ABSTRACT
Particleboards have gained attention in the global market. Understanding their physical-mechanical behavior in the current technological context is essential due to adhesive polymerization, which depends on variables such as pressing time and temperature. Today, the use of nanoparticles has become a plausible option for improving the properties of polymers used in wood-based composites. This study evaluates the influences of the addition of non-commercial 0.5% aluminum oxide (Al2O3) and aluminum oxide copper (CuO) nanoparticles using a greener route with a lower environmental impact obtaining a urea-formaldehyde (UF)-based polymeric adhesive to manufacture particle composites of Eucalyptus urophylla var. grandis wood. Regarding characterizations, the resin properties analyzed were viscosity, gel time, and pH, as well as panel properties, including density, moisture content, thickness swelling, modulus of elasticity, modulus of rupture, and thermal conductivity. The results were compared with scientific publications and standards. The addition of nanoparticles interfered with viscosity, and all treatments indicated a basic pH. It was not possible to determine the gel time after 10 min. Nanoparticles added to the polymers in the internal layer did not cause an improvement in the swelling properties in terms of thickness, with no significant statistical difference for density and moisture content. The increase from 150 °C to 180 °C may have caused an improvement in all physical-mechanical properties, indicating that the higher temperature positively influenced the polymerization of the formaldehyde-based adhesive. Therefore, the additions of both nanoparticles (0.5% in each condition) led to a limitation in the material influence with respect to physical-mechanical performance.
ABSTRACT
The development of new materials for the construction sector is a global trend, and products that use by-products in their composition and have also incorporated technology are commercially competitive. Microparticles have large surface areas and can modify the microstructure of materials, positively affecting their physical and mechanical properties. In this context, this study aims to investigate the effect of incorporating aluminium oxide (Al2O3) microparticles on the physical and mechanical properties of oriented strand boards (OSBs) made from reforested residual balsa and castor oil polyurethane resin and to evaluate their durability performance under accelerated aging conditions. The OSBs were produced on a laboratory scale with a density of 650 kg/m3, strand-type particles measuring 90 × 25 × 1 mm3, using castor oil-based polyurethane resin (13%) and Al2O3 microparticle content ranging from 1% to 3% of the resin mass. The physical and mechanical properties of the OSBs were determined following the EN-300:2002 recommendations. The results obtained indicated that the OSBs with 2% Al2O3 presented thickness swelling significantly lower (at the 5% significance level) after being subjected to accelerated aging and internal bonding of the particles higher than the values obtained for the references, evidencing the positive effect of including Al2O3 microparticles in balsa OSBs.