ABSTRACT
Stationary energy storage infrastructure based on zinc-ion transport and storage chemistry is attracting more attention due to favorable metrics, including cost, safety, and recycling feasibility. However, splitting water and liquid electrolyte fluidity lead to cathode dissolution and Zn corrosion, resulting in rapid attenuation of the capacity and service life. Herein, a new architecture of solid-state electrolytes with high zinc ionic conductivity at room temperature was prepared via solidification of deep eutectic solvents utilizing MXene as nucleation additives. The ionic conductivity of MXene/ZCEs reached 6.69 × 10-4 S cm-1 at room temperature. Dendrite-free Zn plating/stripping with high reversibility can remain for over 2500 h. Subsequently, the fabricated solid-state zinc-ion battery with eliminated HER and suppressed Zn dendrites exhibited excellent cycling performance and could work normally in a range from -10 to 60 °C. This design inspired by eutectic solidification affords new insights into the multivalent solid electrochemistry suffering from slow ion migration.
ABSTRACT
How to construct a new electrode/electrolyte interface structure in solid-state batteries (SSBs), enhance interface stability, and improve the cycling performance of SSBs is a great challenge for the development of SSBs. Here, an all-in-one "interface-free" structure was developed. This interfacial structure constructs a full-interface hydrogen bonding network through the abundant hydrogen bond donors and acceptors in the cathode and electrolyte to enhance the interfacial stability and avoid interfacial failure during charging and discharging, and generates cathode-electrolyte interface (CEI) in-situ to effectively regulate zinc ion transport. Square cells assembled in this structure are stabilized for 100 cycles at a current density of 0.1 mA cm-2. This integrated electrode provides a new idea for the long stable cycle of SSBs.