In vitro cytotoxicity of resin cement and its influence on the expression of antioxidant genes / Avaliação in vitro da toxicidade de cimentos resinosos e sua influência na expressão de genes antioxidantes em fibroblastos humanos

ABSTRACT Aim: This study evaluated cytotoxicity and antioxidant gene expression of resin cements on human gingival fibroblasts (hGF). Materials and Method: RelyX Ultimate™(RXU), Variolink™II(VLII), and RelyXU200™(RXU200) resin cements were incubated with culture medium for 24 h to obtain eluates. Then, the eluates were applied over hGF to assess cell viability at 24 h, 48 h, and 72 h and antioxidant gene expression at 24 h. hGF cultures non-exposed to the eluates were used as Control. Data were submitted to ANOVA and Bonferroni tests (α≤0.05). Results: RXU and RXU200 reduced the number of viable cells in 24 h. Longer exposure to cement extracts caused cell death. Gene expression showed peroxiredoxin 1 (PRDX1) induction by all resin cement types, and superoxide dismutase 1 (SOD1) induction by RXU200 and VLII. Moreover, RXU200 induced not only PRDX1 and SOD1, but also glutathione peroxidase 1 (GPX1), catalase (CAT), and glutathione synthetase (GSS). Conclusions: All resin cements showed toxicity, and induced antioxidant genes in hGF. Antioxidant gene induction is at least partly associated with cytotoxicity of tested cements to oxidative stress experience.

RESUMO Objetivo: O objetivo deste estudo foi avaliar a toxicidade dos cimentos resinosos Rely X Ultimate 2, Rely X U200 e Variolink II, bem como sua influência na expressão de genes antioxidantes em fibroblastos gengivais humanos. Materiais e Método: Corpos de prova de cada cimento foram colocados em meio de cultura por 24 h e os extratos correspondentes foram aplicados aos fibroblastos. A viabilidade celular foi avaliada após 24, 48 e 72 h de exposição pelo ensaio de exclusão do azul de tripano e MTT. A expressão gênica foi avaliada por PCR quantitativo após 24 h de exposição aos extratos. Estes parâmetros foram comparados aos das células não expostas aos cimentos. Os dados foram submetidos ao teste ANOVA, seguido pelo pós-teste de Bonferroni (a≤0.05). Resultados: Os resultados demonstraram que todos os cimentos promoveram redução do número de células viáveis e da atividade mitocondrial nos períodos de 48 e de 72 h (p < 0,01), sendo que o Variolink II apresentou o menor efeito e os cimentos Rely X Ultimate e Rely X U200 promoveram similarmente os maiores efeitos. A análise de expressão gênica evidenciou influência significativa em todos os cimentos avaliados sobre os níveis de transcritos de PRDX1, SOD1, GPX1 e GSS (p> 0,05), com um aumento considerável no Rely X U200. Conclusão: A indução de genes antioxidantes está, pelo menos em parte, associada à citotoxicidade dos cimentos testados para a experiência de estresse oxidativo.

Tratamento restaurador traumático (ART): uma alternativa de mínima intervenção para lesões de cárie / Atraumatic Restorative Treatment (ART): a minimal intervention alternative for caries injuries

Este trabalho teve como objetivo demonstrar a importância do Tratamento Restaurador Atraumático (ART) na Odontologia, assim como compreender sua contextualização histórica, descrever suas vantagens e desvantagens, conhecer suas indicações e limitações e seu protocolo. Foram selecionados artigos científicos publicados em português e inglês, disponíveis nas bases de dados MEDLINE, SciELO e Google Acadêmico, tendo sido incluídos artigos dos últimos dez anos, utilizando os descritores: "Tratamento Dentário Restaurador sem Trauma", "Cárie dentária", "Cimento de Ionômero de Vidro" e "Avaliação da Promoção de Saúde". O tratamento restaurador Atraumático (ART), consiste na empregabilidade de uma técnica que tem como finalidade combater a doença cárie e promover saúde. Resume-se em uma abordagem de gerenciamento para lesões de cárie com mínimos preparos, sendo utilizados apenas instrumentos manuais para remoção da dentina infectada, a exemplo a colher de dentina, sendo finalizada posteriormente com cimento de ionômero de vidro para selar a cavidade. As principais vantagens estão relacionadas a sua aplicação, sendo pregada como uma técnica de fácil execução, procedimento rápido, apresenta baixo custo, devido à necessidade mínima de materiais que são utilizados, dispensa a utilização da energia elétrica, pode ser feita em diversos ambientes. Diante da literatura compreende-se que ART é uma técnica de grande importância para o gerenciamento e declínio da doença cárie em diversos âmbitos odontológico, capaz de proporcionar grandes vantagens positiva para abordagem odontológica, tornando o atendimento menos estressante, mais colaborativo e rápido.

This study aimed to demonstrate the importance of Atraumatic Restorative Treatment (ART) in Dentistry, as well as to understand its historical context, describe its advantages and disadvantages, know its indications and limitations and its protocol. Scientific articles published in Portuguese and English, available in the MEDLINE, SciELO and Google Scholar databases were selected, including articles from the last ten years, using the descriptors: "Restorative Dental Treatment without Trauma", "Dental Caries", "Glass Ionomer Cement" and "Evaluation of Health Promotion". The Atraumatic Restorative Treatment (ART) consists of the employability of a technique that aims to combat caries and promote health. It is summarized in a management approach for caries lesions with minimal preparations, using only manual instruments to remove the infected dentin, such as the dentin spoon, being finished later with glass ionomer cement to seal the cavity. The main advantages are related to its application, being preached as a technique of easy execution, quick procedure, low cost, due to the minimum need for materials that are used, it does not require the use of electricity, it can be performed in different environments. In view of the literature, it is understood that ART is a technique of great importance for the management and decline of caries in various dental areas, capable of providing great positive advantages for the dental approach, making care less stressful, more collaborative and faster.

Outcomes of Extended Curettage with and without Bone Allograft for Grade II Giant Cell Tumors around the Knee. A Retrospective Comparative Study / Resultados da curetagem estendida com e sem aloenxerto ósseo para tumores de células gigantes de grau II no joelho. Um estudo comparativo retrospectivo

Abstract Objective This is the first study to establish the utility of extended curettage with or without bone allograft for Grade II giant cell tumors GCTs around the knee joint with the aim of exploring postoperative functional outcomes. Methods We retrospectively reviewed 25 cases of Campanacci grade II GCTs undergoing extended curettage between January 2014 and December 2019. The participants were divided into two groups: one group of 12 patients underwent extended curettage with bone allograft and bone cement, while the other group of 13 patients underwent extended curettage with bone cement only. Quality of life was assessed by the Revised Musculoskeletal Tumor Society Score and by the Knee score of the Knee Society; recurrence and complications were assessed for each cohort at the last follow-up. The Fisher test and two-sample t-tests were used to compare the categorical and continuous outcomes, respectively. Results The mean age was 28.09 (7.44) years old, with 10 (40%) males and 15 females (60%). The distal femur and the proximal tibia were involved in 13 (52%) and in 12 (48%) patients, respectively. There was no significant difference in the musculoskeletal tumor society score (25.75 versus 27.41; p= 0.178), in the knee society score (78.67 versus 81.46; p= 0.33), recurrence (0 versus 0%; p= 1), and complications (25 versus 7.69%; p= 0.21). Conclusions Extended curettage with or without bone allograft have similar functional outcomes for the knee without any major difference in the incidence of recurrence and of complications for Grade II GCTs. However, surgical convenience and cost-effectiveness might favor the bone cement only, while long-term osteoarthritis prevention needs to be investigated to favor bone allograft.

Resumo Objetivo Este é o primeiro estudo a estabelecer a utilidade da curetagem estendida com ou sem enxerto ósseo em tumores de células gigantes (TCGs) de grau II na articulação do joelho com o objetivo de explorar os resultados funcionais pós-operatórios. Métodos Revisamos retrospectivamente 25 casos de TCGs de grau II de Campanacci submetidos a curetagem estendida entre janeiro de 2014 e dezembro de 2019. Os participantes foram divididos em 2 grupos: um grupo de 12 pacientes foi submetido a curetagem estendida com aloenxerto ósseo e cimento ósseo, enquanto o outro grupo, com 13 pacientes, foi submetido a curetagem estendida apenas com cimento ósseo. A qualidade de vida foi avaliada pela Pontuação Revista da Musculoskeletal Tumor Society (MTS, na sigla em inglês) e pela Pontuação da Knee Society (KS, na sigla em inglês), enquanto as taxas de recidiva e complicações foram avaliadas em cada coorte na última consulta de acompanhamento. O teste de Fisher e os testes t de duas amostras foram usados para comparação de resultados categóricos e contínuos, respectivamente Resultados A média de idade dos pacientes foi de 28,09 (7,44) anos; 10 (40%) pacientes eram do sexo masculino e 15 (60%) pacientes eram do sexo feminino. O fêmur distal e a tíbia proximal foram acometidos em 13 (52%) e 12 (48%) dos pacientes, respectivamente. Não houve diferença significativa na pontuação revista da MTS (25,75 versus 27,41; p= 0,178), na pontuação da KS (78,67 versus 81,46; p= 0,33) e nas taxas de recidiva (0 versus 0%; p= 1) e complicações (25 versus 7,69%; p= 0,21). Conclusões A curetagem estendida com ou sem aloenxerto ósseo tem resultados funcionais semelhantes em pacientes com TCGs de grau II no joelho, sem qualquer diferença importante na incidência de recidivas e complicações. No entanto, a conveniência cirúrgica e o custo-benefício podem favorecer a utilização apenas de cimento ósseo, enquanto a prevenção da osteoartrite em longo prazo precisa ser investigada para favorecer o enxerto ósseo.

