ABSTRACT
The article presents an experimental study of an issue of whether the formation of arrays of Ge quantum dots on the Si(001) surface is an equilibrium process or it is kinetically controlled. We deposited Ge on Si(001) at the room temperature and explored crystallization of the disordered Ge film as a result of annealing at 600 °C. The experiment has demonstrated that the Ge/Si(001) film formed in the conditions of an isolated system consists of the standard patched wetting layer and large droplike clusters of Ge rather than of huts or domes which appear when a film is grown in a flux of Ge atoms arriving on its surface. We conclude that the growth of the pyramids appearing at temperatures greater than 600 °C is controlled by kinetics rather than thermodynamic equilibrium whereas the wetting layer is an equilibrium structure. PACS: Primary 68.37.Ef; 68.55.Ac; 68.65.Hb; 81.07.Ta; 81.16.Dn.
ABSTRACT
: Nickel silicide Schottky diodes formed on polycrystalline Si ãPã films are proposed as temperature sensors of monolithic uncooled microbolometer infrared focal plane arrays. The structure and composition of nickel silicide/polycrystalline silicon films synthesized in a low-temperature process are examined by means of transmission electron microscopy. The Ni silicide is identified as a multi-phase compound composed of 20% to 40% of Ni3Si, 30% to 60% of Ni2Si, and 10% to 30% of NiSi with probable minor content of NiSi2 at the silicide/poly-Si interface. Rectification ratios of the Schottky diodes vary from about 100 to about 20 for the temperature increasing from 22â"ƒ to 70â"ƒ; they exceed 1,000 at 80 K. A barrier of around 0.95 eV is found to control the photovoltage spectra at room temperature. A set of barriers is observed in photo-electromotive force spectra at 80 K and attributed to the Ni silicide/poly-Si interface. Absolute values of temperature coefficients of voltage and current are found to vary from 0.3%â"ƒ to 0.6%/â"ƒ for forward bias and around 2.5%/â"ƒ for reverse bias of the diodes.
ABSTRACT
: Issues of Ge hut cluster array formation and growth at low temperatures on the Ge/Si(001) wetting layer are discussed on the basis of explorations performed by high resolution STM and in-situ RHEED. Dynamics of the RHEED patterns in the process of Ge hut array formation is investigated at low and high temperatures of Ge deposition. Different dynamics of RHEED patterns during the deposition of Ge atoms in different growth modes is observed, which reflects the difference in adatom mobility and their 'condensation' fluxes from Ge 2D gas on the surface for different modes, which in turn control the nucleation rates and densities of Ge clusters. Data of HRTEM studies of multilayer Ge/Si heterostructures are presented with the focus on low-temperature formation of perfect films.Heteroepitaxial Si p-i-n-diodes with multilayer stacks of Ge/Si(001) quantum dot dense arrays built in intrinsic domains have been investigated and found to exhibit the photo-emf in a wide spectral range from 0.8 to 5 µm. An effect of wide-band irradiation by infrared light on the photo-emf spectra has been observed. Photo-emf in different spectral ranges has been found to be differently affected by the wide-band irradiation. A significant increase in photo-emf is observed in the fundamental absorption range under the wide-band irradiation. The observed phenomena are explained in terms of positive and neutral charge states of the quantum dot layers and the Coulomb potential of the quantum dot ensemble. A new design of quantum dot infrared photodetectors is proposed.By using a coherent source spectrometer, first measurements of terahertz dynamical conductivity (absorptivity) spectra of Ge/Si(001) heterostructures were performed at frequencies ranged from 0.3 to 1.2 THz in the temperature interval from 300 to 5 K. The effective dynamical conductivity of the heterostructures with Ge quantum dots has been discovered to be significantly higher than that of the structure with the same amount of bulk germanium (not organized in an array of quantum dots). The excess conductivity is not observed in the structures with the Ge coverage less than 8 Å. When a Ge/Si(001) sample is cooled down the conductivity of the heterostructure decreases.
ABSTRACT
Issues of morphology, nucleation, and growth of Ge cluster arrays deposited by ultrahigh vacuum molecular beam epitaxy on the Si(001) surface are considered. Difference in nucleation of quantum dots during Ge deposition at low (â²600°C) and high (â³600°C) temperatures is studied by high resolution scanning tunneling microscopy. The atomic models of growth of both species of Ge huts--pyramids and wedges-- are proposed. The growth cycle of Ge QD arrays at low temperatures is explored. A problem of lowering of the array formation temperature is discussed with the focus on CMOS compatibility of the entire process; a special attention is paid upon approaches to reduction of treatment temperature during the Si(001) surface pre-growth cleaning, which is at once a key and the highest-temperature phase of the Ge/Si(001) quantum dot dense array formation process. The temperature of the Si clean surface preparation, the final high-temperature step of which is, as a rule, carried out directly in the MBE chamber just before the structure deposition, determines the compatibility of formation process of Ge-QD-array based devices with the CMOS manufacturing cycle. Silicon surface hydrogenation at the final stage of its wet chemical etching during the preliminary cleaning is proposed as a possible way of efficient reduction of the Si wafer pre-growth annealing temperature.
ABSTRACT
The Si(001) surface deoxidized by short annealing at T ~ 925°C in the ultrahigh vacuum molecuar beam epitaxy chamber has been in situ investigated using high-resolution scanning tunneling microscopy (STM)and redegreesected high-energy electron diffraction (RHEED. RHEED patterns corresponding to (2 × 1) and (4 × 4) structures were observed during sample treatment. The (4 × 4) reconstruction arose at T â² 600°C after annealing. The reconstruction was observed to be reversible: the (4 × 4) structure turned into the (2 × 1) one at T â³ 600°C, the (4 × 4) structure appeared again at recurring cooling. The c(8 × 8) reconstruction was revealed by STM at room temperature on the same samples. A fraction of the surface area covered by the c(8 × 8) structure decreased, as the sample cooling rate was reduced. The (2 × 1) structure was observed on the surface free of the c(8 × 8) one. The c(8 × 8) structure has been evidenced to manifest itself as the (4 × 4) one in the RHEED patterns. A model of the c(8 × 8) structure formation has been built on the basis of the STM data. Origin of the high-order structure on the Si(001) surface and its connection with the epinucleation phenomenon are discussed.PACS 68.35.B-·68.37.Ef·68.49.Jk·68.47.Fg.
ABSTRACT
We report a direct observation of Ge hut nucleation on Si(001) during UHV molecular beam epitaxy at 360°C. Nuclei of pyramids and wedges were observed on the wetting layer (WL) (M × N) patches starting from the coverage of 5.1 Å and found to have different structures. Atomic models of nuclei of both hut species have been built as well as models of the growing clusters. The growth of huts of each species has been demonstrated to follow generic scenarios. The formation of the second atomic layer of a wedge results in rearrangement of its first layer. Its ridge structure does not repeat the nucleus. A pyramid grows without phase transitions. A structure of its vertex copies the nucleus. Transitions between hut species turned out to be impossible. The wedges contain point defects in the upper corners of the triangular faces and have preferential growth directions along the ridges. The derived structure of the {105} facet follows the paired dimer model. Further growth of hut arrays results in domination of wedges, and the density of pyramids exponentially drops. The second generation of huts arises at coverages >10 Å; new huts occupy the whole WL at coverages ~14 Å. Nanocrystalline Ge 2D layer begins forming at coverages >14 Å.