Hybrid Implants Based on Calcium-Magnesium Silicate Ceramic Diopside as a Carrier of Recombinant BMP-2 and Demineralized Bone Matrix as a Scaffold: Ectopic Osteogenesis in Intramuscular Implantation in Mice.

High efficiency of hybrid implants based on calcium-magnesium silicate ceramic, diopside, as a carrier of recombinant BMP-2 and xenogenic demineralized bone matrix (DBM) as a scaffold for bone tissue regeneration was demonstrated previously using the model of critical size cranial defects in mice. In order to investigate the possibility of using these implants for growing autologous bone tissue using in vivo bioreactor principle in the patient's own body, effectiveness of ectopic osteogenesis induced by them in intramuscular implantation in mice was studied. At the dose of 7 µg of BMP-2 per implant, dense agglomeration of cells, probably skeletal muscle satellite precursor cells, was observed one week after implantation with areas of intense chondrogenesis, initial stage of indirect osteogenesis, around the implants. After 12 weeks, a dense bone capsule of trabecular structure was formed covered with periosteum and mature bone marrow located in the spaces between the trabeculae. The capsule volume was about 8-10 times the volume of the original implant. There were practically no signs of inflammation and foreign body reaction. Microcomputed tomography data showed significant increase of the relative bone volume, number of trabeculae, and bone tissue density in the group of mice with BMP-2-containing implant in comparison with the group without BMP-2. Considering that DBM can be obtained in practically unlimited quantities with required size and shape, and that BMP-2 is obtained by synthesis in E. coli cells and is relatively inexpensive, further development of the in vivo bioreactor model based on the hybrid implants constructed from BMP-2, diopside, and xenogenic DBM seems promising.

Hybrid Implants Based on Calcium-Magnesium Silicate Ceramics Diopside as a Carrier of Recombinant BMP-2 and Demineralized Bone Matrix as a Scaffold: Dynamics of Reparative Osteogenesis in a Mouse Craniotomy Model.

Calcium-magnesium silicate ceramics, diopside, is a promising material for use in bone plastics, but until now the possibility of its use as a carrier of recombinant bone morphogenetic protein-2 (BMP-2) has not been studied, as well as the features of reparative osteogenesis mediated by the materials based on diopside with BMP-2. Powder of calcium-magnesium silicate ceramics was obtained by solid-state synthesis using biowaste - rice husks and egg shells - as source components. Main phase of the obtained ceramics was diopside. The obtained particles were irregularly shaped with an average size of about 2.3 µm and ~20% porosity; average pore size was about 24 nm, which allowed the material to be classified as mesoporous. Diopside powder adsorbs more than 150 µg of recombinant BMP-2 per milligram, which exceeds binding capacity of hydroxyapatite, a calcium-phosphate ceramic often used in hybrid implants, by more than 3 times. In vitro release kinetics of BMP-2 was characterized by a burst release in the first 2 days and a sustained release of approximately 0.4 to 0.5% of the loaded protein over the following 7 days. In vivo experiments were performed with a mouse model of cranial defects of critical size with implantation of a suspension of diopside powder with/without BMP-2 in hyaluronic acid incorporated into the disks of demineralized bone matrix with 73-90% volume porosity and macropore size from 50 to 650 µm. Dynamics of neoosteogenesis and bone tissue remodeling was investigated histologically at the time points of 12, 21, 48, and 63 days. Diopside particles were evenly spread in the matrix and caused minimal foreign body reaction. In the presence of BMP-2 by the day 63 significant foci of newly formed bone tissue were formed in the implant pores with bone marrow areas, moreover, large areas of demineralized bone matrix in the implant center and maternal bone at the edges were involved in the remodeling. Diopside could be considered as a promising material for introduction into hybrid implants as an effective carrier of BMP-2.

Identification of HI-like loop in CELO adenovirus fiber for incorporation of receptor binding motifs.

Vectors based on the chicken embryo lethal orphan (CELO) avian adenovirus (Ad) have two attractive properties for gene transfer applications: resistance to preformed immune responses to human Ads and the ability to grow in chicken embryos, allowing low-cost production of recombinant viruses. However, a major limitation of this technology is that CELO vectors demonstrate decreased efficiency of gene transfer into cells expressing low levels of the coxsackie-Ad receptor (CAR). In order to improve the efficacy of gene transfer into CAR-deficient cells, we modified viral tropism via genetic alteration of the CELO fiber 1 protein. The alphav integrin-binding motif (RGD) was incorporated at two different sites of the fiber 1 knob domain, within an HI-like loop that we identified and at the C terminus. Recombinant fiber-modified CELO viruses were constructed containing secreted alkaline phosphatase (SEAP) and enhanced green fluorescent protein genes as reporter genes. Our data show that insertion of the RGD motif within the HI-like loop of the fiber resulted in significant enhancement of gene transfer into CAR-negative and CAR-deficient cells. In contrast, CELO vectors containing the RGD motif at the fiber 1 C terminus showed reduced transduction of all cell lines. CELO viruses modified with RGD at the HI-like loop transduced the SEAP reporter gene into rabbit mammary gland cells in vivo with an efficiency significantly greater than that of unmodified CELO vector and similar to that of Ad type 5 vector. These results illustrate the potential for efficient CELO-mediated gene transfer into a broad range of cell types through modification of the identified HI-like loop of the fiber 1 protein.