ABSTRACT
Graphene oxide (GO), reduced graphene oxide (rGO) and carbon nanotubes (CNTs) have their own advantages in electrical, optical, thermal and mechanical properties. An effective combination of these materials is ideal for preparing transparent conductive films to replace the traditional indium tin oxide films. At present, the preparation conditions of rGO are usually harsh and some of them have toxic effects. In this paper, an SnCl2/ethanol solution was selected as the reductant because it requires mild reaction conditions and no harmful products are produced. The whole process of rGO preparation was convenient, fast and environmentally friendly. Then, SEM, XPS, Raman, and XRD were used to verify the high reduction efficiency. CNTs were introduced to improve the film conductive property. The transmittance and sheet resistance were the criteria used to choose the reduction time and the content ratios of GO/CNT. Thanks to the post-treatment of nitric acid, not only the by-product (SnO2) and dispersant in the film are removed, but also the doping effect occurs, which are all conducive to reducing the sheet resistances of films. Ultimately, by combining rGO, GO and CNTs, transparent conductive films with a bilayer and three-dimensional structure were prepared, and they exhibited high transmittance and low sheet resistance (58.8 Ω/sq. at 83.45 T%, 47.5 Ω/sq. at 79.07 T%), with corresponding [Formula: see text] values of 33.8 and 31.8, respectively. In addition, GO and rGO can modify the surface and reduce the film surface roughness. The transparent conductive films are expected to be used in photoelectric devices.
ABSTRACT
In this paper, we used tannic acid (TA) functionalized carbon nanotubes (TCNTs), and silver nanowires (AgNWs) to construct a new type of transparent conductive film (TCF) with a double-layered conductive network structure. The hybrid film exhibits excellent light transmittance, high electrical conductivity, ultra-flexibility, and strong adhesion. These outstanding performances benefit from the filling and adhesion of hydrophilic TCNT layers to the AgNW networks. Besides, we introduced the post-treatment process of mechanical pressing and covering polymer conductive polymer PEDOT:PSS, which obtained three layers of TCNT/AgNW/PEDOT hybrid film and greatly improved the comprehensive properties. The hybrid film can reach a sheet resistance of 9.2 Ω sq-1 with a transmittance of 83.4% at 550 nm wavelength, and a low root mean square (RMS) roughness (approximately 3.8 nm). After 10 000 bends and tape testing, the conductivity and transmittance of the hybrid film remain stable. The resistance of the film has no significant degradation after 14 d of exposure to high temperature of 85 °C and humidity of 85%, indicating excellent stability. The organic light-emitting diodes (OLEDs) with TCNT/AgNW/PEDOT hybrid film as anode exhibit high current density and luminosity, confirming this process has considerable potential application in photovoltaic devices.
ABSTRACT
In this paper, the eco-friendly plant polyphenol, tannic acid (TA) was demonstrated as a non-covalent modifier for carbon nanotubes (CNTs), as well as a stripping medium to achieve exfoliated graphite to graphene by microfluidization. High-performance transparent flexible heater (TFH) with an embedded structure had been successfully fabricated by integrating conductive nanocomposites (TA-functionalized grapheme/TA-functionalized CNT/PEDOT:PSS; TG/TCNT/PEDOT) into waterborne polyurethane (WPU) film. Such a film exhibited favorable optical transmittance and sheet resistance (T = ca. 80% at 550 nm, Rs = 62.5 Ω/sq.), low root mean square (rms) roughness (approximately 0.37 nm), excellent adhesion and mechanical stability (the sheet resistance remained almost constant after 1000 bending cycle test for the bending radius of 10 mm), which are ideal as transparent heaters with high thermal efficiency. For TG/TCNT/PEDOT-WPU TFHs, the temperature increased rapidly and reached a steady state within 20 s with the maximum temperature reached to 116 °C, when the applied voltage was 20 V. Moreover, no variation in temperature was observed after the repeated heating-cooling tests and long-time stability test, indicating that TG/TCNT/PEDOT-WPU TCFs can be used as high performance TFHs. These TFH's are expected to be suitable for vehicle defrosting, smart windows, portable heating, smart wearable devices, etc.