ABSTRACT
The structural, morphological, and optical properties of Ni2+ ions substitution in CoCr2O4 matrix as ceramic pigments were investigated. The thermal decomposition of the dried gel was performed aiming to understand the mass changes during annealing. The X-ray diffraction (XRD) studies reveal a spinel-type Face-Centered Cubic structure and a secondary Cr2O3 phase when x ≤ 0.75 and a Body-Centered Tetragonal structure when x = 1. Fourier Transform Infrared Spectroscopy (FT-IR) indicated two strong absorption bands corresponding to the metal-oxygen stretching from tetrahedral and octahedral sites, characteristic of spinel structure. Ultraviolet-Visible (UV-Vis) spectra exhibited the electronic transitions of the Cr2+ Cr3+ and Ni2+ ions. From the UV-Vis data, the CIE color coordinates, (x, y) of the pigments were evaluated. The morphology was examined by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) showing the agglomeration behavior of the particles. The stability, coloring properties and potential ceramic applications of studied pigments were tested by their incorporation in matte and glossy tile glazes followed by the application of obtained glazes on ceramic tiles. This study highlights the change in pigment color (from turquoise to a yellowish green) with Ni2+ ions substitution in the CoCr2O4 spinel matrix.
ABSTRACT
MnO2-lead materials have attracted attention in their applications as electrodes. This work reports a detailed spectroscopic study of the compositional variation of MnO2-xLead vitroceramic materials with varied Pb contents. The concentration variation of lead and manganese ions issystematically characterized throughthe analysis of X-ray diffraction (XRD), Fourier transform infrared (FTIR), ultraviolet-visible (UV-Vis), and electron paramagnetic resonance (EPR) spectroscopy.The MnO2-xLead samples consist of a vitroceramic structure with Pb, PbO, PbO2,and Mn3O4 crystalline phases. The introduction of higher Pb content in the host vitroceramic reveals the [PbO6]â[PbOn] conversion, where n = 3, 4, and the formation of distorted [MnO6] octahedral units. The UV-Vis data of the samples possess the intense bands between 300 and 500 nm, which are due to the presence of divalent lead ions (320 nm) and divalent and trivalent manganese ions (420 and 490 nm, respectively) in the structure of glass ceramics. The EPR data show resonance lines located around g ~ 8 and 4.3, and a sextet hyperfine structure at g ~ 2, which isascribed to the Mn+3 and Mn+2 ions.