ABSTRACT
Porous self-assembled α-Fe2O3 hollow microspheres were fabricated via an ionic liquid-assisted solvothermal reaction and sequential calcinations. The concentration of the ionic liquid (1-butyl-3-methylimidazolium tetrafluoroborate [C4Mim]BF4) was found to play a crucial role in the control of these α-Fe2O3 hollow structures. Trace amounts ionic liquid was used as the soft template to synthesize α-Fe2O3 hollow spheres with a large specific surface (up to 220 m2/g). Based on time-dependent experiments, the proposed formation mechanisms were presented. Under UV light irradiation, the as-synthesized α-Fe2O3 hollow spheres exhibited excellent photocatalysis in Rhodamine B (RhB) photodegradation and the rate constant was 2-3 times higher than α-Fe2O3 particles. The magnetic properties of α-Fe2O3 hollow structures were found to be closely associated with the shape anisotropy.
ABSTRACT
A novel "selective surface dissolution" (SSD) method was successfully utilized in previous research to prepare "all-polymer composites" aiming to structural applications. In the current study, this simple, cost-effective, and environmentally friendly method was employed for the first time to synthesize cellulose-derived highly porous three-dimensional (3D) activated carbon materials to assemble superior electrodes for supercapacitors. ZnCl2 aqueous solution was used to partially dissolve the surface of cellulose fibers. The partially dissolved cellulose I crystalline phase at the fiber surface can be consolidated into fibrillar cellulose polymorphs (e.g., cellulose II) which connects remaining fibers together. By a carefully controlled SSD method, a highly porous 3D cellulosic skeleton with interconnected bridge-like fibrillar linkages and hierarchical pore structures can be created. After carbonization, the 3D fiber construct with interconnected fibrillar linkages and hierarchical pore structures remains and highly porous activated carbons were obtained. The effects of various processing parameters (e.g., solvent concentration, immersion time, etc.) on the morphology of the as-formed activated porous carbons and their electrochemical performance as electrodes in supercapacitors were systematically investigated and discussed. It was concluded that the SSD method is a promising chemical approach to produce large-scale cellulose-derived activated porous carbons in an environmentally friendly manner.