ABSTRACT
Graphene oxide aerogel (GOA) has wide application prospects due to its low density and high porosity. However, the poor mechanical properties and unstable structure of GOA have limited its practical applications. In this study, polyethyleneimide (PEI) was used to graft onto the surface of GO and carbon nanotubes (CNTs) to improve compatibility with polymers. Composite GOA was prepared by adding styrene-butadiene latex (SBL) to the modified GO and CNTs. The synergistic effect of PEI and SBL, resulted in an aerogel with excellent mechanical properties, compressive resistance, and structural stability. When the ratio of SBL to GO and GO to CNTs was 2:1 and 7:3, respectively, the obtained aerogel performance was the best, and the maximum compressive stress was 784.35% higher than that of GOA. The graft of PEI on the surface of GO and CNT could improve the mechanical properties of the aerogel, with greater improvements observed with grafting onto the surface of GO. Compared with GO/CNT/SBL aerogel without PEI grafting, the maximum stress of GO/CNT-PEI/SBL aerogel increased by 5.57%, that of GO-PEI/CNT/SBL aerogel increased by 20.25%, and that of GO-PEI/CNT-PEI/SBL aerogel increased by 28.99%. This work not only provided a possibility for the practical application of aerogel, but also steered the research of GOA in a new direction.
ABSTRACT
Three-dimensional (3D) graphene oxide aerogel (GOA) is one of the best fillers for composites for microwave absorption. However, its further development has been hindered by the poor mechanical properties. Methodology to improve the mechanical properties of the aerogel remains an urgent challenge. Herein, graphene oxide/carbon nanotube/epoxy resin composite aerogel (GCEA) was successfully prepared by a facile method. The results showed that the prepared GCEA with the hierarchical and 3D cross-linked structures exhibited excellent compression performance, structural and thermal stability, high hydrophilicity, and microwave absorption. The prepared GCEA recovered from multiple large strain cycles without significant permanent deformation. The minimum reflection loss (RL) was -39.60 dB and the maximum effective absorption bandwidth (EAB) was 2.48 GHz. The development of the enhanced GO aerogels will offer a new approach to the preparation of 3D microwave-absorbing skeletal materials with good mechanical properties.
ABSTRACT
The rational design of carbon nanomaterials-reinforced polymer matrix composites based on the excellent properties of three-dimensional porous materials still remains a significant challenge. Herein, a novel approach is developed for preparing large-scale 3D carbon nanotubes (CNTs) and graphene oxide (GO) aerogel (GO-CNTA) by direct grafting of CNTs onto GO. Following this, styrene was backfilled into the prepared aerogel and polymerized in situ to form GO-CNTA/polystyrene (PS) nanocomposites. The results of X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy indicate the successful establishment of CNTs and GO-CNT and the excellent mechanical properties of the 3D frameworks using GO-CNT aerogel. The nanocomposite fabricated with around 1.0 wt% GO-CNT aerogel displayed excellent thermal conductivity of 0.127 W/mâK and its mechanical properties were significantly enhanced compared with pristine PS, with its tensile, flexural, and compressive strengths increased by 9.01%, 46.8%, and 59.8%, respectively. This facile preparation method provides a new route for facilitating their large-scale production.