The properties of particleboard composites made from three sorghum (Sorghum bicolor) accessions using maleic acid adhesive.

It is very important to develop green composite materials owing to increasing global environmental issues. One of the alternative raw materials for the production of green composites is biomass. Bagasse sorghum is a promising alternative raw material for the manufacturing of particleboard composites. The influence of sorghum accessions on the performance of particleboard composites was analyzed in this study. In addition, the particleboard quality was made using maleic acid (MA) adhesive and compared with citric acid (CA) and phenol-formaldehyde (PF) adhesives. Three accessions of sorghum, 4183A, super 1, and Pahat, were used as raw materials in particleboard manufacturing. The 20 wt% MA adhesive was applied in particleboard manufacturing. The board dimensions and density targets were 30 × 30 × 0.9 cm3 and 0.8 g/cm3, respectively. The particle mat was pressed 200 °C for 10 min with a maximum of 6.5 MPa. For reference, the JIS A 5908-2003 was used to evaluate physical and mechanical properties, SNI 7207-2014 was used for the resistance against termites, and JIS K 1571-2004 for evaluated the particleboard against decay. The results showed that the sorghum accession in this research did not affect the quality of the particleboard. The thickness swelling (TS), internal bond (IB), modulus of elasticity (MOE), and modulus of rupture (MOR) of particleboard satisfied JIS A 5908-2003 type 8. The particleboard using MA was comparable with those bonded with CA and had better durability against termites and decay than PF adhesives. The ester linkages were formed due to the reaction between MA (carboxyl groups) and the sorghum bagasse (hydroxyl groups) after being analyzed using Fourier transform infrared (FTIR). Therefore, particleboard in this study has good quality.

Novel antimicrobial bioplastic based on PLA-chitosan by addition of TiO2 and ZnO.

PURPOSE: The purpose of this study was to develop antimicrobial bioplastics based on Poly Lactic Acid (PLA) with the addition of chitosan-ZnO, and chitosan-TiO2 to improve antimicrobial properties. METHODS: For the preparation of the bioplastics, PLA with chitosan-ZnO or chitosan-TiO2 were used. The antimicrobial activity, mechanical and thermal properties, and water vapor permeability of bioplastics were evaluated. RESULTS: PLA-chitosan-ZnO indicated a robust antimicrobial activity against bacteria such as Salmonella typhi, Bacillus subtilis, Escherichia coli, Staphylococcus aureus, yeast such as Candida albicans, and fungus Aspergillus niger. No formation of new functional groups in PLA-chitosan-ZnO composites. In comparison to other PLA-based bioplastics, this bioplastic has medium tensile strength, tensile modulus, and elongation percentages with low barrier ability to water vapor. Chitosan-ZnO itself has a greater tensile strength compared to chitosan-TiO2. These two compounds undergo 2 stages of decomposition in a temperature range of 43 °C to 265 °C. The addition of PLA into chitosan-ZnO or chitosan TiO2 causes the bioplastics decomposed in a single stage. It also increases the decomposition temperature of bioplastic. However, compared to chitosan-ZnO or TiO2, the PLA-chitosan-ZnO or TiO2 bioplastics tend to produce a fragile composite indicating by decrease in their tensile strength. CONCLUSION: In general, the addition of chitosan-ZnO into in PLA-based bioplastic produces better antimicrobial properties compared to TiO2.

Antimicrobial Imperata cylindrica paper coated with anionic nanocellulose crosslinked with cationic ions.

Recently, the interest in active packaging utilization has increased with population growth, food demand and new consumer trend like food delivery services. This new system, however, requires the use of additives to extend the food product quality and safety as well as in maintaining the shelf-life. This study was to prepare the antimicrobial paper from I. cylindrica coated anionic nanocellulose crosslinked cationic to create a system with the ability to actively control microbe growth in the packaging materials. The process involved pulping of I. cylindrica using semi-chemical and soda chemical method. The antimicrobial paper was prepared by printing the pulp suspension in 60 g/m2 grammage in mold followed by the spray of anionic nanocellulose and subsequent soaking of the paper in cationic solution. The results showed the I. cylindrica paper coated anionic nanocellulose crosslinked with H+ and Al3+ cations were successfully produced. The paper produced was also observed to have antimicrobial activity against Gram-negative of E. coli and S. typhi as well as Gram-positive of S. aureus and B. subtilis bacteria. Furthermore, the best coating method was found on antimicrobial paper coated anionic nanocellulose crosslinked Al3+ as evidenced by smoother and compact surface structure.

The Efficacy of Organo-Complex-Based Wood Preservative Formula Against Dry-Wood Termite Cryptotermes cynocephalus Light.

The utilization of pesticides often leaves residues which potentially pollute the environment. This journal issue has been encouraging some researchers to find an environmentally friendly insecticide by a cheaper wood preservative method. The International Standard for Phytosanitary Measures 15 (ISPM 15) [1] that is adopted in wood packaging protection in Europe is not suitable for tropical countries like Indonesia. Therefore, the treatment by Organo-Complex-based wood preservation, which consists of copper chromium combined with natural organic compounds, is proposed for effective treatment at a lower cost. The bioassay test was subjected to dry wood termite Cryptotermes cynocephalus Light. The result showed that wood materials treated by 10 ppm Organo-Complex formula gave good results which were indicated by the low consumption and the fast termination of the termites. The toxicity analysis of C-C organic compound solution is classified as grade IV (WHO, 2003) [2], or not harmful. Analysis of the residual content four weeks after the spraying treatment showed a significant reduction in the inorganic content (copper chromate complex), in the range of 35%, and in extracts of natural materials (natural extracts), above 80%.