Studies of Defect Structure in Epitaxial AlN/GaN Films Grown on (111) 3C-SiC.

Several aspects such as the growth relation between the layers of the GaN/AlN/SiC heterostructure, the consistency of the interfaces, and elemental diffusion are achieved by High Resolution Transmission Electron Microscopy (HR-TEM). In addition, the dislocation densities together with the defect correlation lengths are investigated via High-Resolution X-ray Diffraction (HR-XRD) and the characteristic positron diffusion length is achieved by Doppler Broadening Spectroscopy (DBS). Moreover, a comparative analysis with our previous work (i.e., GaN/AlN/Si and GaN/AlN/Al2O3) has been carried out. Within the epitaxial GaN layer defined by the relationship F4¯3m (111) 3C-SiC || P63mc (0002) AlN || P63mc (0002) GaN, the total dislocation density has been assessed as being 1.47 × 1010 cm-2. Compared with previously investigated heterostructures (on Si and Al2O3 substrates), the obtained dislocation correlation lengths (Le = 171 nm and Ls =288 nm) and the mean distance between two dislocations (rd = 82 nm) are higher. This reveals an improved crystal quality of the GaN with SiC as a growth template. In addition, the DBS measurements upheld the aforementioned results with a higher effective positron diffusion length LeffGaN2 = 75 ± 20 nm for the GaN layer.

Defect Structure Determination of GaN Films in GaN/AlN/Si Heterostructures by HR-TEM, XRD, and Slow Positrons Experiments.

The present article evaluates, in qualitative and quantitative manners, the characteristics (i.e., thickness of layers, crystal structures, growth orientation, elemental diffusion depths, edge, and screw dislocation densities), within two GaN/AlN/Si heterostructures, that alter their efficiencies as positron moderators. The structure of the GaN film, AlN buffer layer, substrate, and their growth relationships were determined through high-resolution transmission electron microscopy (HR-TEM). Data resulting from high-resolution X-ray diffraction (HR-XRD) was mathematically modeled to extract dislocation densities and correlation lengths in the GaN film. Positron depth profiling was evaluated through an experimental Doppler broadening spectroscopy (DBS) study, in order to quantify the effective positron diffusion length. The differences in values for both edge (ρde) and screw (ρds) dislocation densities, and correlation lengths (Le, Ls) found in the 690 nm GaN film, were associated with the better effective positron diffusion length (Leff) of LeffGaN2 = 43 ± 6 nm.

Study of Edge and Screw Dislocation Density in GaN/Al2O3 Heterostructure.

This study assesses the characteristics (edge and screw dislocation density) of a commercially available GaN/AlN/Al2O3 wafer. The heterostructure was evaluated by means of high-resolution X-ray diffraction (HR-XRD), high-resolution transmission electron microscopy (HR-TEM), and Doppler-Broadening Spectroscopy (DBS). The results were mathematically modeled to extract defect densities and defect correlation lengths in the GaN film. The structure of the GaN film, AlN buffer, Al2O3 substrate and their growth relationships were determined through HR-TEM. DBS studies were used to determine the effective positron diffusion length of the GaN film. Within the epitaxial layers, defined by a [GaN P 63 m c (0 0 0 2) || P 63 m c AlN (0 0 0 2) || (0 0 0 2) R 3 ¯ c Al2O3] relationship, regarding the GaN film, a strong correlation between defect densities, defect correlation lengths, and positron diffusion length was assessed. The defect densities ρ d e = 6.13 × 1010 cm-2, ρ d s = 1.36 × 1010 cm-2, along with the defect correlation lengths Le = 155 nm and Ls = 229 nm found in the 289 nm layer of GaN, account for the effective positron diffusion length Leff~60 nm.