Establishing an experimental agenda at the Accademia del Cimento: Carlo Rinaldini's book lists.

Information on the origins of the Accademia del Cimento is extremely limited. Almost all of the surviving correspondence relating to the year before the Academy began its activities variously concerns print culture. Lists of books (read, studied, purchased, and researched), handwritten notes on old or new publications, vernacular translations of edited passages, and inquiries about new works punctuate the archive. The study of these lists and of the relationship between reading practices and ones related to annotation and knowledge production leads to a reinterpretation of certain aspects of the Accademia del Cimento, suggesting the pursuit of a more flexible agenda.Through the analysis of some book lists, this contribution aims to shed light on the presence in Florence of interconnected groups of scholars, common epistemic practices, and a kind of methodological unity centred on the sharing of materials and agreement concerning the need to subject theories to experimental verification.

Color stability and degree of conversion of amine-free dual cured resin cement used with two different translucencies of lithium disilicate ceramics / Estabilidade de cor e grau de conversão de cimento resinoso dual sem amina usado com duas translucidezes diferentes de cerâmica de dissilicato de lítio

Objective: The present study aims to evaluate the color stability and degree of conversion of amine-free dual cured resin cement compared to light cured and amine-containing dual cured resin cements used with two different translucencies of thin esthetic restorations. Material and Methods: A total of 120 specimens were prepared for color stability testing (n=60). The specimens were divided into three main groups according to the resin cement type. Group 1: amine-free dual cured, Group 2: light cured, Group 3: amine-containing dual cured. Each group was further subdivided according to the ceramic translucency into two subgroups: high and low translucency. Color stability was assessed by a spectrophotometer before and after thermal aging. For the degree of conversion assessment (n=60), Fourier transform infrared spectroscopy was used at three different time intervals. Statistical analysis was performed using multi-factorial ANOVA, followed by one-way ANOVA with Bonferroni correction. Results: Amine-containing resin cement showed significantly higher ΔEab and ΔE00in both translucencies (4.5±0.3, 3.5±0.3 respectively for high translucency ceramic and 3.8±0.4, 3.0±0.3 respectively for low translucency) than the other tested cements (p<0.001). The highest degree of conversion (DC) was shown after 2 weeks by the amine-free dual cured resin cement (86.27±0.74). Conclusion: Amine-free dual cured resin cement can be an alternative to light cured one for cementation of thin veneers since it showed comparable color stability and high degree of conversion (AU)

Objetivo: O presente estudo tem como objetivo avaliar a estabilidade de cor e o grau de conversão do cimento resinoso dual sem amina em comparação com cimentos resinosos fotopolimerizáveis contendo amina usados com duas translucidezes diferentes em restaurações estéticas definitivas. Material e Métodos: Um total de 120 espécimes foram preparados para teste de estabilidade de cor (n=60). Os espécimes foram divididos em três grupos principais de acordo com o tipo de cimento resinoso. Grupo 1: polimerização dupla sem amina, Grupo 2: fotopolimerização, Grupo 3: polimerização dupla contendo amina. Cada grupo foi ainda subdividido de acordo com a translucidez da cerâmica em dois subgrupos: alta e baixa translucidez. A estabilidade da cor foi avaliada por um espectrofotômetro antes e após o envelhecimento térmico. Para a avaliação do grau de conversão (n=60), a espectroscopia de infravermelho com transformada de Fourier foi usada em três intervalos de tempo diferentes. A análise estatística foi realizada usando ANOVA multifatorial, seguida de ANOVA um faot com correção de Bonferroni. Resultados: O cimento resinoso contendo amina apresentou ΔEab e ΔE00 significativamente maiores em ambas as translucidezes (4,5±0,3, 3,5±0,3 respectivamente para cerâmica de alta translucidez e 3,8±0,4, 3,0±0,3 respectivamente para baixa translucidez) do que os outros cimentos testados (p< 0,001). O maior grau de conversão (DC) foi mostrado após 2 semanas pelo cimento resinoso dual sem amina (86,27±0,74). Conclusão: O cimento resinoso dual sem amina pode ser uma alternativa ao cimento polimerizável na restauração de facetas finas, uma vez que apresentou estabilidade de cor comparável e alto grau de conversão. (AU).

Effect of adhesive primer application on shear bond strength of self-adhesive cement to tooth structure and two different CAD/CAM milled blocks / Efeito da aplicação do primer adesivo na resistência ao cisalhamento do cimento autoadesivo à estrutura dentária e a dois diferentes blocos fresados CAD/CAM

Objective: This study was conducted to evaluate the influence of the G-CEM ONE adhesive enhancing primer on the shear bond strength of self-adhesive resin cement (G-CEM ONE) to both tooth structure and two different CAD/CAM blocks (GC Initial LiSi and Cerasmart 270). Material and Methods: Forty specimens (cylindrical-shaped, 5 mm in diameter and height) were milled from both CAD/CAM blocks (20 specimens from each block type). Forty sound upper premolars were sectioned to the level of peripheral dentin, then randomly divided into four groups (n = 10): A1: GC Initial LiSi without adhesive enhancing primer; B1: Cerasmart 270 without adhesive enhancing primer; A2: GC Initial LiSi with adhesive enhancing primer; B2: Cerasmart 270 group with adhesive enhancing primer application. The CAD/CAM blocks were cemented on teeth using a self-adhesive resin cement (G-cem one). The shear bond strength was assessed using a computerized universal testing machine. A digital microscope was used to study the mode of failure. The shear bond strength values data were analyzed statistically using paired t-test and independent t-test at the significance level of (0.05). Results: A significant difference was shown in the shear bond strength values among groups (P =0.000). The highest shear bond strength value was revealed in group A2, while group B1 exhibited the lowest shear bond strength value. Conclusion: Using the adhesive enhancing primer on the tooth's surface improved the resin cement's bond strength to CAD/CAM blocks. Additionally, GC Initial LiSi exhibited higher bond strength than Cerasmart 270, with or without the primer (AU)

Objetivo: Este estudo foi conduzido para avaliar a influência do primer adesivo G-CEM ONE na resistência ao cisalhamento do cimento resinoso autoadesivo (G-CEM ONE) tanto na estrutura dentária quanto em dois diferentes blocos CAD/CAM (GC Initial LiSi e Cerasmart 270). Material e Métodos: Quarenta corpos de prova (formato cilíndrico, 5 mm de diâmetro e altura) foram fresados em blocos CAD/CAM (20 corpos de prova de cada tipo de bloco). Quarenta pré-molares superiores sadios foram seccionados até o nível da dentina mais externa e, em seguida, divididos aleatoriamente em quatro grupos (n = 10): A1: GC Initial LiSi sem primer adesivo; B1: Cerasmart 270 sem primer adesivo; A2: GC Initial LiSi com primer adesivo; B2: Grupo Cerasmart 270 com aplicação de primer adesivo. Os blocos CAD/CAM foram cimentados nos dentes com cimento resinoso autoadesivo (G-CEM ONE). A resistência ao cisalhamento foi avaliada utilizando uma máquina de ensaios universal computadorizada. Um microscópio digital foi utilizado para estudar o modo de falha. Os dados dos valores de resistência ao cisalhamento foram analisados estatisticamente por meio do teste t pareado e teste t independente ao nível de significância de (0,05). Resultados: Foi demonstrada diferença significativa nos valores de resistência ao cisalhamento entre os grupos (P =0,000). O maior valor de resistência ao cisalhamento foi revelado no grupo A2, enquanto o grupo B1 exibiu o menor valor de resistência ao cisalhamento. Conclusão:A utilização do primer adesivo na superfície dentária melhorou a resistência de união do cimento resinoso aos blocos CAD/CAM. Além disso, o GC Initial LiSi apresentou maior resistência de união que o Cerasmart 270, com ou sem primer.(AU)

Avaliação da resistência adesiva de restaurações indiretas em resina composta com ou sem uso de material forrador após remoção seletiva da dentina / Evaluation of the adhesive strength of indirect composite resin restorations with or without the use of linear material after selective removal of dentin

