self-repair efficiency of maximum amplitude and main frequency amplitude was up to more than 60%, and the recovery rate of compressive strength was increased to more than 30%. However, the increase in fly ash content was not conducive to the self-repair of cracked samples at 210 d, and with the increase in fly ash content, the crack closure effect weakened, the UPV value after recovery decreased, the crack repair rate based on ultrasonic transmission decreased to about 20%, and the compressive strength recovery rate increased slightly. In addition, calcium carbonate precipitation was the main repair product of crack filling and healing, including calcite and spherulite. With the increase in fly ash content, the content of element C in the self-repair products of 28-day-old specimens gradually increased, and the size of calcium carbonate crystals gradually decreased, but the filling was denser, whereas the calcium carbonate crystals in the self-repair products of 210 d specimens gradually became fine and loose.
ABSTRACT
Cement-based materials are susceptible to internal cracks during service, leading to a reduction in their durability. Microcapsules can effectively self-repair cracks in cement-based materials. In this study, novel electromagnetic-induced rupture microcapsules (DWMs) were prepared by using the melt dispersion method with Fe3O4 nano-particles/polyethylene wax as the shell and epoxy resin as the repairing agent. The core fraction, compactness, particle size distribution, morphology, and chemical structure of DWMs were characterized. DWMs were subsequently incorporated into the mortar to measure the pore size distribution, compressive strength recovery, and maximum amplitudes of the pre-damaged mortar after self-repairing. DWMs were also evaluated for their ability to self-repair cracks on mortar surfaces. The results showed that the core fraction, remaining weight (30 days), and mean size of DWMs were 72.5%, 97.6 g, and 220 µm, respectively. SEM showed that the DWMs were regular spherical with a rough surface and could form a good bond with cement matrix. FTIR indicated that the epoxy resin was successfully encapsulated in the Fe3O4 nano-particles/polyethylene wax. After 15 days of self-repairing, the harmful pore ratio, compressive strength recovery, and maximum amplitude of the pre-damaged mortars were 48.97%, 91.9%, and 24.03 mV, respectively. The mortar with an initial crack width of 0.4-0.5 mm was self-repaired within 7 days. This indicated that the incorporation of DWMs can improve the self-repair ability of the mortar. This work is expected to provide new insights to address the mechanism of microcapsule rupture in self-repairing cement-based materials.
ABSTRACT
With the construction of projects under severe environments, new and higher requirements are put forward for the properties of concrete, especially the autogenous self-sealing property, which is greatly affected by the curing environment and the state of the water. Herein, six types of curing conditions, including in air with a relative humidity of 30%, 60%, and 95%; flowing water; wet-dry cycles; and static water, are designed to investigate the autogenous self-sealing of mortar under different curing conditions. The results showed that the self-sealing ratios are higher than 60% and the cracks are closed for the mortar undergoing the wet-dry cycles and the static water. However, the self-sealing ratios of mortar are lower than 10% and the cracks are almost unchanged when the mortar is cured in the air with a relative humidity (RH) of 30% and 60%. The static liquid water is more conducive to the continued hydration of cement and the formation of CaCO3 than the flowing water. The research provides guidance for the design of concrete and the improvement of autogenous self-sealing when the concrete serves in different environments.
ABSTRACT
Overgrinding of Portland cement brings excessive shrinkage and poor self-healing ability to concrete. In this paper, through the ultrasonic test and optical micrograph observation, the self-healing properties of concrete prepared by cement with different particle size distributions were studied. Besides, the effect of carbonation and continued hydration on self-healing of concrete was analyzed. Results show that, for the Portland cement containing more particles with the size 30~60 µm, the concrete could achieve a better self-healing ability of concrete at 28 days. For the two methods to characterize the self-healing properties of concrete, the ultrasonic test is more accurate in characterizing the self-healing of internal crack than optical micrograph observation. The autogenous self-healing of concrete is jointly affected by the continued hydration and carbonation. At 7 days and 30 days, the autogenous self-healing of concrete is mainly controlled by the continued hydration and carbonation, respectively. The cement particle size could affect the continued hydration by affecting un-hydrated cement content and the carbonation by affecting the Ca(OH)2 content. Therefore, a proper distribution of cement particle size, which brings a suitable amount of Ca(OH)2 and un-hydrated cement, could improve the self-healing ability of concrete.