ABSTRACT
Ultrasmall black phosphorus quantum dots (BPQDs) serve as the near-infrared light absorber and charge transfer layer in the photocathode of a bifacial n-type dye sensitized solar cell. Wideband light absorption and ≈20% enhancement in the light-to-electron efficiency are accomplished due to the fast carrier transfer and complementary light absorption by the BPQDs demonstrating that BP has large potential in photovoltaics.
ABSTRACT
Titanium dioxide sols were synthesized by hydrothermal reactions with addition of poly (ethylene glycol) (Mw=20,000). Using techniques of X-ray diffraction, transmission electron microscopy, dynamic light scattering, and scanning electron microscopy, effect of PEG on the crystallographic properties, particle size, aggregating behavior, and the morphological properties of nanoparticles in the sols were studied. It was found that growth of anatase nanocrystallites was retarded by PEG. Average crystallite size of anatase nanocrystallites first decreased from 20.7 nm to 10.5 nm as the polymer concentration increased from 1 g/L to 3 g/L, and then changed little. Meanwhile, small amount of rutile phases like rutile nanowires, twin crystallites, and the "flowers" appeared continuously when the concentration increased from 3 g/L to 5 g/L. Mono-dispersion was obtained with relatively lower PEG concentration. The observed evolvement was discussed based on the interaction between the polymers and the nanocrystallites with assistance of FTIR. The coverage of polymer chains on surface of nanocrystallites leads to isolated reactors, which benefits the uniform coarsening rate of the nanocrystallites. The synthesized TiO(2) sols were utilized in dye sensitized solar cells. Performance parameters of the solar cells were discussed with assistance of dye desorption experiments. The improved dispersion in sols was found to benefit the photovoltaic performance of the cells.
ABSTRACT
A quasi-solid-state dye-sensitized solar cell employing a poly(ethylene oxide)-poly(vinylidene fluoride) (PEO-PVDF)/TiO2 gel electrolyte modified by various concentrations of water and ethanol is described. It is shown that the introduction of water and ethanol prevents the crystallization of the polymer matrix, and enhances the free I(-)/I(3)(-) concentration and the networks for ion transportation in the electrolyte, thus leading to an improvement in conductivity. A high energy conversion efficiency of about 5.8% is achieved by controlling the additive concentration in the electrolyte. Optimization of the additive-modified electrolyte performance has been obtained by studying the cross-linking behavior of water and ethanol with Fourier transform infrared (FTIR), differential scanning calorimetry (DSC) and viscosity measurements, and the electrical conduction behavior of the electrolyte with impedance spectra measurements.