ABSTRACT
ABSTRACT: The present study analyzed the color change (DE) and surface roughness (Ra) of glass ionomer cements (GICs) subjected to typical herbaceous South American beverage action - Ilex paraguariensis. 90 specimens (n = 10) were made: M1 - GIC Riva Light Cure® (SDI); M2 - GIC Riva Self Cure® (SDI); M3 - GIC Vitremer® (3M ESPE). After light curing/ polymerization of GICs, specimens were divided for being submitted to solutions for one hour a day for 21 days: S1 - Yerba Mate Pajarito Traditional (Pajarito); S2 - Erva Mate Chimarrão (Barão de Cotegipe); S3 - Water (control). Four DE and Ra readings were taken: T0 - initial; T1 - 7 days; T2 - 14 days and T3 - 21 days, with a spectrophotometer and a roughness meter respectively. The obtained data were submitted to ANOVA statistical analysis and Bonferroni. S1 and S2 at T1 and T2 there was no statistical difference between the materials, and at T3 Materials M1=M2, M1=M3, and M2>M3. For S3 at T1, T2 and T3 there was no difference between the materials. Analyzing surface roughness, there was no statistical significance. Concluded that all materials changed color with greater influence of time, but without changing surface roughness.
RESUMEN: En el presente estudio se analizó el cambio de color (DE) y la rugosidad superficial (Ra) de los cementos ionómero de vidrio (CIV) sometidos a la acción típica de las bebidas herbáceas sudamericanas - Ilex paraguariensis. Se realizaron 90 especímenes (n = 10): M1 - GIC Riva Light Cure® (SDI); M2 - GIC Riva Self Cure® (SDI); M3 - GIC Vitremer® (3M ESPE). Después de la fotopolimerización/ polimerización de los CIV, los especímenes se dividieron y fueron sometidos a soluciones durante una hora al día durante 21 días: S1 - Yerba Mate Pajarito Tradicional (Pajarito); S2 - Erva Mate Chimarrão (Barão de Cotegipe); S3 - Agua (control). Se tomaron cuatro lecturas de DE y Ra: T0 - inicial; T1 - 7 días; T2 - 14 días y T3 - 21 días, con espectrofotómetro y rugosímetro respectivamente. Los datos obtenidos fueron sometidos a análisis estadístico ANOVA y Bonferroni. S1 y S2 en T1 y T2 no hubo diferencia estadística entre los materiales y en T3 Materiales M1=M2, M1=M3 y M2>M3. Para S3 en T1, T2 y T3 no hubo diferencia entre los materiales. Al analizar la rugosidad de la superficie, no hubo significación estadística. En conclusion, todos los materiales cambiaron de color con mayor influencia del tiempo, pero sin cambiar la rugosidad de la superficie.
ABSTRACT
El objetivo de la revisión fue conocer las propiedades y la aplicación clínica de los diferentes ionómeros de vidrio de alta densidad disponibles en Lima-Perú. Se realizó una revisión de la literatura científica desde enero 2010 hasta diciembre 2019 acerca de los ionómeros de vidrio de alta densidad. Esta revisión se realizó en las bases de datos SciELO, Pubmed y Google Scholar. Los descriptores para realizar la búsqueda fueron: cementos de ionómero de vidrio, ionómeros de vidrio de alta densidad y propiedades físicas, las combinaciones entre ellos y su equivalente en inglés. Se seleccionaron finalmente 40 artículos que cumplieron con los criterios de inclusión. Dentro de las marcas de ionómeros de alta densidad disponibles en Lima-Perú se encuentran: Ionofil® Plus (VOCO), KetacTM Molar Easymix (3M ESPE), Fuji IX GP (GC corporation) y EQUIA Forte™®GC (Europe GC). Se presentan las propiedades y aplicación clínica de todos estos ionómeros. De acuerdo a la revisión de la literatura, de los cinco grupos estudiados: EQUIA Forte presentó una excelente adhesión al esmalte y la dentina. Fuji IX GP puede ser usado en restauraciones de Clase I y II, sin contactos oclusales y; EQUIA Forte puede utilizarse en pequeñas Clase II con /sin contactos oclusales, y con cuidado en grandes cavidades MOD siguiendo las recomendaciones del fabricante.