O objetivo deste estudo foi analisar a resistência de união de restaurações indiretas cimentadas em superfícies dentinárias desmineralizadas com simulação da remoção seletiva da dentina com e sem uso de material forrador. Foram utilizados 60 dentes bovinos com a superfície vestibular desgastada até dentina sadia e divididos em quatro grupos: dentina sadia (controle), dentina desmineralizada (des), dentina desmineralizada e selada com resina flow (des-flow) e dentina desmineralizada e coberta com cimento de inonômero de vidro (des-civ). Todos os espécimes receberam condicionamento com ácido fosfórico (37% Condac, FGM) previamente a hibridização com adesivo universal (Single Bond Universal; 3M). O grupo des-civ recebeu uma cobertura de cimento de ionômero de vidro previamente ao condicionamento e hibridização e o grupo des-flow recebeu um selamento com resina flow (Resina Filtek Z350 XT Supreme Flowable, 3M) após condicionamento e hibridização. Em sequência, foram cimentadas peças simulando restaurações indiretas em resina composta (Grandioso ­ VOCO) na região condicionada de cada amostra. O conjunto recebeu fotoativação por 60 segundos em cada face da peça cimentada. Após 48 horas da cimentação, os espécimes dos três primeiros grupos foram submetidos aos testes mecânicos de tração, com velocidade de 1 mm/min. E após 29 dias, o quarto grupo foi submetido ao mesmo teste. A análise do tipo de fratura foi realizada por estereomicroscopia e os dados foram convertidos em MPa. Os resultados apresentaram diferença estatística de acordo com o teste ANOVA a 1 fator (p=0,011). Para as comparações múltiplas, o teste de Tukey apontou que o grupo des-flow apresentou valores menores do que o grupo controle. Todas as outras comparações foram similares. Concluiu-se que o grupo des-flow, quando comparado ao grupo controle, apresentou uma adesão inferior e que os materiais forradores não diferiram entre si (AU)

The aim of this study was to analyze the bond strength of cemented indirect restorations on demineralized dentin surfaces by simulating selective dentin removal with and without the use of a liner material. Sixty bovine teeth were used with the buccal surface worn down to healthy dentin and divided into four groups: healthy dentin (control), demineralized dentin (des), demineralized dentin sealed with flow resin (desflow) and demineralized dentin covered with glass ionomer cement (des-civ). All specimens were etched with phosphoric acid (37% Condac, FGM) prior to hybridization with universal adhesive (Single Bond Universal; 3M). The des-civ group received a glass ionomer cement cover prior to etching and hybridization, and the desflow group received a flowable resin seal (Filtek Z350 XT Supreme Flowable Resin, 3M) after etching and hybridization. Subsequently, specimens simulating indirect composite resin restorations (Grandioso - VOCO) were cemented in the etched region of each sample. The set was photoactivated for 60 seconds on each side. 48 hours after cementation, the specimens from the first three groups were subjected to mechanical tensile testing at a speed of 1 mm/min. After 29 days, the fourth group was subjected to the same test. The analysis of the fracture type was performed by stereomicroscopy and the data were converted into MPa. The results showed statistical difference according to the one-way ANOVA (p=0.011). For multiple comparisons, the Tukey's test showed that the des-flow group presented lower values than the control group. All other comparisons were similar. It was concluded that the des-flow group, when compared to the control group, presented lower adhesion and that the liner materials did not differ among themselves.(AU)

Efeito do tipo de sistema de cimentação na força de união de materiais utilizados para coroas livres de metal empregados a pilares intermediários / Effect of the type of cementation system on the bond strength of materials used for metal free crowns to employed for intermediate abutments

O objetivo deste estudo foi avaliar a influência do sistema de cimentação, do tipo de material empregado para confecção do pilar intermediário e do tipo de material empregado para a confecção da coroa na força de união de próteses cimentadas sobre implantes. Para simular o desempenho do pilar noventa espécimes de zircônia (IPS E.MAX ZirCAD, Ivoclar Vivadent) e noventa espécimes de titânio (O'ring Capsule, Peclab) foram obtidos. A rugosidade superficial foi padronizada utilizando-se uma politriz circular com lixa de granulação 600 durante 1 minuto. Os espécimes que simularam as coroas foram confeccionados a partir de blocos de resina (Grandio Blocs, Voco), dissilicato de lítio (IPS E.MAX eCAD, Ivoclar Vivadent) e de zircônia translúcidos (Zirkom, OdontoMega) com 3mm de diâmetro e 4 mm de altura. Cada tipo de material de pilar recebeu a cimentação de todos os três tipos de materiais que simulam as coroas. Para cada combinação foram testados três diferentes cimentos, sendo eles Bifix Hybrid Abutment (Voco), Multilink Abutment (Ivoclar Vivadent) e Vita Adiva (VITA). Os espécimes foram submetidos a um ensaio de cisalhamento a uma velocidade de 1 mm/min. Os dados foram analisados usando ANOVA a três fatores (pilar x coroa x cimento) seguido pelo teste de Tukey (α = 5%). Os resultados mostraram que houve diferenças significativas para o tipo de pilar e de coroa (p<0.05) e para o tipo de cimento (p<0.05). Pode-se observar que o cimento Bifix propiciou uma resistência adesiva significativamente menor que o Vita, enquanto o Multilink resultou em valores intermediários. Observou-se também que a resistência de união ao titânio foi menor do que à zircônia para infraestrutura. A resistência de união entre a zircônia e a zircônia de infraestrutura obtiveram valores significativamente maiores. Podemos concluir que o tipo de sistema de cimentação, o tipo de pilar e o tipo de coroa influenciaram significativamente na força de união entre os espécimes de simularam as coroas e os espécimes que simularam o pilar intermediário. O cimento Bifix Abutment proporcionou os menores valores enquanto o Vita Adiva os maiores. A resistência de união ao pilar de titânio foi menor do que à zircônia para infraestrutura, enquanto a adesão à coroa de resina composta foi menor do que ao dissilicato de lítio, que por sua vez foi menor do que à zircônia translúcida.(AU)

The aim of this study was to evaluate the influence of the cementation system, the type of material used to make the intermediate abutment and the type of material used to make the crown on the bond strength of implant-cemented prostheses. To simulate the performance of the abutment, ninety zirconia specimens (IPS E.MAX ZirCAD, Ivoclar Vivadent) and ninety titanium specimens (O'ring Capsule, Peclab) were obtained. Surface roughness was standardized using a circular polisher with 600-grit sandpaper for 1 minute. The specimens that simulated the crowns were made from resin blocks (Grandio Blocs, Voco), lithium disilicate (IPS E.MAX eCAD, Ivoclar Vivadent) and translucent zirconia blocks (Zirkom, OdontoMega) with 3 mm in diameter and 4 mm height. Each type of abutment material was cemented from all three types of crown-simulating materials. For each combination, three different cements were tested, Bifix Hybrid Abutment (Voco), Multilink Abutment (Ivoclar Vivadent) and Vita Adiva (VITA). Specimens were secured to a shear test at a speed of 1 mm/min. Data were analyzed using three-way ANOVA (abutment x crown x cement) followed by Tukey's test (α = 5%). The results showed significant differences for the type of abutment and crown (p<0.05), and for the type of cement (p<0.05). It can be observed that Bifix cement provided significantly lower bond strength than Vita, while Multilink evolved in intermediate values. It was observed the tensile bond strength was lower than backbone zirconia. The bond strength between zirconia crown and zirconia infrastructure obtained significantly higher values. We can conclude that the type of cementation system, the type of abutment and the type of crown significantly influenced the bond strength between the crowns and the intermediate abutment. Bifix Abutment cement introduced the lowest values while Vita Adiva presented the highest values. The strength adhesion to the titanium abutment was lower than to the infrastructure zirconia, while the adhesion to the composite resin crown was lower than to the lithium disilicate, which in turn was lower than to the translucent zirconia (AU)

The Effect of Immediate Dentin Sealing on the Marginal Adaptation of LithiumDisilicate Overlay Restorations using different types of luting agents / Efeito do selamento imediato da dentina na adaptação marginal de restaurações overlay de dissilicato de lítio utilizando diferentes tipos de agentes de cimentação: estudo in vitro

Objective:This study evaluated the effect of immediate dentin sealing on the marginal adaptation of lithium disilicate overlays with three different types of resin-luting agents: preheated composite, dual-cure adhesive resin, and flowable composite. Materials and Methods: Forty-eight maxillary first premolars of similar size were prepared with a butt joint preparation design. The teeth were separated into two primary groups, each with twenty-four teeth: Group DDS: Delay dentin sealing (non-IDS) teeth were not treated. Group IDS: dentin sealing was applied immediately after teeth preparation. Each group was subsequently separated into three separate subgroups. Subgroups (DDS+Phc, IDS+Phc): cemented with preheated composite (Enamel plus HRi, Micerium, Italy), Subgroups (DDS+Dcrs, IDS+Dcrs): cemented with dual-cured resin cement (RelyX Ultimate, 3M ESPE, Germany) and Subgroups (DDS+Fc, IDS+Fc): Cemented with flowable composite (Filtek supreme flowable, 3M ESPE, USA). Using a digital microscope with a magnification of 230x, the marginal gap was measured before and after cementation at four different locations from each surface of the tooth, and the mean of measurements was calculated and analyzed statistically using the independent t-test, one-way ANOVA test, Bonferroni correction at a significance level of 0.05. Results: The samples that were immediately sealed with dentin bonding agent showed lower marginal gaps than delayed dentin sealing, both pre-and post-cementation for all subgroups, with a statistically significant difference (p˂0.01). The marginal gap was significantly lower in the IDS+Fc (48.888 ±5.5 µm) followed by the IDS+Dcrs group (53.612 ±5.8 µm) and IDS+Phc (79.19 9±6.9 µm) respectively, while the largest marginal gaps were observed in the DDS+Phc group (86.505 ±5.4 µm). Conclusion: Generally, the teeth with IDS showed better marginal adaptation than teeth without IDS. The marginal gap was smaller with flowable composite and dual-cure resin cement than with preheated composite (AU)

