ABSTRACT
Arsenic sulfide compounds have a long history of application in a traditional medicine. In recent years, realgar has been studied as a promising drug in cancer treatment. In this study, the arsenic sulfide (As4S4) nanoparticles combined with zinc sulfide (ZnS) ones in different molar ratio have been prepared by a simple mechanochemical route in a planetary mill. The successful synthesis and structural properties were confirmed and followed via X-ray diffraction and high-resolution transmission electron microscopy measurements. The morphology of the particles was studied via scanning electron microscopy and transmission electron microscopy methods and the presence of nanocrystallites was verified. For biological tests, the prepared As4S4/ZnS nanoparticles were further milled in a circulation mill in a water solution of Poloxamer 407 (0.5wt%), in order to cover the particles with this biocompatible copolymer and to obtain stable nanosuspensions with unimodal distribution. The average size of the particles in the nanosuspensions (~120nm) was determined by photon cross-correlation spectroscopy method. Stability of the nanosuspensions was determined via particle size distribution and zeta potential measurements, confirming no physico-chemical changes for several months. Interestingly, with the increasing amount of ZnS in the sample, the stability was improved. The anti-cancer effects were tested on two melanoma cell lines, A375 and Bowes, with promising results, confirming increased efficiency of the samples containing both As4S4 and ZnS nanocrystals.
Subject(s)
Antineoplastic Agents , Arsenicals , Drug Carriers , Melanoma/drug therapy , Nanoparticles/chemistry , Poloxamer , Sulfides , Zinc Compounds , Antineoplastic Agents/chemistry , Antineoplastic Agents/pharmacokinetics , Antineoplastic Agents/pharmacology , Arsenicals/chemistry , Arsenicals/pharmacokinetics , Arsenicals/pharmacology , Cell Line, Tumor , Drug Carriers/chemistry , Drug Carriers/pharmacokinetics , Drug Carriers/pharmacology , Humans , Melanoma/metabolism , Melanoma/pathology , Poloxamer/chemistry , Poloxamer/pharmacokinetics , Poloxamer/pharmacology , Sulfides/chemistry , Sulfides/pharmacokinetics , Sulfides/pharmacology , Zinc Compounds/chemistry , Zinc Compounds/pharmacokinetics , Zinc Compounds/pharmacologyABSTRACT
Significant increase of the adsorption ability of the eggshell biomaterial toward cadmium was observed upon milling, as is evidenced by the value of maximum monolayer adsorption capacity of 329mgg(-1), which is markedly higher than in the case of most "green" sorbents. The main driving force of the adsorption was proven to be the presence of aragonite phase as a consequence of phase transformation from calcite occurring during milling. Cadmium is adsorbed in a non-reversible way, as documented by different techniques (desorption tests, XRD and EDX measurements). The optimum pH for cadmium adsorption was 7. The adsorption process was accompanied by the increase of the value of specific surface area. The course of adsorption has been described by Langmuir, Freundlich and Dubinin-Radushkevich isotherms. The adsorption kinetics was evaluated using three models, among which the best correlation coefficients and the best normalized standard deviation values were achieved for the pseudo-second order model and the intraparticle diffusion model, respectively.
Subject(s)
Cadmium/isolation & purification , Calcium Carbonate/chemistry , Drinking Water/chemistry , Wastewater/chemistry , Water Pollutants, Chemical/isolation & purification , Adsorption , Animals , Cations, Divalent , Chickens , Eggs/analysis , Hydrogen-Ion Concentration , Kinetics , Thermodynamics , Waste Products , Water Purification/methodsABSTRACT
In this paper, the sorption of arsenic onto nanocrystalline magnetite mineral Fe3O4 was studied in a model system. Nanocrystalline magnetite was produced by mechanical activation in a planetary ball mill from natural microcrystalline magnetite. As a consequence of milling, the specific surface area increased from 0.1m(2)/g to 11.9 m(2)/g and the surface site concentration enhanced from 2.2 sites/nm(2) to 8.4 sites/nm(2). These changes in surface properties of magnetite lead to the enhancement of arsenic removal from model system. The best sorption ability was achieved with magnetite sample activated for 90 min. In this case the sample was able to absorb around 4 mg/g. The structural changes of magnetite were also observed and the new hematite phase was detected after 120 min of milling. A good correlation between the decreasing particle size, increasing specific surface area and reduction of saturation magnetization was found. In desorption study, KOH and NaOH were found as the best eluents where more than 70% of arsenic was released back into the solution. The principal novelty of the paper is that mineral magnetite, truly one nature's gift can be used after "smart" milling (mechanical activation) as an effective arsenic sorbent.