The objective of the review was to understand the properties and clinical application of the different high-density glass ionomers available in Lima, Perú. A review of the scientific literature about high-density glass ionomers, was conducted from January 2010 to December 2019. This review was performed in SciELO, Pubmed and Google Scholar databases. The descriptors used in the search were: glass ionomer cements, high density glass ionomers and physical properties, the combinations between them and their equivalent in English. Ultimately forty articles that met the inclusion criteria, were selected. The high-density ionomers available in Lima-Peru are Ionofil® Plus (VOCO), KetacTM Molar Easymix (3M ESPE), Fuji IX GP (GC corporation) and EQUIA Forte™® GC (Europe GC). The properties and clinical application of all these ionomers are presented. According to the literature review, of the five groups studied; EQUIA Forte presented excellent adhesion to enamel and dentin. Fuji IX GP can be placed in Class II restorations without occlusal contacts and EQUIA Forte can be used in small Class II with / without occlusal contacts, and cautiously in large MOD cavities following the manufacturer's recommendations.
ABSTRACT
ABSTRACT: The glass ionomer cements (GICs) is a generic name given to a group of materials widely used in clinical dentistry which if used after the specified expiration date, material properties may be affected. to evaluate the Vick ers microhardness, surface morphology and the energy dispersive X-ray microanalysis (EDX), of GICs with different expiration dates that were stored at room temperature. specimens of highly viscous glass ionomer cement (HVGIC) (Ketac Cem and Ketac Molar) and resin-modified glass ionomer cement (RMGIC) (Vitrebond) with different expiration dates (current, close to their expiration and expired) were prepared for Vickers microhardness test and scanning electronic microscopy (SEM) with EDX, measuring 5 mm in diameter and 2 mm length, per the manufacturer's instructions, in standard cylindrical teflon molds. For the comparison of obtained values, the ANOVA test was used, while Tukey test was used for the multiple comparisons. In all the GICs used, the microhardness decreased as the expiration date approached, finding a significant statistical differen ce (P<0.05) in Ketac Molar and Vitrebond. SEM sample analysis revealed similar cohesive cracks in all tested materials. The EDX analysis revealed the presence of the elements F, Al and Si in all GICs and Ca only in Ketac Molar and Ketac Cem. The elements were found in a higher atomic percentage in the GICs with an current date and in a lower percentage in those with an expired date. HVGIC and RMGIC with an expiration date finish and that were stored at room temperature, suffer significant physical and chemical changes, which could put doubts its clinical effectiveness.
RESUMEN: El cemento de ionómero de vidrio (CIV) es un nombre genérico que se le da a un grupo de materiales ampliamente utilizados en odontología clínica que si se usan después de la fecha de vencimiento especificada, las propiedades del material pueden verse afectadas. evaluar la microdureza Vickers, la morfología superficial y el microanálisis de energía dispersa de rayos X (EDX), de CIV con diferentes fechas de caducidad almacenados a temperatura ambiente. Muestras de cemento de ionómero de vidrio de alta viscosidad (CIVAV) (Ketac Cem y Ketac Molar) y cemento de ionómero de vidrio modificado con resina (CIVMR) (Vitrebond) con diferentes fechas de vencimiento (vigente, próximo a su vencimiento y vencido) de 5 x 2 mm, fueron preparadas para microscopía electrónica de barrido (MEB) con EDX y microdureza Vickers, según las instrucciones del fabricante, en moldes de teflón cilíndricos estándar. Para la comparación de los valores obtenidos se utilizó la prueba ANOVA, mientras que para las comparaciones múltiples se utilizó la prueba de Tukey. En todos los CIV utilizados, la microdureza disminuyó a medida que se acercaba la fecha de vencimiento, encontrándose una diferencia estadística significativa (P <0.05) en Ketac Molar y Vitrebond. El análisis de la muestra en MEB reveló grietas cohesivas similares en todos los materiales probados. El análisis EDX reveló la presencia de los elementos F, Al y Si en todos los GIC y Ca solo en Ketac Molar y Ketac Cem. Los elementos se encontraron en mayor porcentaje atómico en los GIC con fecha vigente y en menor porcentaje en aquellos con una fecha vencida. Los CIVAV y CIVMR con fecha de caducidad vencida y que fueron alma- cenados a temperatura ambiente, sufrieron cambios físicos y químicos importantes, lo que podría poner en duda su efectividad clínica.
