Use of 1,3-diaminepropane-3-propyl grafted onto a silica gel as a sorbent for flow-injection spectrophotometric determination of copper (II) in digests of biological materials and natural waters.

The 1,3-diaminepropane-3-propyl-anchored silica gel (DAPPS) was successfully employed as a sorbent in a spectrophotometric flow system for the preconcentration of Cu(2+) in digests of biological materials (maize powder, soybean, citrus leaves, corn stalks) as well as water samples (river, stream, streamlet, springwater and well). The system presented a minicolumn packed with DAPPS, where the sample solution was passed through it for a period of time, and subsequently, an eluent solution, stripped-out the retained analyte which was further determined with DDTC at 460 nm. The better preconcentration conditions utilized were: 120s loading, 60s elution, 30s regeneration of the column, loading flow rate 6.5 ml min(-1), buffer solution for the preconcentration and regeneration of the column-borate buffer pH 8.5, elution flow rate 2.3 ml min(-1), time of elution 60s, eluent composition, 0.4 mol l(-1) HNO(3). Under these conditions, the preconcentration factor obtained was 36, and the detection limit achieved was 8.4 ng ml(-1) in water samples and 0.84 microg g(-1) in biological material. The maximum adsorption capacity of DAPPS to Cu(2+) was 0.49 mmol g(-1) (31.1 mg g(-1)) obtained in a batch system. The recovery of copper in the water samples ranged from 96.9 to 102.4% and in the biological materials ranged from 97.0 to 102.6%.

7-amino-4-azaheptyl grafted onto a silica gel as a sorbent for the on-line preconcentration and determination of iron(III) in water samples.

A new sorbent was synthesized by anchoring 7-amino-4-azaheptyltrimetoxisilane, freshly prepared, to silica gel, producing 7-amino-4-azaheptyl anchored silica gel (AAHSG). This material was characterized by infrared spectroscopy (IR), elemental analysis (CHN), and nitrogen adsorption-desorption isotherms. Isotherms of the adsorption of Fe3+, Fe2+ and Cu2+ on AAHSG were recorded, which indicated that Fe3+ presents a higher affinity by the sorbent. Therefore, AAHSG was successfully employed as a sorbent in a simple flow system for the preconcentration of Fe3+ in natural water samples, such as, river water, lagoonwater, springwater, stream water, well water and two water reference materials (NIST-SRM 1640, NIST-SRM 1643d). The obtained preconcentration factor was 82.2, and the detection limit achieved was 5.9 ng ml(-1). The recovery of spiked water samples ranged from 95.0 - 103.1%.

Silica-titania sol-gel hybrid materials: synthesis, characterization and potential application in solid phase extraction.

The biphenilaminepropylsilica and biphenilaminepropylsilicatitania were synthesized by sol-gel method, in two steps: (a) biphenylamine reacts with chloropropyltrimethoxysilane and (b) the product of reaction was polycondensed with tetraethylorthosilicate (TEOS) or TEOS and titanium isopropoxide. The sol-gel materials were characterized using infrared spectroscopy and N(2) adsorption-desorption isotherms and they were employed as sorbents for carcinogenic N-containing compound retention, in aqueous solution, using the SPE technique. The N-containing compounds adsorption was influenced by the titania presence and the sorption process seems to happen in the pores with higher organic density.