Effect of 830 nm Diode Laser Irradiation of Root Canal on Bond Strength of Metal and Fiber Post.

OBJECTIVE AND BACKGROUND: The correct selections of the cementing agent, the endodontic post material and placement protocol are critical to provide an increased longevity of the teeth that went through endodontic treatment. The irradiation with diode laser before post cementation, can promote an antimicrobial effect. However, there is a lack of information about the effect of 830 nm diode laser on the post bond strength. This study analyzed the effect of dentin root canal irradiation with high-intensity diode laser, at 830 nm, operating in continuous or pulsed mode, on the retention of metal or fiber posts, cemented with self-etching resinous composite (Panavia F) and zinc phosphate cement (ZnPO4). MATERIALS AND METHODS: Human roots were irradiated with diode laser (continuous and pulsed mode). The fiber posts were luted with Panavia F and the metal posts with Panavia F or ZnPO4 cement. Specimens were sectioned into three sections (cervical, middle, and apical). The bond strength was measured by a push-out mechanical analysis. For the statistical analysis, a three-way ANOVA test was applied following a Tukey's pairwise comparison with a significance level of p = 0.05. RESULTS: The irradiated groups presented higher bond strength compared with nonirradiated group (p < 0.05), and the cervical and middle thirds presented higher on bond strength than the apical. The association of metal post and Panavia F presented higher bond strength when irradiated on continuous mode (p < 0.05). Fiber post and Panavia F presented higher bond strength associated to pulsed mode. The mode seems not to make a significant difference. CONCLUSIONS: These results corroborate the importance of the post bond to dentin and root canal debris removal to increase the tooth longevity. It was shown that the dentin to post bond strength were enhanced by the diode laser irradiation either on continuous or pulsed modes.

Influence of Er,Cr:YSGG laser on CaF2 -like products formation because of professional acidulated fluoride or to domestic dentifrice application.

This study evaluated the synergy of professional acidulated fluoride gel (APF) or fluoridated dentifrice application combined with Er,Cr:YSGG laser irradiation on the formation of CaF2 -like products (CaF2 ), in vitro. Thus, 272 bovine enamel slabs were randomly distributed among eight groups: G1: untreated enamel; G2: treated with fluoridated dentifrice (NaF, 1,100 µgF/g); G3: treated with acidulated phosphate fluoride gel (APF, 1.23% F(-) ); G4: irradiated with Er,Cr:YSGG laser at 8.5 J/cm(2) ; G5 and G6: combination of pre-irradiation with Er,Cr:YSGG followed by dentifrice or APF application, respectively; G7: combination of dentifrice application followed by Er,Cr:YSGG irradiation; G8: combination of APF application followed by Er,Cr:YSGG irradiation. After treatments, samples were evaluated by scanning electron microscopy, and the content of CaF2 was determined by an ion specific electrode. Both APF and dentifrice application promoted the formation of CaF2 on enamel, whereas Er,Cr:YSGG irradiation promoted an increase of roughness of the enamel, increasing the surface area. Laser irradiation before fluoridated products increased the content of CaF2 formed when compared to groups that APF or dentifrice were applied isolated. However, the content of CaF2 formed when irradiation was performed after APF or dentifrice was not statically significant when compared to the control groups. In conclusion, Er,Cr:YSGG laser increases the formation of CaF2 on enamel when the irradiation is performed before the application of APF or dentifrice. The association of laser with APF is most promissory for caries prevention because of the higher concentration of CaF2 formation and also the chemical changes promoted by laser irradiation demonstrated in literature.