ABSTRACT
ABSTRACT Secondary caries is an important factor in the replacement of the restorations, and it is thought that fluoride-releasing materials may prevent this problem. Furthermore, the fluoride release of the materials may be increased by polishing process. Available knowledge about the effect of polishing systems (PS) on the fluoride release of materials is limited. Therefore, this study was conducted to evaluate the effect of PS on the fluoride release of fluoride-containing materials. Restorative materials were divided into 6 groups: Fuji IX GP, Fuji II, Dyract XP, Beautifil II, Beautifil-Bulk, and Filtek Ultimate. Each group was also divided into four subgroups: Mylar strip, Sof-Lex Discs, Sof-Lex Diamond, and OneGloss. Fluoride release was determined using a fluoride ion-selective electrode. Surface roughness was evaluated with a profilometer. Two- way repeated measure and one-way ANOVA tests were used for statistical analysis. The initial rapid fluoride release was observed only in Fuji IX. The PS increased the fluoride release of Fuji IX and Fuji II and Dyract XP materials while reducing the fluoride release of resin-based materials. The highest surface roughness values were obtained with OneGloss. Further, a significant relationship between fluoride release and surface roughness was found. The polishing provides an increase in fluoride release, especially in glass-ionomer-based materials. This article revealed that there is a relationship between fluoride release and surface roughness. Proper PS must be chosen according to the material to provide the best clinical benefits in terms of fluoride release and surface roughness.
RESUMEN La caries secundaria es un factor importante para el reemplazo de restauraciones y se considera que los materiales que liberan flúor pueden prevenir este problema. Además, la liberación de fluoruro de estos materiales podría incrementarse mediante el proceso de pulido. El conocimiento disponible sobre el efecto de los sistemas de pulido (SP) en la liberación de fluoruro de los materiales es limitado. Por lo tanto, este estudio se realizó para evaluar el efecto de los SP sobre la liberación de fluoruro de materiales que contienen fluoruro. Los materiales de restauración se dividieron en 6 grupos: Fuji IX GP, Fuji II, Dyract XP, Beautifil II, Beautifil-Bulk y Filtek Ultimate. Cada grupo también se dividió en cuatro subgrupos: Banda Mylar, Discos Sof-Lex, Sof-Lex Diamond y OneGloss. La liberación de fluoruro se determinó usando un electrodo selectivo de iones fluoruro. La rugosidad de la superficie se evaluó con un perfilómetro. Se utilizaron medidas repetidas bidireccionales y pruebas ANOVA de una vía para el análisis estadístico. La liberación inicial rápida de fluoruro se observó solo en Fuji IX. El SP aumentó la liberación de fluoruro de los materiales Fuji IX y Fuji II y Dyract XP al tiempo que redujo la liberación de fluoruro de los materiales a base de resina. Los valores más altos de rugosidad de la superficie se obtuvieron con OneGloss. Además, se encontró una relación significativa entre la liberación de fluoruro y la rugosidad de la superficie. El pulido proporciona un aumento en la liberación de fluoruro, especialmente en materiales a base de ionómero de vidrio. Este artículo reveló que existe una relación entre la liberación de fluoruro y la rugosidad de la superficie. El SP adecuado debe elegirse de acuerdo con el material para proporcionar los mejores beneficios clínicos en términos de liberación de fluoruro y rugosidad de la superficie.