ABSTRACT
The aim of the this study was to quantitatively evaluate in three-dimensional (3D), the porosity degree of three improved silicate-based endodontic repair cements (iRoot BP Plus®, Biodentine®, and Ceramicrete) compared to a gold-standard calcium silicate bioactive cement (Pro Root® MTA). From each tested cement, four samples were prepared by a single operator following the manufacturer's instructions in terms of proportion, time, and mixing method, using cylindrical plastic split-ring moulds. The moulds were lubricated and the mixed cements were inserted with the aid of a cement spatula. The samples were scanned using a compact micro-CT device (Skyscan 1174, Bruker micro-CT, Kontich, Belgium) and the projection images were reconstructed into cross-sectional slices (NRecon v.1.6.9, Bruker micro-CT). From the stack of images, 3D models were rendered and the porosity parameters of each tested material were obtained after threshold definition by comparison with standard porosity values of Biodentine®. No statistically significant differences in the porosity parameters among the different materials were seen. Regarding total porosity, iRoot BP Plus® showed a higher percentage of total porosity (9.58%), followed by Biodentine® (7.09%), Pro Root® MTA (6.63%), and Ceramicrete (5.91%). Regarding closed porosity, Biodentine® presented a slight increase in these numbers compared to the other sealers. No significant difference in porosity between iRoot BP Plus®, Biodentine®, and Ceramicrete were seen. In addition, no significant difference in porosity between the new calcium silicate-containing repair cements and the gold-standard MTA were found.