ABSTRACT
Thermal power plant slag is a waste that is presently obtained from many power stations all over the world. A possible method for its utilization is using it to produce concrete. This paper analyses the effect of thermal power plant slag on the technological properties of concrete mixtures and the mechanical properties of concrete subjected to heat-moisture processing. Quantitative estimates of the investigated factors' influence on the concrete mixture's water demand and the strength of steamed concrete were obtained. The influences of TPP slag content and its water demand on concrete composition features as well as concrete strength are shown. The novelty of the work lies in the use of an experimental-statistical model to optimize the composition of steamed concrete using slag from the viewpoint of maximum strength per kilogram of cement. It has been demonstrated that the optimal part of slag in aggregate, which provides maximum strength at 4 h and 28 days after steaming, is 0.5-0.55 and 0.45-0.55, respectively. A method for the design of concrete composition using slag from thermal power plants is proposed.
ABSTRACT
This paper presents experimental results on the influence of concrete composition factors on the criterion characterizing the ratio between the compressive strength of activated low-cement concrete and clinker consumption. The investigation was carried out using mathematical planning of the experiments. Experimental and statistical models describing the influence of the fly ash, activating additive (microsilica), consumption of cement and aggregates, as well as the superplasticizer on the strength of low-cement concrete under normal hardening conditions and after steaming were obtained. The values of the clinker efficiency criterion and the mineral additive cementing efficiency coefficient were calculated, and models of these parameters were obtained for the investigated concrete compositions. It was shown that the activating effect of microsilica yields an increase in ash cementing efficiency and clinker efficiency criterion in concrete. Using the obtained models, an example for calculating the ash cementing efficiency coefficient is given.
ABSTRACT
The paper deals with the effectiveness of various types of polymers (naphthalene formaldehyde, polycarboxylate, and lignosulfonate) as superplasticizers of concrete mixtures based on low-clinker slag Portland cement. Using the mathematical planning experimental method and statistical models of water demand of concrete mixtures with polymer superplasticizers, as well as concrete strength at different ages and under different curing conditions (normal curing and after steaming) were obtained. According to the models, the superplasticizer's water-reducing effect and relative change in concrete strength were obtained. The proposed criterion for evaluating the effectiveness and compatibility of superplasticizers with cement takes into account the water-reducing effect of the superplasticizer and the corresponding relative change in concrete strength. The results demonstrate that the use of the investigated superplasticizer types and low-clinker slag Portland cement allows for achieving a significant increase in concrete strength. The effective contents of various polymer types, which allow the achieving of concrete strengths from 50 MPa to 80 Mpa, has been found.
ABSTRACT
Ground blast-furnace slag is one of the waste products available in Ukraine and other countries. It is obtained at metallurgical enterprises in huge quantities and can be efficiently used for concrete production. The article is devoted to obtaining experimental-statistical models of the influence of technological factors that determine the composition of self-compacting concrete (SCC) based on ground blast-furnace slag and polycarboxylate superplasticizer on compressive strength, tensile strength, prismatic strength, elastic modulus and crack resistance. Analysis of the investigated factors' influence on the specified SCC properties is carried out and positive influence of blast-furnace slag and superplasticizer simultaneous action on durability and deformation characteristics is studied. A design method of SCC composition design using the obtained mathematical models is developed. It allows for the consideration of a set of necessary parameters simultaneously. A numerical example is given.