Objetivo:Esse estudo avaliou o efeito do selamento imediato da dentina na adaptação marginal de overlays em dissilicato de lítio com três tipos diferentes de agentes de cimentação resinosos: resina composta pré-aquecida, adesivo resinoso dual e resina fluida. Materiais e métodos: Quarenta e oito primeiros pré-molares maxilares com tamanho similar foram preparados com término em ombro. O dente foi separado em dois grupos primários, cada um com vinte e quatro dentes: Grupo DDS: retardado selamento da dentina (non-IDS) dente não foi tratado. Grupo IDS: selamento dentinário foi aplicado imediatamente após a preparação do dente. Cada grupo foi separado de modo subsequente em três subgrupos. Subgrupo (DDS+Phc, IDS+Phc): cimentado com resina pré-aquecida (Enamel plus HRi, Micerium, Italy), Subgrupo (DDS+Dcrs, IDS+Dcrs): cimentado com cimento resinoso dual (RelyX Ultimate, 3M ESPE, Germany) e Subgrupo (DDS+Fc, IDS+Fc): cimentado com resina fluida (Filtek supreme flowable, 3M ESPE, USA). Usando um microscópio digital com magnificação de 230x, o gap marginal foi medido antes e após a cimentação em quatro diferentes localizações de cada superfície do dente e a média das medidas foi calculada e estatisticamente analisada através do uso do teste ANOVA um-fator e teste independente de Tukey e correção Bonferroni com nível de significância de 0,05. Resultado: As amostras que foram imediatamente seladas com agente adesivo dentinário apresentaram menores gaps marginais do que o selamento dentinário retardado, ambos pré e pós cimentação para todos os subgrupos apresentaram diferença estatística significante (p˂0.01). O gap marginal foi significativamente menor para IDS+Fc (48.888 ±5.5 µm) acompanhado do IDS+Dcrs group (53.612 ±5.8 µm) e IDS+Phc (79.19 9 ±6.9 µm) respectividamente, enquanto o maior gap marginal foi observado no grupo DDS+Phc (86.505 ±5.4 µm). Conclusão:Geralmente, o dente com IDS apresentou melhor adaptação marginal do que o dente sem IDS. O gap marginal foi menor com resina fluida e cimento resinoso dual do que com a resina composta pré-aquecida (AU)

Análise comparativa das características composicionais, técnicas e comerciais dos cimentos endodônticos obturadores à base de silicato de cálcio / Comparative analysis of compositional, technical and commercial characteristics of calcium silicate-based endodontic root canal sealers

Introdução: os cimentos endodônticos obturadores à base de silicato de cálcio têm sido amplamente utilizados na endodontia, principalmente em razão de suas reconhecidas propriedades bioativas. Como consequência, uma quantidade expressiva de marcas comerciais foi lançada no mercado, dificultando a compreensão do profissional, principalmente no que diz respeito às diferentes composições químicas, apresentações, formas de uso e custo-benefício. Objetivos: o Objetivo deste trabalho foi analisar as diferenças composicionais, técnicas (indicações e apresentação comercial) e comerciais (custo e disponibilidade de venda) dos cimentos endodônticos obturadores à base de silicato de cálcio, disponíveis para uso e comercialização no Brasil. Metodologia: foi realizada uma busca sistemática no site da Anvisa, sendo identificados sete cimentos endodônticos obturadores biocerâmicos para uso no Brasil. As bulas dos produtos foram analisadas para verificação de composição, apresentação e indicação de uso. Sites especializados foram consultados para verificação de preço dos produtos. Resultados: observou-se que a composição química varia bastante, a depender do fabricante, sendo os silicatos tricálcico e dicálcico os componentes mais frequentes. A maioria dos cimentos é apresentada comercialmente pronta para uso, e possui óxido de zircônio como agente radiopacificador. A venda através de sites especializados ainda é restrita a alguns produtos, e o custo varia de acordo com a quantidade de material por embalagem. Conclusão: este trabalho apresentou as características composicionais, técnicas e comerciais de sete cimentos endodônticos obturadores à base de silicato de cálcio registrados na ANVISA e autorizados para uso no Brasil.

Introduction: calcium silicate-based endodontic sealers have been widely used in endodontics, mainly because of their recognized bioactive properties. As a result, a significant number of commercial brands were launched on the market, making it difficult for professionals their comprehension, especially with regard to different chemical compositions, presentations, forms of use and cost-effectiveness. Objective: the Objective of this work was to analyze the compositional, technical (indications and commercial presentation) and commercial (cost and availability) differences of calcium silicate-based endodontic sealers, available for use and commercialization in Brazil. Methodology: a systematic search was carried out on the Anvisa website, and seven bioceramic endodontic sealers for use in Brazil were identified. Product leaflets were analyzed to verify composition, presentation and indication of use. Specialized websites were consulted to verify the price of the products. Results: it was observed that the chemical composition varies a lot, depending on the manufacturer, with tricalcium and dicalcium silicates being the most frequent components. Most sealers are commercially available ready-to-use, and have zirconium oxide as a radiopacifying agent. The sale through specialized websites is still restricted to some products, and the cost varies according to the amount of material per package. Conclusion: this work presented the compositional, technical and commercial characteristics of seven calcium silicate-based endodontic sealers registered at ANVISA and authorized for use in Brazil.

Avaliação das propriedades físico-químicas e osteogênicas do cimento portland associado ao pentóxido de nióbio / Evaluation of the physicochemical and osteogenic properties of portland cement associated with niobium pentoxide

Este trabalho objetivou desenvolver, caracterizar e avaliar a atividade osteogênica de formulações de CP com diferentes proporções de óxido de Nióbio (Nb2O5), substituindo o Bi2O3. Foram utilizados três grupos, um controle e dois experimentais: GC (MTA Angelus®), F6 (75% CP, 20% Nb2O5 e 5% CaSO4) e F7 (75% CP, 10% Bi2O3, 10% Nb2O5e 5% CaSO4). As formulações foram submetidas às análises de Difração de RaioX (DRX), Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Espectrometria de Fluorescência de Raios-X (FRX), pH, tempo de presa, radiopacidade, resistência a compressão, citotoxicidade e bioatividade. Os dados obtidos foram avaliados estatisticamente pelo teste de variância (ANOVA) com correção de Bonferroni (p<0,05%). O resultado do teste de pH: Nióbio 10% Imediato (12,205 ±0,304); 24h; (12,770 ± 0,226) 48h: (12,910 ± 0,169). Nióbio 20%: imediato (12,080 ± 0,282); 24 h: (12,350 ± 0,593); 48 h: (12,580 ± 0,73). Para o tempo de presa inicial em segundos: MTA (397,500 ±10,606); Nióbio 10% (294,333 + 90,897) e Nióbio 20% (279,000 + 15,874). O tempo de presa final para os grupos foram: MTA (15,000 + 49,497), Nióbio 10% (560 ±38,587), sendo menor quando comparado ao MTA (p<0,001) e Nióbio 20% (715,666 ± 30,664) (p<0,01). Os valores da radiopacidade em mm Al do Nióbio 10% (3,888 ±0,340); Nióbio 20% (3,713 ± 0,712). A resistência a compressão em MPa foi: Nióbio 10% (694,150 + 78,951) Nióbio 20% (699,295 + 47,672). A viabilidade celular não apresentou diferença entre o MTA e grupos experimentais (p<0,05). Os resultados da capacidade osteogênese das formulações a partir do ensaio da fosfatase alcalina (FAL) em UI/L por grama de proteína para cada grupo foi: MTA (1,9 + 1,227) e Nióbio 20% (1,784 + 1,342) (p>0,05). Nossos achados apontam propriedades relevantes para as formulações com Nb2O5 como, pH alcalino, radiopacidade, resistência a compressão e atividade da fosfatase alcalina (AU).

