ABSTRACT
Adhesion of carbon nanotube (CNT) onto a cathode substrate is very crucial for field electron emitters that are operating under high electric fields. As a supporting precursor of CNT field emitters, we adopted silicon carbide (SiC) nano-particle fillers with Ni particles and then enhanced interfacial reactions onto Kovar-alloy substrates through the optimized wet pulverization process of SiC aggregates for reliable field electron emitters. As-purchased SiC aggregates were efficiently pulverized from 20 to less than 1 micro-meter in a median value (D50). CNT pastes for field emitters were distinctively formulated by a mixing process of the pulverized SiC aggregates and pre-dispersed CNTs. X-ray photoelectron spectroscopy studies showed that the optimally pulverized SiC-CNT paste-emitter had a stronger Si 2p3/2 signal in the Ni2Si phase than the as-purchased one. The Si 2p3/2 signal would represent interfacial reaction of the SiC nano-particle onto Ni from the CNT paste and the Kovar substrate, forming the supporting layer for CNT emitters. The optimal paste-emitter even in a vacuum-sealed tube exhibited a highly reliable field emission current with a high current density of 100 mA cm-2 for over 50 h along with good reproducibility. The enhanced interfacial reaction of SiC filler onto the metal substrates could lead to highly reliable field electron emitters for vacuum electronic devices.
ABSTRACT
The field emission properties of boron nitride nanotube (BNNT) field emitters according to vacuum pressure were demonstrated. During the short-term emission operation, the field emission behaviors were almost similar, regardless of the vacuum pressure, even though the turn-on electric field of the BNNT field emitter was slightly increased as the vacuum pressure increased. On the other hand, during the long-term emission operation, both the degradation and fluctuations of the emission current of the BNNT field emitters were dramatically increased as the vacuum pressure increased. The degradation of field emission properties of the BNNT emitters according to vacuum pressure is mainly attributed to the ion bombardment effect, rather than the oxidation effect. The field emission behavior under Ar ambient also strongly demonstrates that the degradation and the fluctuation of the emission current are largely dependent on the ion bombardment effect.
ABSTRACT
Carbon nanotube (CNT) paste emitters were fabricated using graphite nanopowder filler. The CNT paste emitters consist of CNTs as the emitting material, graphite nanopowder as the filler and a graphite rod as the cathode. Rather than metal or inorganic materials, graphite nanopowder was adapted as a filler material to make the CNT paste emitters. After fabricating the emitters, sandpaper treatment was applied to increase the density of emission sites. The CNT paste emitters showed a high field emission performance, for example a high emission current of 8.5 mA from a cylindrical emitter with a diameter of 0.7 mm (corresponding to a current density of 2.2 A cm-2) and an extremely stable emission current at 1 mA (260 mA cm-2 for 20 h). Interestingly, after a number of electrical arcing events, the emitters still showed a high emission current of 5-8 mA (higher than 1 A cm-2). In addition to the sound electrical and thermal properties of the graphite filler, effective mechanical adhesion of the CNTs onto the graphite cathode induced by the use of the graphite nanopowder filler contributed the excellent field emission properties of the CNT paste emitters.
ABSTRACT
Boron nitride nanotubes (BNNTs) have attracted considerable attention as a field emission material because of their high mechanical strength, high negative electron affinity, and high oxidation resistance. Nevertheless, the obtained field-emission properties of BNNTs have indicated poor emission performance, which is a very high turn-on electric field with a low emission current. We fabricated BNNT field emitters and investigated their field-emission properties. The field-emission properties of the BNNT field emitters were considerably enhanced compared to those of other BN nanomaterial-based field emitters. The turn-on and the threshold electric fields of the BNNT field emitter were 3.1 and 5.4 V/µm at the gap distance of 750 µm, respectively. Both the turn-on and the threshold electric fields of the BNNT field emitters were decreased by increasing the gap distance between the emitter tip and the anode electrode. Degradation of the emission current during field emission operation for 20 h showed no significant difference according to the gap distance. Emission current fluctuation of the BNNT field emitters showed that the smaller gap was more unstable than the larger gap. The enhanced emission properties are mainly attributed to the small diameter, high-quality, and straight structure of BNNTs as well as the stable network formation of the BNNT film with good mechanical and electrical contact between the BNNTs and the cathode electrode. The remarkable emission performance of the BNNT field emitters might have promising applications for various field-emission devices.