ABSTRACT
The anti-solvent-free fabrication of high-efficiency perovskite solar cells (PSCs) holds immense significance for the transition from laboratory-scale to large-scale commercial applications. However, the device performance is severely hindered by the increased occurrence of surface defects resulting from the lack of control over nucleation and crystallization of perovskite using anti-solvent methods. In this study, 2-(naphthalen-2-yl)ethylamine hydriodide (NEAI) is employed as the surface passivator for perovskite films without using any anti-solvent. Naphthalene demonstrates strong π-π conjugation, which aids in the efficient extraction of charge carriers. Additionally, the naphthalene-ring moieties form a tight attachment to the perovskite surface. After NEAI treatment, FA and I vacancies are selectively occupied by NEA+ and I- in NEAI respectively, thus effectively passivating the surface defects and isolating the surface from moisture. Ultimately, the optimized NEAI-treated device achieves a promising power conversion efficiency (PCE) of 24.19% (with a certified efficiency of 23.94%), featuring a high fill factor of 83.53%. It stands out as one of the reported high PCEs achieved for PSCs using the spin-coating technique without the need for any anti-solvent so far. Furthermore, the NEAI-treated device can maintain ≈87% of its initial PCE after 2000 h in ambient air with a relative humidity of 30% ± 5%.
ABSTRACT
Photovoltaic technology with low weight, high specific power in cold environments, and compatibility with flexible fabrication is highly desired for near-space vehicles and polar region applications. Herein, we demonstrate efficient low-temperature flexible perovskite solar cells by improving the interfacial contact between electron-transport layer (ETL) and perovskite layer. We find that the adsorbed oxygen active sites and oxygen vacancies of flexible tin oxide (SnO2 ) ETL layer can be effectively decreased by incorporating a trace amount of titanium tetrachloride (TiCl4 ). The effective defects elimination at the interfacial increases the electron mobility of flexible SnO2 layer, regulates band alignment at the perovskite/SnO2 interface, induces larger perovskite crystal growth, and improves charge collection efficiency in a complete solar cell. Correspondingly, the improved interfacial contact transforms into high-performance solar cells under one-sun illumination (AM 1.5G) with efficiencies up to 23.7 % at 218â K, which might open up a new era of application of this emerging flexible photovoltaic technology to low-temperature environments such as near-space and polar regions.