ABSTRACT
Silicon is considered as a blooming candidate material for next-generation lithium-ion batteries due to its low electrochemical potential and high theoretical capacity. However, its commercialization has been impeded by the poor cycling issue associated with severe volume changes (â¼380%) upon (de)lithiation. Herein, an organic-inorganic hybrid film of titanicone via molecular layer deposition (MLD) is proposed as an artificial solid electrolyte interphase (SEI) layer for Si anodes. This rigid-soft titanicone coating with Young's modulus of 21 GPa can effectively relieve stress concentration during the lithiation process, guaranteeing the stability of the mechanical structure of a Si nanoparticles (NPs)@titanicone electrode. Benefiting from the long-strand (Ti-O-benzene-O-Ti-) unit design, the optimized Si NPs@70 cycle titanicone anode delivers a high Li+ diffusion coefficient and a low Li+ diffusion barrier, as revealed by galvanostatic intermittent titration (GITT) investigations and density functional theory (DFT) simulations, respectively. Ultimately, the Si NPs@70 cycle titanicone electrode shows high initial Coulombic efficiency (84%), long cycling stability (957 mAh g-1 after 450 cycles at 1 A g-1), a stable SEI layer, and good rate performances. The molecular-scale design of the titanicone-protected Si anodes may bring in new opportunities to realize the next-generation lithium-ion batteries as well as other rechargeable batteries.
ABSTRACT
In this work, commercial anatase TiO2 powders were modified using ultrathin Fe2O3 layer by atomic layer deposition (ALD). The ultrathin Fe2O3 coating having small bandgap of 2.20 eV can increase the visible light absorption of TiO2 supports, at the meantime, Fe2O3/TiO2 heterojunction can effectively improve the lifetime of photogenerated electron-hole pairs. Results of ALD Fe2O3 modified TiO2 catalyst, therefore, showed great visible light driven catalytic degradation of methyl orange compared to pristine TiO2. A 400 cycles of ALD Fe2O3 (~ 2.6 nm) coated TiO2 powders exhibit the highest degradation efficiency of 97.4% in 90 min, much higher than pristine TiO2 powders of only 12.5%. Moreover, an ultrathin ALD Al2O3 (~ 2 nm) was able to improve the stability of Fe2O3-TiO2 catalyst. These results demonstrate that ALD surface modification with ultrathin coating is an extremely powerful route for the applications in constructing efficient and stable photocatalysts.
ABSTRACT
To address the issues of large volume expansion and low electrical conductivity of ZnO anode nanomaterials during lithium ion battery operation, herein we engineered a rod-like ZnO anode with robust and conductive TiO2 quantum dot (QD)@carbon coating derived from molecular layer deposited titanicone, in which the TiO2 QDs are well confined inside the carbon layer. Transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) confirm the formation of TiO2 QDs and carbonization of fumaric acid in hybrid films after annealing in H2 atmosphere at 700 °C. Benefiting from a unique protective layer design, the prepared TiO2 QD@carbon@ZnO nanorod (NR) anodes display outstanding cycling performance with a discharge capacity of 1154 mA h g-1 after 100 cycles and 70% capacity retention, along with a high rate capacity of 470 mA h g-1 for 500 cycles at 2 A g-1. Moreover, our work demonstrates an innovative and promising approach toward a robust and conductive metal oxide QD@carbon nanocomposite layer for electrode materials in the future.
ABSTRACT
Co-Pt bimetallic nanoparticles with adjustable composition and particle size were prepared by the combination of atomic layer deposition and H2 post-deposition annealing. The structure, magnetic and electrocatalytic properties of Co-Pt bimetallic nanoparticles can be facilely tuned by controlling the composition.