Copper recovery by solvent extraction for nanoparticle synthesis from waste motherboards.

Printed circuit boards, which make up part of waste from electrical and electronic equipment, contain elements that can be economically reused, such as copper, silver, gold, and nickel, as well as metals that are harmful to the environment and health, such as lead, mercury, and cadmium. Thus, through recycling this scrap, materials that would otherwise be discarded can be reinserted as secondary raw materials to produce new consumer goods through urban mining. In this context, the synthesis of nanoparticles shows promise as it allows the reinsertion of these materials in the manufacture of new products. Therefore, this study used obsolete computer motherboards as a secondary material to obtain copper to produce nanoparticles of this metal. From a solution based on the leach liquor of this scrap, a purification route using solvent extraction was defined and applied to the real leach liquor. Applying the hydroxyoxime extractant at a dilution of 20% (v/v) in kerosene, A/O of 1/1, 298 K, and 0.25 h of contact during extraction, and stripping in H2SO4 (2 M), 298 K, 0.25 h, W/O ratio of 3/1, and two theoretical countercurrent stages, a solution containing more than 95% of the copper in the leach liquor could be obtained with less than 1% of contaminants. From this purified liquor, nanoparticles containing copper and metallic copper oxides and hydroxides were produced, with an average size of 84 nm, at pH 11, 3 h of hot stirring, volume of 0.015 L of ascorbic acid (0.50 M) and 0.015 L of precursor solution (0.03 M Cu), and temperature (343 K).

Recycling of WEEE: characterization of spent printed circuit boards from mobile phones and computers.

This paper presents a comparison between printed circuit boards from computers and mobile phones. Since printed circuits boards are becoming more complex and smaller, the amount of materials is constantly changing. The main objective of this work was to characterize spent printed circuit boards from computers and mobile phones applying mineral processing technique to separate the metal, ceramic, and polymer fractions. The processing was performed by comminution in a hammer mill, followed by particle size analysis, and by magnetic and electrostatic separation. Aqua regia leaching, loss-on-ignition and chemical analysis (inductively coupled plasma atomic emission spectroscopy - ICP-OES) were carried out to determine the composition of printed circuit boards and the metal rich fraction. The composition of the studied mobile phones printed circuit boards (PCB-MP) was 63 wt.% metals; 24 wt.% ceramics and 13 wt.% polymers; and of the printed circuit boards from studied personal computers (PCB-PC) was 45 wt.% metals; 27 wt.% polymers and ceramics 28 wt.% ceramics. The chemical analysis showed that copper concentration in printed circuit boards from personal computers was 20 wt.% and in printed circuit boards from mobile phones was 34.5 wt.%. According to the characteristics of each type of printed circuit board, the recovery of precious metals may be the main goal of the recycling process of printed circuit boards from personal computers and the recovery of copper should be the main goal of the recycling process of printed circuit boards from mobile phones. Hence, these printed circuit boards would not be mixed prior treatment. The results of this paper show that copper concentration is increasing in mobile phones and remaining constant in personal computers.