Work aimed to develop, characterize and evaluate the osteogenic activity of PC formulations with different proportions of Niobium oxide (Nb2O5), replacing Bi2O3. Three groups were used, one control and two experimental: GC (MTA Angelus®), F6 (75% CP, 20% Nb2O5 and 5% CaSO4) and F7 (75% CP, 10% Bi2O3, 10% Nb2O5e 5% CaSO4) . The formulations were submitted to X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR), X-ray Fluorescence Spectrometry (FRX), pH, setting, radiopacity, compressive strength, cytotoxicity and bioactivity. The data obtained were statistically evaluated by the test of variance (ANOVA) with Bonferroni correction (p<0.05%). The pH test result: Niobium 10% Immediate (12.205 ±0.304); 24h; (12.770 ± 0.226) 48h: (12.910 ± 0.169). Niobium 20%: immediate (12.080 ± 0.282); 24h: (12.350 ± 0.593); 48 h: (12.580 ± 0.73). For initial setting time in seconds: MTA (397,500 ±10,606); Niobium 10% (294,333 + 90,897) and Niobium 20% (279,000 + 15,874). The final setting time for the groups were: MTA (15,000 + 49,497), Niobium 10% (560 ± 38,587), being smaller when compared to MTA (p<0,001) and Niobium 20% (715,666 ± 30,664) (p<0 .01). Radiopacity values in mm Al of 10% Niobium (3.888 ±0.340); Niobium 20% (3.713 ± 0.712). The compressive strength in MPa was: Niobium 10% (694.150 + 78.951) Niobium 20% (699.295 + 47.672). Cell viability showed no difference between MTA and experimental groups (p<0.05). The results of the osteogenesis capacity of the formulations from the alkaline phosphatase assay (ALF) in IU/L per gram of protein for each group were: MTA (1.9 + 1.227) and Niobium 20% (1.784 + 1.342) (p> 0.05). Our findings point to relevant properties for Nb2O5 formulations such as alkaline pH, radiopacity, compressive strength and alkaline phosphatase activity (AU).

Efeito do cimento cirúrgico sobre o pós-operatório de gengivectomias e gengivoplastias: uma revisão crítica da literatura / Effect of surgical cement on the post-operative following gingivectomy and gingivoplasty: a critical review of the literature

Contexto:O cimento cirúrgico é um material alternativo no pós operatório de gengivoplastia e gengivectomia, que proporciona conforto ao paciente. Porém, existem controvérsias sobre sua utilização, sendo relatado por alguns especialistas o surgimento do processo inflamatório agudo, sendo classificado como desnecessário.Objetivo: Identificar evidências na literatura acerca do efeito do cimento cirúrgico no pós-operatório do tecido gengival após gengivectomia e gengivoplastia. Materiais e métodos: Foi realizada uma revisão crítica de literatura por meio de buscas nas bases de dadosPubmed, Scielo, Lilacs, Cochrane, Scopus e na literatura cinzenta (Periódicos Capes, Google Scholar). Foram incluídos ensaios clínicos randomizados que testaram o cimento cirúrgico em casos de gengivectomias. Os artigos foram selecionados inicialmente pelo título e resumo, seguido de análise do texto na íntegra. Os estudos incluídos tiveram o nível de evidência avaliado por parâmetros do CONSORT. Resultados:Foram levantados 1458 estudos, sendo 16 escolhidos para leitura na íntegra e, destes, 3 foram incluídos na revisão. A amostra teve idade variando de dezessete a setenta e um anos. Foi utilizado cimento cirúrgico sem eugenol comparado com o bochecho de clorexidina 0,2% e a escovação mecânica precoce no pós-cirúrgico. Um estudo relatou menor índice de dor com o uso de cimento cirúrgico. O tempo de acompanhamento dos estudos foi de 30 dias. Dois estudos tiveram nível de evidência III.Conclusão: Os artigos apresentaram baixa evidência científica e quenão há consenso na literatura quanto ao efeito de cimento cirúrgico após gengivectomias.

Aim:To identify evidence in the literature about the effect of periodontal dressing on the healing of gingival tissue after gingivectomy and gingivoplasty. Materials and methods: A critical literature review was carried out through electronic searches in thePubmed, Scielo, Lilacs, Cochrane, Scopus databases and in the gray literature (Periódicos Capes, Google Scholar). Randomized clinical trials evaluating periodontal dressing in gingivectomies were included. The articles were selected by title and abstract,followed by analysis of the full text. The included studies have the level of evidence determined by CONSORT parameters. Results: A total of 1458 studies were surveyed, 16 were selected for full reading and, of these, 3 were included in the review. The age sample ranged from seventeen to seventy-one years old. A periodontal dressing without eugenol was used compared to a 0.2% chlorhexidine mouthwash and an early mechanical brushing after surgery. One study reported less pain with the use of periodontal dressing. The follow-up of the studies was 30 days. Two studies had Level of Evidence III.Conclusion:It was concluded that the articles had low scientific evidence and that there is no consensus in the literature regarding the effect of periodontal dressing after gingivectomies.

Effect of laser-assisted retrograde cavity preparation on push-out-bond-strength of mineral trioxide aggregate and calcium-enriched-mixture-cement / Efeito de preparo cavitário retrógrado assistido por laser na força de união de cimento de agregado trióxido mineral e cimento enriquecido com cálcio

Objective: This study aimed to determine the push-out-bond-strength(PBS) of mineral trioxide aggregate (BIOMTA+) and calcium-enriched-mixture-cement (CEM) in retrograde cavities prepared using Er: YAG laser and stainless-steel bur. Material and Methods: The root canals of 60 extracted single-rooted human teeth were prepared, filled and their apical portion of 3-mm were resected using a diamond bur and randomly divided into four groups according to technique of retrograde preparation and filling material as follows(n=15): Group1: bur/ BIOMTA+ ,Group2: bur/ CEM, Group3: Er:YAG laser/ BIOMTA+, Group4: Er:YAG laser/ CEM. PBS test were performed to specimens and failure modes were evaluated. The data were statistically analyzed with ANOVA, Post-Hoc Tukey and t tests (p< 0.05). Results: CEM was exhibited higher than bond strength compared to BIOMTA+ in retrograde cavity prepared using laser (p= 0.021) and BIOMTA+ in retrograde cavity prepared using bur was exhibited higher than bond strength compared to in retrograde cavities prepared using laser (p= 0.024). Failure modes were dominantly cohesive in all groups tested and one representative specimen each failure mode was examined in SEM and the general characteristics of the failure modes were confirmed. Conclusion: With in the limitations of the present study, when used CEM, Er: YAG laser-assisted retrograde cavity preparation positively affected the bond strength values compared to BIO MTA+. Considering its optimal adhesion, the calcium-enriched-mixture-cement (CEM) might be a good option as a filling material in retrograde cavities in clinical use. (AU)

Objetivo: O objetivo deste estudo foi determinar a força de união (PBS) de cimento de agregado trióxido mineral (BIO MTA+) e cimento enriquecido com cálcio (CEM) em preparos cavitários retrógrados realizados com: Laser Er-YAG e brocas de aço inoxidável. Material e Métodos: Canais radiculares de 60 dentes unirradiculares extraídos foram preparados, preenchidos e 3 mm de suas porções apicais foram ressecadas usando uma broca diamantada e divididos randomicamente em quatro grupos de acordo com a técnica de preparação retrógrada e o material de preenchimento (n=15): Grupo 1: Broca/BIO MTA+, Grupo 2: Broca/CEM, Grupo 3: Laser Er-YAG/BIO MTA+, Grupo 4: Laser Er-YAG/CEM. O teste de PBS foi realizado para as amostras e os modelos de falha foram avaliados. Os dados foram analisados estatisticamente pelos testes de ANOVA, Post-Hoc Tukey e testes t (p< 0.05). Resultados: CEM apresentou maior força de união que BIO MTA+ em cavidades retrógradas preparadas com laser (p= 0.021) e BIO MTA+ em cavidades retrógradas preparadas com brocas apresentou maior força de união quando comparado à cavidades retrógradas preparadas com laser (p= 0.024). Os modelos de falha foram predominantemente coesos em todos os grupos testados e um espécime representativo de cada modelo de falha foi examinado em MEV e as características gerais dos modelos de falha foram confirmadas. Conclusão: Com as limitações do presente estudo, quando usou-se CEM, o preparo de cavidades retrógradas através de Laser Er-YAG afetou positivamente os valores da força de união quando comparados com BIO MTA+. Considerando sua ótima adesão, o cimento enriquecido com cálcio (CEM) pode ser uma boa opção como um material de preenchimento em cavidades retrógradas no uso clínico.

Resistencia adesiva a longo prazo entre zirconias odontologicas com diferentes niveis de translucidez e cimento resinoso / Long-term bond strength between dental zirconia of different translucency levels and resin cement

Este estudo avaliou a resistência e a confiabilidade adesiva entre zircônias com diferentes graus de translucidez com o cimento resinoso, sinterizadas de forma convencional e rápida, além de avaliar a susceptibilidade ao envelhecimento térmico dessas interfaces. Espécimes de quatro diferentes zircônias (3YTZP/Translúcida [T], 3Y-TZP/Alta Translucidez [HT], 4Y-PSZ/Super Translúcida [ST] e 5Y-PSZ/Extra Translúcida [XT]) foram obtidos a partir de blocos de CAD/CAM e polidos. Todas as zircônias foram sinterizadas de forma convencional (ciclo de ~12h), entretanto as zircônias T e HT foram subdivididas em grupos também sinterizados na forma rápida (~2h), seguindo o protocolo do fabricante. As superfícies adesivas foram jateadas com Al2O3 50 µm e silanizadas com primer contendo MDP, um cilindro de cimento resinoso foi construído na superfície cerâmica (Ø = 1 mm; h = 2 mm). Metade dos espécimes foram submetidos a termociclagem previamente ao ensaio (6000 ciclos; 5 ­ 55ºC); a outra metade das amostras foi submetida diretamente ao ensaio de microcisalhamento com fio em uma máquina de ensaios universal. Os dados de resistência adesiva foram submetidos a ANOVA 2-fatores e teste de Tukey (95%), bem como à análise de Weibull para determinação da confiabilidade adesiva. A média do valor da resistência adesiva foi estatisticamente diferente entre os materiais, apenas as zircônias HT e ST não foram afetadas negativamente pelo envelhecimento térmico. A forma de sinterização rápida foi estatisticamente semelhante à convencional para a zircônia T, entretanto a HT com sinterização rápida mostrou maior resistência adesiva imediata do que a convencional. O módulo de Weibull foi superior paras zircônias HT convencional e ST. O envelhecimento térmico causa uma degradação das interfaces adesivas das zircônias 3Y-TZP (T) e 5Y-PSZ (XT) com o cimento resinoso, entretanto não afeta as interfaces das zircônias 3Y-TZP (HT) e 4YPSZ (ST). O método de sinterização rápido não altera a resistência de união das zircônias estudadas com o cimento resinoso a longo prazo. A confiabilidade adesiva segundo o módulo de Weibull é superior para a 3Y-TZP (HT convencional) e 4Y-PSZ (ST). (AU)

