Improving the performance of ASA in the DAC of 2,5-DMF and ethylene.

A variety of methods are employed to synthesize amorphous silica-alumina (ASA) to resolve the role of Al speciation and surface area in the catalytic performance in the Diels-Alder cycloaddition reaction of 2,5-dimethylfuran and ethylene to p-xylene. ASA was prepared by homogeneous deposition-precipitation (HDP) of Al3+ on ordered mesoporous silica, i.e., SBA-15 and OMS prepared under hydrothermal synthesis conditions using an imidazole-based template, and one-step flame spray pyrolysis (FSP). IR spectroscopy and 27Al MAS NMR showed that the resulting ASA represented a set of materials with distinct textural and acidic properties. ASA prepared by grafting Al to ordered mesoporous silica led to a much higher concentration of Brønsted acid sites (BAS). These samples performed much better in the DAC reaction, with p-xylene yields higher than those obtained with a HBeta zeolite benchmark. Materials with Al partially in the bulk of silica (OMS, FSP) and containing significant alumina domains are less acidic and exhibit much lower p-xylene yields. These findings point to the importance of Brønsted acidity for p-xylene formation. This study shows that careful design of the Al speciation can lead to amorphous silica-alumina with similar DAC performance to microporous zeolites.

Structure Sensitivity of CO2 Hydrogenation on Ni Revisited.

Despite the large number of studies on the catalytic hydrogenation of CO2 to CO and hydrocarbons by metal nanoparticles, the nature of the active sites and the reaction mechanism have remained unresolved. This hampers the development of effective catalysts relevant to energy storage. By investigating the structure sensitivity of CO2 hydrogenation on a set of silica-supported Ni nanoparticle catalysts (2-12 nm), we found that the active sites responsible for the conversion of CO2 to CO are different from those for the subsequent hydrogenation of CO to CH4. While the former reaction step is weakly dependent on the nanoparticle size, the latter is strongly structure sensitive with particles below 5 nm losing their methanation activity. Operando X-ray diffraction and X-ray absorption spectroscopy results showed that significant oxidation or restructuring, which could be responsible for the observed differences in CO2 hydrogenation rates, was absent. Instead, the decreased methanation activity and the related higher CO selectivity on small nanoparticles was linked to a lower availability of step edges that are active for CO dissociation. Operando infrared spectroscopy coupled with (isotopic) transient experiments revealed the dynamics of surface species on the Ni surface during CO2 hydrogenation and demonstrated that direct dissociation of CO2 to CO is followed by the conversion of strongly bonded carbonyls to CH4. These findings provide essential insights into the much debated structure sensitivity of CO2 hydrogenation reactions and are key for the knowledge-driven design of highly active and selective catalysts.

Carbon dioxide and nitrate co-electroreduction to urea on CuOxZnOy.

Urea is a commonly used nitrogen fertiliser synthesised from ammonia and carbon dioxide using thermal catalysis. This process results in high carbon dioxide emissions associated with the required amounts of ammonia. Electrocatalysis provides an alternative method to urea production with reduced carbon emissions while utilising waste products like nitrate. This manuscript reports on urea synthesis from the electroreduction of nitrate and carbon dioxide using CuOxZnOy electrodes under mild conditions. Catalysts with different ratios of CuO and ZnO, synthesised via flame spray pyrolysis, were explored for the reaction. The results revealed that all the CuOxZnOy electrocatalyst compositions produce urea, but the efficiency strongly depends on the metal ratio composition of the catalysts. The CuO50ZnO50 composition had the best performance in terms of selectivity (41% at -0.8 V vs RHE) and activity (0.27 mA/cm2 at -0.8 V vs RHE) towards urea production. Thus, this material is one of the most efficient electrocatalysts for urea production reported so far. This study systematically evaluates bimetallic catalysts with varying compositions for urea synthesis from carbon dioxide and nitrate.