Investigation of Thermal Properties of Zr-Based Metallic Glass-Polymer Composite with the Addition of Silane.

Composites based on Zr65Cu17.5Ni10Al7.5/PTFE (polytetrafluoroethylene) with silane were prepared by ball milling with subsequent thermal pressing. Silanization was performed in the alcoholic solution with metallic glass powder. Different composites, 30/70 and 50/50 with silane, were prepared. During ball milling, Zr2Cu and Zr2Ni intermetallic phases were formed. The Zr-based metallic glass had a large supercooled region, and the melting point of the 30/70 and 50/50 composites with silane was near to the melting point of PTFE. The 50/50 composite (silane) had the highest thermal conductivity compared to the 30/70 composite samples. The incorporation of silane in metallic glass/polymer was investigated by Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscope (SEM) analysis. Thermogravimetric analysis (TGA) showed the thermal stability of the composite samples up to 450-460 °C. It was also concluded that the 50/50 composite with silane has better thermal stability than the 30/70 composite with silane. The addition of silane in 30/70 and 50/50 composites increased the thermal conductivity compared to the composites without silane.

Hydrogen storage performance of the multi-principal-component CoFeMnTiVZr alloy in electrochemical and gas-solid reactions.

The single-phase multi-principal-component CoFeMnTiVZr alloy was obtained by rapid solidification and examined by a combination of electrochemical methods and gas-solid reactions. X-ray diffraction and high-resolution transmission electron microscopy analyses reveal a hexagonal Laves-phase structure (type C14). Cyclic voltammetry and electrochemical impedance spectroscopy investigations in the hydrogen absorption/desorption region give insight into the absorption/desorption kinetics and the change in the desorption charge in terms of the applied potential. The thickness of the hydrogen absorption layer obtained by the electrochemical reaction is estimated by high-resolution transmission electron microscopy. The electrochemical hydrogen storage capacity for a given applied voltage is calculated from a series of chronoamperometry and cyclic voltammetry measurements. The selected alloy exhibits good stability for reversible hydrogen absorption and demonstrates a maximum hydrogen capacity of ∼1.9 wt% at room temperature. The amount of hydrogen absorbed in the gas-solid reaction reaches 1.7 wt% at 298 K and 5 MPa, evidencing a good correlation with the electrochemical results.