This study evaluated the adhesive strength and reliability of zirconia with different degrees of translucency with resin cement, sintered in a conventional and speed mode, in addition to evaluating the susceptibility to thermal aging of these interfaces. Specimens of four different zirconia (3Y-TZP/Translucent [T], 3Y-TZP/High Translucent [HT], 4Y-PSZ/Super Translucent [ST] and 5YPSZ/Extra Translucent [XT]) were obtained from CAD/CAM blocks and polished. All zirconia were conventionally sintered (~12h cycle), however the T and HT zirconia were subdivided into groups also sintered in the speed mode (~2h), following the manufacturer's protocol. The adhesive surfaces were sandblasted with 50 µm Al2O3 and silanized with a primer containing MDP, a resin cement cylinder was built on the ceramic surface (Ø = 1 mm; h = 2 mm). Half of the specimens were submitted to thermocycling prior to the assay (6000 cycles; 5 ­ 55ºC); the other half of the samples were directly subjected to the wire microshear test in a universal testing machine. The bond strength data were submitted to 2-way ANOVA and Tukey's test (95%), as well as Weibull analysis to determine the adhesive reliability. The average value of bond strength was statistically different between materials, only HT and ST zirconia were not negatively affected by thermal aging. The speed sintering form was statistically similar to the conventional one for T zirconia, however the speed sintered HT showed higher immediate bond strength than the conventional one. The Weibull modulus was superior for conventional HT and ST zirconia. Thermal aging causes a degradation of the adhesive interfaces of 3Y-TZP (T) and 5Y-PSZ (XT) zirconia with the resin cement, however it does not affect the interfaces of 3Y-TZP (HT) and 4Y-PSZ (ST) zirconia. The speed sintering method does not change the bond strength of the zirconia studied with the resin cement in the long term. Adhesive reliability according to the Weibull module is superior for 3Y-TZP (conventional HT) and 4Y-PSZ (ST). (AU)

Effect of immediate dentin sealing and temporary cement removal on bond strength of resin cements to dentin / Efeito do selamento dentinário imediato e da remoção do cimento provisório na resistência de união de cimentos resinosos à dentina

Objective: To evaluate the influence of immediate dentin sealing (IDS) and mechanical methods for removing the temporary cement on the bond strength between dentin and resin cements. Material and Methods: Bovine incisors were ground until dentin exposure and divided according to two factors: "dentin surface treatment"' - cleaning with manual dental excavator (DE), with Robinson bristle brush and pumice paste (PP) or IDS application with Single Bond 2 (IDS/SB+PP) or Single Bond Universal (IDS/SBU+PP) plus cleaning with PP; and "resin cement" - Self-adhesive (RelyX U200) or conventional cement with self-etching adhesive (Multilink Automix). Simulating provisional restoration, acrylic resin plates were cemented onto the dentin surface (with or without IDS) with a non-eugenol temporary cement, and stored in distilled water (37 ºC; 7 days). The acrylic plates were removed, the dentin surface was cleaned (PP or DE), and starch tubes were positioned on the dentin where the resin cements were applied. After 24 h, the specimens were submitted to a microshear test (wire-loop method). Results: Two-way analysis of variance showed statistically significant influence of dentine surface treatments (p< 0.001) and resin cement (p= 0.001) in the bond strength values. The IDS/SBU+PP/U200 (7.24 MPa) and IDS/SBU+PP/MULTI (6.40 MPa) groups presented higher values when compared to cleaning with DE (DE/U200= 4.60 MPa; DE/MULTI= 1.45 MPa) and PP (PP/U200= 3.74 MPa; PP/MULTI= 3.14 MPa). Statistical difference was also found between the cements when dental excavator treatment was used (RelyX U200 ˃ Multilink Automix). The IDS/SBU+PP protocol presented a higher percentage of cohesive failures. The micrographs showed differences in dentin surface characteristics among the groups. Conclusion: Immediate dentin sealing increased the bond strength of the resin cements to dentin compared to mechanical cleaning only, regardless the resin cement. (AU)

Objetivo: Avaliar a influência do selamento dentinário imediato (IDS) e dos métodos mecânicos de remoção do cimento provisório na resistência de união entre dentina e cimentos resinosos. Materiais e Métodos: Incisivos bovinos foram desgastados até a exposição da dentina e divididos de acordo com dois fatores: "tratamento da superfície dentinária" - limpeza com cureta dentária manual (DE), com escova de cerdas Robinson e pasta de pedra-pomes (PP) ou aplicação de IDS com Single Bond 2 (IDS/SB +PP) ou Single Bond Universal (IDS/SBU+PP) mais limpeza com PP; e "cimento resinoso" - autoadesivo (RelyX U200) ou cimento convencional com adesivo autocondicionante (Multilink Automix). Simulando a restauração provisória, placas de resina acrílica foram cimentadas na superfície dentinária (com ou sem IDS) com um cimento provisório sem eugenol e armazenadas em água destilada (37 ºC; 7 dias). As placas de acrílico foram removidas, a superfície dentinária foi limpa (PP ou DE) e tubos de amido foram posicionados na dentina onde os cimentos resinosos foram aplicados. Após 24 h, os corpos-de-prova foram submetidos ao ensaio de microcisalhamento (método wire-loop). Resultados: A análise de variância de dois fatores mostrou influência estatisticamente significativa dos tratamentos de superfície dentinária (p< 0,001) e cimento resinoso (p= 0,001) nos valores de resistência de união. Os grupos IDS/SBU+PP/U200 (7,24 MPa) e IDS/SBU+PP/MULTI (6,40 MPa) apresentaram valores maiores quando comparados à limpeza com DE (DE/U200= 4,60 MPa; DE/MULTI= 1,45 MPa) e PP (PP/U200= 3,74 MPa; PP/MULTI= 3,14 MPa). Uma diferença estatística também foi encontrada entre os cimentos quando o tratamento com cureta dentária foi usado (RelyX U200 ˃ Multilink Automix). O protocolo IDS/SBU+PP apresentou maior percentual de falhas coesivas. As micrografias mostraram diferenças nas características da superfície dentinária entre os grupos. Conclusão: O selamento dentinário imediato aumentou a resistência de união dos cimentos resinosos à dentina em comparação com a limpeza mecânica apenas, independentemente do cimento resinoso.(AU)

Clinical assessment of two inlay -retained bridge designs (proximal box-shaped and inlay shaped) in missing posterior teeth cases. (Randomized Clinical Trial) / Avaliação clínica de dois modelos de ponte fixa inlay (forma de caixa proximal e em forma de inlay) em casos de dentes posteriores ausentes. (Ensaio clínico randomizado)

Objective: This study aimed to evaluate the clinical performance of two inlay-retained bridge designs (proximal shaped and inlay shaped) in single missing posterior teeth cases. Material and Methods: A total of 70 cases with missing single posterior teeth were included in this study and divided into two groups with a 1:1 allocation ratio (n = 35 for each group). Group 1 (the control group): this group received an inlay retained bridge with inlay design on both abutments. Group 2 (the intervention group): this group received an inlay retained bridge with a proximal box on both abutments. PMMA resin (YAMAHACHI PMMA) was used for the try-in stage and monolithic zirconia (Katana, Kuraray) was used for the final restorations. The restoration surfaces were treated using sandblasting and Z-prime S (Bisco) and the cementation was done by using self-adhesive resin cement (Bisco). Fracture, marginal adaptation, postoperative sensitivity, caries, and gingivitis were assessed using the modified United States Public Health Service for restoration clinical assessments (MUSPHS standards) over 12 months of follow-up. Results: The results show there was no significant difference between the two groups. Kaplan-Meier survival curve was constructed to calculate the mean survival estimates of the two groups and we found that the two groups were clinically successful during a one-year follow-up. Conclusion: Both designs of inlay retained fixed dental prostheses revealed successful clinical performance in terms of Fracture, marginal adaptation, postoperative sensitivity, caries, and gingivitis (AU)

