ABSTRACT
A laser-diode-pumped dual-loss-modulated Q-switching Tm:LuAG laser with an acousto-optic modulator (AOM) and monolayer graphene saturable absorber (SA) around 2 µm is presented for the first time to the best of our knowledge. The average output power and the pulse widths for different repetition rates have been measured. In comparison with the singly Q-switching laser with AOM or with monolayer graphene SA, the dual-loss-modulated Q-switching laser could generate shorter pulse width and higher peak power. The maximum pulse width compression ratio was found to be 3.11, and the highest peak power was enhanced 97.4 times. The experimental results show that the dual-loss-modulated technology is an efficient method for compressing the pulse width, improving the peak power, and enhancing the pulse stability for the Q-switched lasers at 2 µm.
Subject(s)
Graphite/chemistry , Lasers, Solid-State , Acoustics , Aluminum , Equipment Design , Lasers , Lutetium , Optical Devices , Oscillometry , ThuliumABSTRACT
Holmium doped scandium silicate (Ho:SSO) bulk crystal grown by Czochralski technique is reported. The absorption cross section of 4.8 × 10(-21) cm2 at pumping wavelength 1940 nm and emission cross section of 5.56 × 10(-21) cm2 at lasing wavelength 2112 nm were calculated, respectively. Lifetime was measured to be 1.51 ms at 300 K and 0.92 ms at 77 K. Continuous-wave laser was operated by using a diode-pumped Tm:YAP laser as pump source with central wavelength of 1940 nm. Output power of 385 mW at 2112 nm was primarily obtained.