Flexural Properties of Renewable Coir Fiber Reinforced Magnesium Phosphate Cement, Considering Fiber Length.

Coir fiber (CF), a renewable natural plant fiber, is more competitive in improving poor toughness and crack resistance of magnesium phosphate cement (MPC) than artificial fibers, due to its slight energy consumptions and low costs in production and waste treatment. In this paper, a typical three-point bending test was carried out to study the effects of CF length on MPC flexural properties. A total of forty-two cuboid specimens were employed to investigate the flexural strength, load-deflection behavior, and flexural toughness of MPC, with CF lengths varying from 0 to 30 mm at the curing age of 7 days and 28 days. Results showed that, at both two curing ages, MPC flexural strength first increased with CF length increasing, and then deceased when CF length exceeded the threshold. However, with the increase of CF length, MPC flexural toughness increased continuously, while MPC elastic modulus displayed a decreasing trend. Additionally, Modern micro testing techniques, such as scanning electron microscope (SEM) and X-ray diffraction (XRD), were also used to study the microstructure and phase compositions of specimens for further explaining the themicroscopic mechanism.

Study on the Compressive Properties of Magnesium Phosphate Cement Mixing with Eco-Friendly Coir Fiber Considering Fiber Length.

Coir fiber (CF), an eco-friendly and renewable natural fiber, was introduced into magnesium phosphate cement (MPC) mortar to improve its crack resistance. A total of 21 specimens were employed to investigate the failure pattern, compressive strength, stress-strain curve, and energy absorption of MPC with varying CF lengths (0, 5, 10, 15, 20, 25, and 30 mm) after a curing period of 28 days through a static compressive test. The results demonstrated that compressive strength, elastic modulus, and secant modulus decreased with the increase in CF length. However, energy absorption presented a convex curve, which increased to the maximum value (77.0% relative to the value of the specimen without CF) with a CF length of 20 mm and then declined. A series of modern micro-tests were then carried out to analyze the microstructure and composition of specimens to explain the properties microscopically.