1.
Nanotechnology ; 28(19): 194003, 2017 May 12.
Article in English | MEDLINE | ID: mdl-28332486

ABSTRACT

In this work, we propose a new method for the large-scale production of flexible, periodic alumina arrays with well-ordered pores. We show the incorporation of pre-patterning based on polystyrene (PS) nanosphere lithography into an aluminium anodization process. We prepared ordered monolayers of PS spheres with average diameters of (510 ± 10) nm and (430 ± 10) nm on a large area (1.5 × 1.5 cm2) of the Si substrate. Next, we deposited a 5 µm aluminium layer on arrays of PS nanospheres using the sputtering technique. After the deposition, we covered the aluminium film with a polymer Scotch adhesive tape, and separated it from the silicon substrate by ultrasonic-assisted lift-off. Finally, we performed the anodization of the aluminium. We compared the pore and cell sizes, and the pore distance for the templates obtained by this technique, with reference to the templates prepared by a two-step anodization process. Using this new approach, we obtained highly ordered hexagonal 2D lattices over a large area of up to 2 cm2 with sparse defects, amounting to not more than four defects per 1000 µm2 on average. Here, we show that the use of indentation techniques is not necessary and can be replaced by a fast, cheap and easy pre-patterning step based on nanosphere lithography.

2.
Nanotechnology ; 26(42): 425301, 2015 Oct 23.
Article in English | MEDLINE | ID: mdl-26422608

ABSTRACT

Ordered FePdCu nanoisland arrays were formed by annealing at 600 °C, which caused solid state dewetting of [Cu/Fe/Pd] multilayers deposited on self-assembled SiO2 nanospheres with a size of 100 nm. A single FePdCu island was formed on the top of each SiO2 nanosphere. The structure of the obtained system was studied by x-ray diffraction (XRD), while its magnetic properties were studied by SQUID magnetometry. A partially ordered L10 alloy appeared in the annealed films, leading to magnetic hardening of the material. The paper presents the influence of the patterning on the system properties. It is shown that templated dewetting is a method providing nanoislands with well-controlled sizes and positions. The role of copper admixture in controlling the structural and magnetic properties is also discussed.