Objetivo: O objetivo deste estudo foi avaliar o desempenho clínico de dois modelos de ponte fixa por inlay (formato proximal e formato inlay) em casos de dentes posteriores perdidos. Material e Métodos: Um total de 70 casos com perda de um único dente posterior foi incluído neste estudo e dividido em dois grupos com uma razão de alocação de 1: 1 (n = 35 para cada grupo). Grupo 1 (grupo controle): Este grupo recebeu uma ponte fixa por inlay com deseho de inlay em ambos os pilares. Grupo 2 (grupo intervenção): Este grupo recebeu uma ponte fixa inlay com uma caixa proximal em ambos os pilares. Resina de PMMA (YAMAHACHI PMMA) foi usada para a etapa de try-in e a zircônia monolítica (Katana, Kuraray) foi utilizada para as restaurações finais. As superfícies das restaurações foram jateadas com Z-prime S (Bisco) e a cimentação realizada com cimento resinoso autoadesivo (Bisco). Fratura, adaptação marginal, sensibilidade pós-operatória, cárie e gengivite foram avaliadas usando o Serviço de Saúde Pública dos Estados Unidos modificado para avaliações clínicas de restauração (padrões MUSPHS) ao longo de 12 meses de acompanhamento. Resultados: Os resultados mostraram que não houve diferença significativa entre os dois grupos. A curva de sobrevida de Kaplan-Meier foi construída para calcular as estimativas de sobrevida média dos dois grupos e foi concluído que os dois grupos foram clinicamente bem-sucedidos durante um acompanhamento de um ano. Conclusão: Ambos os modelos de próteses dentárias fixas de inlay revelaram desempenho clínico bem-sucedido em termos de fratura, adaptação marginal, sensibilidade pós-operatória, cárie e gengivite(AU)

Análise da interface adesiva entre pinos de fibra de vidro e dentina intrarradicular submetida à técnica alcoólica simplificada / Analysis of the adhesive interface glass fiber posts and intrarradicular dentil submitted to the simplified alcoholic technique

A cimentação de pinos de fibra de vidro à dentina intrarradicular, principalmente no terço apical, continua sendo um desafio na odontologia. O objetivo desse estudo foi avaliar a influência do controle de umidade com etanol na resistência de união de pinos de fibra de vidro em diferentes terços de dentina intrarradicular, 24 horas e 6 meses após o processo de cimentação adesiva. Sessenta e quatro incisivos bovinos extraídos foram submetidos ao tratamento endodôntico e divididos em dois grupos, de acordo com o tipo de controle de umidade (técnica convencional e alcoólica). Cada grupo foi dividido em 4 subgrupos (n=8) de acordo com a cimentação: RXU: Single bond Universal + RelyX Ultimate; PNV: primer de dentes Panavia V5 + Panavia V5; U200: RelyX U200; SET: Set PP. A resistência de união do pushout foi medida em diferentes áreas da interface entre o pino e a superfície radicular, 24 horas e 6 meses após o procedimento de união. Os dados foram submetidos ao teste de Bonferroni (α = 0,05). Os menores valores de resistência de união foram encontrados para o grupo SET, com diferença estatisticamente significante entre os demais grupos para os terços cervical e médio. Os maiores valores de resistência de união foram encontrados para o grupo PNV com diferença estatisticamente significante para os demais grupos nos terços médio e apical em 24 horas. Avaliando os diferentes terços, em geral, os maiores valores de resistência de união foram encontrados para o terço cervical. O grupo PNV apresentou maiores valores de resistência de união para os terços cervical e médio, sem diferença estatisticamente significante entre eles. Quanto ao tipo de controle de umidade, pode-se observar que não há diferença estatisticamente significativa para o grupo PNV às 24 horas, U200 e SET aos 6 meses. Na comparação entre os tempos (24 horas e 6 meses), em geral, os valores de resistência de união diminuíram após o armazenamento. Diferenças significativas com menores valores foram observadas após o tempo de seis meses nos valores de envelhecimento para a resistência de união. Por meio de um microscópio óptico e um aparelho de microscopia eletrônica de varredura o padrão de fratura na interface adesiva foi caracterizado.

Cementation of fiberglass posts to intraradical dentin, especially in the apical third, remains a challenge in dentistry. The study was to evaluate the influence of moisture control with ethanol on the bond strength of fiberglass posts in different thirds of intraradicular dentin, 24 hours and 6 months after the adhesive cementation process. Sixty-four extracted bovine incisors were endodontically protected and divided into two groups, according to the type of moisture control (conventional and alcoholic technique). Each group was divided into 4 subgroups (n=8) according to cementation: RXU: Single bond Universal + RelyX Ultimate; PNV: Panavia V5 tooth primer + Panavia V5; U200: RelyX U200; SET: Set PP. The pushout bond strength was measured in different areas of the interface between the post and the root surface, 24 hours and 6 months after the bonding procedure. The data were confirmed by the Bonferroni test (α = 0.05). The lowest bond strength values were found for the SET group, with a statistically significant difference between the other groups for the cervical and middle thirds. The highest bond strength values were found for the PNV group, with a statistically significant difference for the other groups in the middle and apical thirds at 24 hours. Evaluating the different thirds, in general, the highest bond strength values were found for the cervical third. The PNV group showed higher bond strength values for the cervical and middle thirds, with no statistically significant difference between them. As for the type of humidity control, it can be observed that there is no statistically significant difference for the PNV group at 24 hours, U200 and SET at 6 months. In the comparison between times (24 hours and 6 months), in general, the bond strength values decreased after storage. Minor elevation differences with values were observed after the six-month time in the ageing values for bond strength. Using an optical microscope and a scanning electron microscopy device, the fracture pattern at the adhesive interface was characterized.

Diametral tensile strength of conventional glass ionomer cements with modified powder ratio for uses in atraumatic restorative treatment / Resistência à tração diametral de cimentos de ionômero de vidro convencionais modificados na razão de pó para uso em tratamento restaurador atraumático

ABSTRACT Objective: To identify the diametral tensile strength of Brazilian brands of conventional glass ionomer cements (GIC) when modified powder ratio in their composition compared to each other, and with high viscosity glass ionomer cement for Atraumatic Restorative Treatment (ART). Methods: Experimental study with five groups (n=10 each) and specimens (2.5 mm in height and 5.0 mm in diameter), considering G1 (Maxxion R-MR), G2 (Vidrion R-VR) and G3 Vitro molar (VM-control) according to manufacturer recommending powder/liquid (1:1), G4 (MR) and G5 (VR) plus powder (2:1). The specimens were stored in an oven at 37 ± 1 ° C for 1 day. Diametral Tensile Test was performed by the Instron model 4444. Means differences were tested by Student´s T-Test (α = 5%). Results: There significant differences were in the means (standard deviation) of diametral tensile strength of MR (1:1) 4.24 (±1.47) and MR (2:1), 5.74 (±1.51) (p=0.039) and VR (1:1) 4.50 (±1.27) and VR (2:1) 6.20 (±1.89) (p=0.029). When comparing MR and VR (2:1) with MV (1:1) 4.82 (±1.17), VR 2: 1, 6.20 (±1.89) showed significant differences (p=0.0336). Conclusion: There was a significant increase in the means of diametral tensile strength of Brazilian brands conventional GICs when powder increment, approaching the performance observed by the high viscosity GIC.

RESUMO Objetivo: Identificar a resistência à tração diametral de marcas nacionais de cimentos de ionômero de vidro (CIV) convencionais quando acrescidos de pó em sua composição comparados entre si e com cimento de ionômero de vidro de alta viscosidade para Tratamento Restaurador Atraumático (TRA). Métodos: Pesquisa experimental com cinco grupos (n=10 cada) e confeccionados corpos de prova (2,5 mm de altura e 5,0 mm de diâmetro), considerando G1 (Maxxion R/FGM-MR), G2 (Vidrion R/SS White-VR) e G3 Vitro molar (DFL-VM-controle) manipulados segundo fabricante pó/líquido (1:1), G4 (MR) e G5 (VR) acrescidos de pó (2:1). Os espécimes foram armazenados em estufa a 37 ± 1° C por 1 dia. Teste de Tração Diametral foi realizado pelo equipamento Instron modelo 4444. As diferenças das médias foram testadas pelo Test T de Student (α=5%). Resultados: Foram encontradas diferenças significativas das médias (desvio-padrão) de resistência à tração diametral de MR (1:1) 4,24 (±1,47) e MR (2:1), 5,74(±1,51) (p=0,039) e VR (1:1) 4,50 (±1,27) e VR (2:1) 6,20(± 1,89) (p=0,029). Quando da comparação entre MR e VR (2:1) com VM (1:1) 4,82(±1,17), VR 2:1, 6,20 (±1,89) apresentou média superior e significante (p=0,0336). Conclusão: Observou-se aumento significativo nas médias de resistência mecânica à tração diametral dos CIVs convencionais nacionais a partir do incremento de pó, aproximando-se do desempenho observado pelo CIV de alta viscosidade.

