ABSTRACT
Semitransparent perovskite solar cells (ST-PSCs) have great potential in building integrated photovoltaics. However, semitransparent devices suffer from a low electron mobility and an imbalanced charge-carrier transport, leading to an unsatisfactory power conversion efficiency (PCE) and limited stability. Herein, we report a high-performance ST-PSC via the incorporation of a special Lewis base. A better perovskite with an improved crystallinity and less defects was achieved, and a matched energy level alignment between the perovskite and [6,6]-phenyl-C61-butyric acid methyl ester was also induced, thereby leading to a high electron mobility and an exceptional balance of hole and electron mobility approaching 1 : 1. The prepared ST-PSC exhibited a PCE of 20.22% at average visible transmittance (AVT) of 4.93%, 18.32% at AVT of 14.38%, and 15.00% at AVT of 25.65%. These PCEs are the highest values among those ST-PSCs based on top metallic electrodes at a close AVT. The ST-PSCs maintained 92% of the initial PCE in storage for 1000 h, and they held 84% of the initial PCE under the continuous maximum power point tracking measurement for 530 hours. The work paves the way to realize ST-PSCs with a high PCE, high light utilization efficiency and substantially enhanced stability.
ABSTRACT
Lewis base molecules bind the undercoordinated lead atoms at interfaces and grain boundaries, leading to the high efficiency and stability of flexible perovskite solar cells (PSCs). We demonstrated a highly efficient, stable, and flexible PSC via interface passivation using a Lewis base of tri(o-tolyl)phosphine (TTP). It not only induced an intimate interface contact and a complete deposition of the perovskite thin layers on hole transport layers (HTLs) but also led to a better perovskite with a raised crystallinity, fewer defects, and a better morphology, including fewer gullies, high uniformity, and low roughness. Furthermore, the TTP treatments induced a good alignment of energy levels among the perovskites, HTLs, and C60. The resultant flexible inverted PSCs exhibited a high power conversion efficiency (PCE) of 23.81%, which is one of the highest PCEs among these flexible inverted PSCs. Moreover, the optimized flexible PSCs exhibited high storage stability, superior operation stability, and enhanced mechanical flexibility. This study presents an effective method to substantially raise the PCE, stability, and mechanical flexibility of the flexible inverted perovskite photovoltaics.