ABSTRACT
Background: The development of early carious lesions can be prevented with the use of sealants. This study aimed to evaluate the retention and sealant quality of conventional and bioactive self-etching sealants by direct (clinical) and indirect (microscopical) assessment. Materials and Methods: Sixty newly erupted mandibular second molars (International Caries Detection and Assessment System ≤2) from adolescents were selected for the split-mouth trial study. The tooth was randomized and treated with conventional Fluoroshield (FS) and BeautiSealant (BS) bioactive self-etching sealants. Molds were taken and cast with epoxy resin after treatment. Indirect and direct assessments of retention degree and sealant remnant quality were performed after baseline, 1 month, and 1 year. The Chi-square test, ordinal regression, reasons of chance, and Fleiss' kappa statistical test were employed. Results: After 1 month, greater total retention was observed for FS, but 1-year follow-up demonstrated no retention difference for FS and BS. The odds ratios showed an 86% greater chance of FS showing better marginal adaptation, after 1 month. At 1 year, the clinical assessment showed better anatomical shape and marginal adaptation scores for FS, but no microscopical difference was observed. A pour agreement between clinical and microscopical data was observed. Conclusions: The 1-year follow-up showed no significant difference in the degree of retention, and in the microscopic evaluation of the conventional sealant (FS) and the bioactive self-etching sealant (BS), but in the clinical evaluation, better marginal and anatomical adaptation scores for FS were observed.
ABSTRACT
OBJECTIVE: The aim of this study was to evaluate in vitro bond strength of metal brackets bonded with: total etch, total etch with erbium: yttrium aluminum garnet laser (Er:YAG) and self-etching adhesive systems, submitted to thermal-mechanical cycling, simulating 1 year of orthodontic treatment. MATERIALS AND METHODS: For the study, 80 bovine incisors were randomly divided into 3 experimental groups (n=16 each): XT- acid etching + Transbond XT, XT/Er:YAG- Transbond XT associated with Er:YAG laser irradiation (λ=2.94 µm, 60 mJ, 10 Hz) and SEP- Transbond Plus Self Etching Primer. Samples were submitted to thermal-mechanical cycling, simulating 1 year of orthodontic treatment. Afterward, the shear bond strength test was performed in a universal test machine at a speed of 0.5mm/min. Samples were evaluated under a stereomicroscope and by scanning electron microscopy for analysis of enamel surface and adhesive remnant index. Data were analyzed using Kruskal-Wallis and Mann-Whitney (with Bonferroni correction) statistical tests. RESULTS: Statistically significant difference was observed between the groups studied (p<0.05). Groups XT and SEP showed the highest bond strength values, without statistical difference between them, while group XT/Er:YAG showed reduction in bond strength values. Higher frequency of adhesive failures between enamel and adhesive system was verified for groups XT and XT/Er:YAG. CONCLUSION: The conventional (XT) and self-etching (SEP) adhesive systems showed mean bond strength values, similar between them, whereas the previous application of Er:YAG laser promoted the lowest bond strength values.