ABSTRACT
Wire electrical discharge machining (WEDM) is an unconventional machining technology that can be used to machine materials with minimum electrical conductivity. The technology is often employed in the automotive industry, as it makes it possible to produce mold parts of complex shapes. Copper alloys are commonly used as electrodes for their high thermal conductivity. The subject of this study was creating mathematical models for the machining optimization of Ampcoloy 35 with different thicknesses (ranging from 5 to 160 mm with a step of 5 mm) using WEDM to improve the surface properties of the mold parts. The Box-Behnken type experiment was used with a total of 448 samples produced. The following machining parameters were altered over the course of the experiment: the pulse on and off time, discharge current, and material thickness. The cutting speed was measured, and the topography of the machined surfaces in the center and at the margins of the samples was analyzed. The morphology and subsurface layer were also studied. What makes this study unique is the large number of the tested thicknesses, ranging from 5 to 160 mm with a step of 5 mm. The contribution of this study to the automotive industry and plastic injection mold production is, therefore, significant. The regression models for the cutting speed and surface topography allow for efficient defect-free machining of Ampcoloy 35 of 5-160 mm thicknesses, both on the surface and in the subsurface layer.
ABSTRACT
Unconventional wire electrical discharge machining technology (WEDM) is a key machining process, especially for machining newly emerging materials, as there are almost no restrictions (only at least minimal electrical conductivity) in terms of demands on the mechanical properties of the workpiece or the need to develop new tool geometry. This study is the first to present an analysis of the machinability of newly developed high entropy alloys (HEAs), namely FeCoCrMnNi and FeCoCrMnNiC0.2, using WEDM. The aim of this study was to find the optimal setting of machine parameters for the efficient production of parts with the required surface quality without defects. For this reason, an extensive design of experiments consisting of 66 rounds was performed, which took into account the influence of five input factors in the form of pulse off time, gap voltage, discharge current, pulse on time, and wire speed on cutting speed and the quality of the machined surface and its subsurface layer. The analysis of topography, morphology, subsurface layers, chemical composition analysis (EDX), and lamella analysis using a transmission electron microscope (TEM) were performed. An optimal setting of the machine parameters was found, which enables machining of FeCoCrMnNi and FeCoCrMnNiC0.2 with the required surface quality without defects.
ABSTRACT
The unconventional technology of wire electrical discharge machining is widely used in all areas of industry. For this reason, there is always an effort for efficient machining at the lowest possible cost. For this purpose, the following comprehensive study has been carried out to optimize the machining of the copper alloy Ampcoloy 35, which is particularly useful in plastic injection moulds. Within the study, a half-factor experiment of 25-1 with 10 axial points and seven central points of a total of 33 rounds was carried out, which was focused on the response monitoring of the input factors in the form of the machine parameters setup: gap voltage, pulse on time, pulse off time, discharge current, and wire speed. Based on the study of the response in the form of cutting speed and surface topography, their statistical models were created, while the optimal setting of machine parameters was determined to maximize the cutting speed and minimize the topography parameters. Further, a detailed cross-sectional analysis of surface and subsurface layer morphology was performed using electron microscopy including chemical composition analysis. In order to study microstructural changes in the material at the atomic level, a lamella was created, which was then studied using a transmission electron microscope.