Unique design approach to realize an O-band laser monolithically integrated on 300†mm Si substrate by nano-ridge engineering.

We introduce a new design space for optimizing III-V devices monolithically grown on Silicon substrates by extending the concept of nano-ridge engineering from binary semiconductors such as GaAs, InAs and GaSb to the ternary alloy InGaAs. This allows controlling the fundamental lattice constant of the fully relaxed ternary nano-ridge which thereby serves as a tunable base for the integration of diverse device hetero-layers. To demonstrate the flexibility of this approach, we realized an O-band nano-ridge laser containing three In0.45Ga0.55As quantum wells, which are pseudomorphically strained to an In0.25Ga0.75As nano-ridge base. The demonstration of an optically pumped nano-ridge laser operating around 1300 nm underlines the potential of this cost-efficient and highly scalable integration approach for silicon photonics.

Ferroelectric-Driven Exciton and Trion Modulation in Monolayer Molybdenum and Tungsten Diselenides.

In this work, we show how domain-engineered lithium niobate can be used to selectively dope monolayer molybdenum selenide (MoSe2) and tungsten selenide (WSe2) and demonstrate that these ferroelectric domains can significantly enhance or inhibit photoluminescence (PL), with the most dramatic modulation occurring at the heterojunction interface between two domains. A micro-PL and Raman system is used to obtain spatially resolved images of the differently doped transition metal dichalcogenides (TMDs). The domain-inverted lithium niobate causes changes in the TMDs due to electrostatic doping as a result of the remnant polarization from the substrate. Moreover, the differently doped TMDs (n-type MoSe2 and p-type WSe2) exhibit opposite PL modulation. Distinct oppositely charged domains were obtained with a 9-fold PL enhancement for the same single MoSe2 sheet when adhered to the positive (P+) and negative (P-) domains. This sharp PL modulation on the ferroelectric domain results from different free electron or hole concentrations in the material's conduction band or valence band. Moreover, excitons dissociate rapidly at the interface between the P+ and P- domains due to the built-in electric field. We are able to adjust the charge on the P+ and P- domains using temperature via the pyroelectric effect and observe rapid PL quenching over a narrow temperature range, illustrating the observed PL modulation is electronic in nature. This observation creates an opportunity to harness the direct bandgap TMD 2D materials as an active optical component for the lithium niobate platform using domain engineering of the lithium niobate substrate to create optically active heterostructures that could be used for photodetectors or even electrically driven optical sources on-chip.