Ultrasound and Microwave-Assisted Synthesis of Hexagonally Ordered Ce-Promoted Mesoporous Silica as Ni Supports for Ethanol Steam Reforming.

Solvothermal synthesis of mesoporous materials based on amphiphilic molecules as structure-directing agents can be enhanced using non-conventional technologies for stirring and thermal activation. Here, we disclose a green synthesis approach for the preparation of cerium-modified hexagonally ordered silica sieves. Ultrasound micromixing enabled us to obtain well-dispersed Ce in the self-assembled silica network and yielded ordered materials with high cerium content (Ce/Si molar ratio = 0.08). Microwave dielectric heating, applied by an innovative open-end coaxial antenna, was used to reduce the overall hydrothermal synthesis time and to improve the surface area and textural properties. These mesoporous materials were used as a Ni catalyst support (10 wt.% metal loading) for the ethanol steam reforming reaction. The new catalysts featured complete ethanol conversion, high H2 selectivity (65%) and better stability, compared to the same catalyst prepared with magnetic stirring and conventional heating. The Ce-promoted silica sieves offered a suitable support for the controlled growth of nanocarbon that does not result in catalyst deactivation or poisoning after 6 h on stream.

Desorption of Furfural from Bimetallic Pt-Fe Oxides/Alumina Catalysts.

In this work, the desorption of furfural, which is a competitive intermediate during the production of biofuel and valuable aromatic compounds, was studied using pure alumina, as well as alumina impregnated with iron and platinum oxides both individually and in combination, using thermogravimetric analysis (TGA). The bimetallic sample exhibited the lowest desorption percentage for furfural. High-resolution transmission electron microscopy (HRTEM) imaging revealed the intimate connection between the iron and platinum oxide species on the alumina support. The mechanism of furfural desorption from the Pt-Fe/Al2O3 0.5%-0.5% sample was determined using physisorbed furfural instead of chemisorbed furfural; this mechanism involved the oxidation of the C=O group on furfural by the catalyst. The oxide nanoparticles on γ-Al2O3 support helped to stabilize the furfural molecule on the surface.