ABSTRACT
Nanocomposites based on poly(lactic acid) (PLA) and magnetite nanoparticles (MNP-Fe3O4) show promise for applications in biomedical treatments. One key challenge is to improve the stabilization and dispersion of MNP-Fe3O4. To address this, we synthesized MNP-Fe3O4/PLA nanocomposites using ultrasound mediation and a single iron(II) precursor, eliminating the need for surfactants or organic solvents, and conducted the process under ambient conditions. The resulting materials, containing 18 and 33 wt.% Fe3O4, exhibited unique thermal behavior characterized by two mass losses: one at a lower degradation temperature (Td) and another at a higher Td compared to pure PLA. This suggests that the interaction between PLA and MNP-Fe3O4 occurs through hydrogen bonds, enhancing the thermal stability of a portion of the polymer. Fourier Transform Infrared (FT-IR) analysis supported this finding, revealing shifts in bands related to the terminal -OH groups of the polymer and the Fe-O bonds, thereby confirming the interaction between the groups. Raman spectroscopy demonstrated that the PLA serves as a protective layer against the oxidation of MNP-Fe3O4 in the 18% MNP-Fe3O4/PLA nanocomposite when exposed to a high-power laser (90 mW). Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM) analyses confirmed that the synthetic procedure yields materials with dispersed nanoparticles within the PLA matrix without the need for additional reactants.
ABSTRACT
Poly(lactic acid) (PLA) is an important polymer that is based on renewable biomass resources. Because of environmental issues, more renewable sources for polymers synthesis have been sought for industrial purposes. In this sense, cheaper monomers should be used to facilitate better utilization of less valuable chemicals and therefore granting more sustainable processes. Some points are raised about the need to study the total degradability of any PLA, which may require specific composting conditions (e.g., temperature, type of microorganism, adequate humidity and aerobic environment). Polymerization processes to produce PLA are presented with an emphasis on D,L-lactic acid (or rac-lactide) as the reactant monomer. The syntheses involving homogeneous and heterogeneous catalytic processes to produce poly(D,L-Lactic acid) (PDLLA) are also addressed. Additionally, the production of blends, copolymers, and composites with PDLLA are also presented exemplifying different preparation methods. Some general applications of these materials mostly dedicated to the biomedical area over the last 10-15 years will be pointed out.