Effect of delayed light-curing on solubility, color stability, and opacity of Fuji II LC glass ionomer cement: original article / Efeito da fotopolimerização tardia na solubilidade, estabilidade de cor e opacidade do cimento de ionômero de vidro Fuji II LC: artigo original

Objective: Resin-modified glass ionomer (RMGI) cements are among the commonly used restorative materials in low stress-bearing areas and also for temporary restorations. The competition between acid-base reactions and light polymerization reactions in delayed curing of RMGIs can affect their physical and mechanical properties, as well as their degree of conversion. Since solubility, color stability, and opacity are among the main physical properties affecting the durability and clinical service of RMGI restorations, this study aimed to assess the effect of delayed curing on solubility, color stability, and opacity of Fuji II LC RMGI. Material and Methods: This in vitro, experimental study evaluated 80 Fuji II LC RMGI specimens (10 specimens per each in 4 groups) in terms of solubility, color stability, and opacity at 6 months later. Specimens were cured immediately or were cured with 1, 5 and 10 min delay. Results: Maximum solubility and minimum change in opacity and color stability at 6 months were noted in the group with delayed curing by 10 min. A significant difference was noted in the solubility of specimens cured after 10 min and 1 min. Significant differences were also noted in the opacity and color stability of specimens cured after 10 min and all other groups (P < 0.05). Conclusion: Delayed curing by 1 min decreased the solubility of RMGI specimens compared with immediate curing or curing after 5 min. Although this difference did not reach statistical significance. Color stability and changes in opacity are mainly influenced by the acid-base reactions rather than polymerization reactions.(AU)

Objetivo: Cimentos de ionômero de vidro modificado por resina (CIVMR) estão entre os materiais restauradores mais comumente utilizados em áreas de baixa tensão e também para restaurações temporárias. A competição entre reações ácido-base e reações provenientes da fotopolimerização tardia dos CIVRMs podem afetar suas propriedades físicas e mecânicas, bem como seu grau de conversão. Uma vez que a solubilidade, estabilidade de cor e opacidade estão entre as principais propriedades físicas que afetam a durabilidade e o tempo de serviço clinico de restaurações de CIVMR, este estudo teve como objetivo avaliar o efeito da fotopolimerizaçao tardia na solubilidade, estabilidade de cor e opacidade do CIVMR Fuji II LC. Material e Métodos: Este estudo experimental in vitro avaliou 80 espécimes de CIVMR Fuji II LC (4 grupos com 10 espécimes cada) em termos de solubilidade, estabilidade de cor e opacidade apos 6 meses. As amostras foram fotopolimerizadas imediatamente ou com 1, 5 e 10 min de atraso. Resultados: Máxima solubilidade e mínima alteração na opacidade e estabilidade da cor em 6 meses foram observadas no grupo com fotopolimerização tardia em 10 min. Uma diferença significativa foi observada na solubilidade das amostras fotopolimerizadas após 10 min e 1 min. Diferenças significativas também foram observadas na opacidade e estabilidade de cor das amostras fotopolimerizadas após 10 min e em todos os outros grupos (P <0,05). Conclusão: A fotopolimerizaçao tardia em 1 min diminuiu a solubilidade das amostras CIVMR em comparação com a fotopolimerizaçao imediata ou após 5 min. Embora essa diferença não tenha alcançado significância estatística. A estabilidade da cor e as mudanças na opacidade são influenciadas principalmente por reações ácido-base, em vez de reações causadas pela polimerização(AU)

Restaurações diretas com materiais bioativos: observações clínicas, in vitro e revisão sistemática / Direct restorations with bioactive materials: clinical observations, in vitro and systematic review

O objetivo do ensaio clínico foi avaliar o desempenho clínico de 2 materiais bioativos (Cention N e EQUIA Forte) em comparação a resina composta. O estudo in vitro teve como objetivo avaliar o desenvolvimento de lesões de cárie induzida por desafio cariogênico bacteriano na margem de restaurações em esmalte e dentina com Cention N com e sem adesivo, EQUIA Forte e resina composta. A revisão sistemática teve como objetivo responder a seguinte pergunta: A avaliação clínica de restaurações em dentes permanentes com materiais bioativos evidencia maior sucesso do que restaurações com materiais não bioativos? Para o estudo clínico foram selecionados 120 participantes aleatoriamente divididos em 3 grupos (n=40), TC: Tetric N-Ceram, EF: EQUIA Forte, CN: Cention N. O preenchimento das cavidades foi realizado seguindo as indicações do fabricante. Foi utilizado o dispositivo de fluorescência DIAGNOdentTM Pen para avaliação da recorrência de cárie. No estudo in vitro foram confeccionados 100 espécimes a partir de dentes bovinos. Foram divididos em 5 grupos (n=20) metade em esmalte e metade em dentina: Cention N sem adesivo (CN), Cention N com adesivo (CA), EQUIA Forte (EF); Tetric N-Ceram (TC); e sem restauração (SR). Foram submetidos a envelhecimento térmico; leitura de microdureza Knoop (KHN) inicial, esterilizados e expostos a um desafio cariogênico com Streptococcus mutans por 28 dias. Lesões de cárie artificial foi quantificado por meio de KHN superficial e de subsuperfície, e análise com microscopia de luz polarizada. Os dados foram submetidos a ANOVA 1 fator e teste Tukey no esmalte e teste de Kruskal-Wallis na dentina. Em esmalte os grupos EF, CN, CA apresentaram menor porcentagem de perda da microdureza (%PMS) 57,85%, 63,88% e 66,65% respectivamente. Na dentina, EF, CN e CA apresentaram menores valores de %PMD sendo 31,7%, 34,1% e 40,8% respectivamente. Os valores mais altos de %PMS foram registrados para os grupos TC e SR tanto na dentina como no esmalte. Na revisão sistemática, com base na pergunta de pesquisa e estratégia PICO: P- Dentes permanentes, I- Restaurações (classe I, classe II, classe III, classe V) com materiais bioativos, C- Restauração com materiais não bioativos, O- Retenção; foi traçada a estratégia de busca. Após a obtenção dos estudos eles foram analisados por dois revisores independentes. No total foram 27 ensaios clínicos randomizados, com acompanhamento mínimo de 2 anos, foram os qualificados para realizar a revisão e meta-análise em rede. Os resultados de meta-análise em rede mostraram que em cavidades classe III cimento de ionômero de vidro modificado (CIV modificado), foi significativamente mais propenso a falhas do que a resina composta (RC), em restaurações classe I e II, o compômero foi significativamente mais propenso a falhas do que a RC e em restaurações classe V o cimento de ionômero convencional (CIV convencional) foi significativamente mais propenso a falhas do que o CIV modificado. No estudo in vitro foi evidente o maior potencial de inibição da desmineralização dos materiais bioativos. Na revisão sistemática ficou evidente que a maioria de materiais bioativos apresentam um bom comportamento, em relação as taxas de retenção e desempenho clínico. (AU)

The objective of the clinical trial was to evaluate the clinical performance of 2 bioactive materials (Cention N and EQUIA Forte) compared to composite resin. The in vitro study aimed to evaluate the development of caries lesions induced by bacterial cariogenic challenge at the margin of enamel and dentin restorations with Cention N with and without adhesive, EQUIA Forte and composite resin. The systematic review aimed to answer the following question: Does the clinical evaluation of restorations in permanent teeth with bioactive materials show greater success than restorations with nonbioactive materials? For the clinical study, 120 participants were randomly selected and divided into 3 groups (n=40), TC: Tetric N-Ceram, EF: EQUIA Forte, CN: Cention N. The filling of the cavities was performed following the manufacturer's instructions. The DIAGNOdentTM Pen fluorescence device was used to assess caries recurrence. In the in vitro study, 100 specimens were made from bovine teeth. They were divided into 5 groups (n=20) half in enamel and half in dentin: Cention N without adhesive (CN), Cention N with adhesive (CA), EQUIA Forte (EF); Tetric N-Ceram (TC); and without restoration (SR). They were subjected to thermal aging; initial Knoop microhardness (KHN) reading, sterilized and exposed to a cariogenic challenge with Streptococcus mutans for 28 days. Artificial caries lesions were quantified using surface and subsurface KHN and analysis with polarized light microscopy. Data were submitted to 1-way ANOVA and Tukey test on enamel and Kruskal-Wallis test on dentin. In enamel, groups EF, CN, CA had the lowest percentage of microhardness loss (%PMS) 57.85%, 63.88% and 66.65% respectively. In dentin, EF, CN and CA presented lower %PMD values, being 31.7%, 34.1% and 40.8% respectively. The highest %PMS values were recorded for the TC and SR groups in both dentin and enamel. In the systematic review, based on the research question and PICO strategy: P- Permanent teeth, I- Restorations (class I, class II, class III, class V) with bioactive materials, C- Restoration with non-bioactive materials, O- Retention; the search strategy was designed. After obtaining the studies, they were analyzed by two independent reviewers. In total, 27 randomized clinical trials, with a minimum followup of 2 years, were qualified to perform the review and network meta-analysis. The results of network meta-analysis showed that in class III cavities modified glass ionomer cement (modified GIC) was significantly more prone to failure than composite resin (RC), in class I and II restorations, the compomer was significantly more prone to failure than RC and in class V restorations the conventional ionomer cement (conventional GIC) was significantly more prone to failure than the modified GIC. In the in vitro study, the greatest potential for inhibiting the demineralization of bioactive materials was evident. In the systematic review it was evident that most bioactive materials have a good behavior in relation to retention rates and clinical performance (AU).