Ion release of the glass ionomer restoration with silver diamine fluoride dentin pretreatment.

OBJECTIVE: To assess the fluoride and silver ion release of glass ionomer cement (GIC) restorations, including conventional GIC (CGIC) and resin-modified GIC (RMGIC) restorations, with 38% silver diamine fluoride (SDF) solution dentin pretreatment. METHODS: Eighty dentin blocks were allocated into 4 groups and restored with SDF+CGIC, CGIC, SDF+RMGIC and RMGIC, respectively. Each block was stored in deionized water at 37°C for 2 years. Fluoride and silver ion concentration in storage solution was measured using ion-selective electrode and inductively coupled plasma-optical emission spectrometry for up to 2 years. The cross-sectional surfaces of restored dentin blocks were assessed by X-Ray diffraction analysis (XRD), scanning electron microscope (SEM) with energy-dispersive X-ray spectroscopy (EDS) after 1 week and 2 years, respectively. RESULTS: The mean ± standard deviation (SD) of accumulative fluoride releasing in SDF+CGIC, CGIC, SDF+RMGIC and RMGIC for 2 years were 0.13±0.005 mg, 0.09±0.006 mg, 0.15±0.008 mg and 0.05±0.003 mg, respectively (Groups SDF+RMGIC > SDF+CGIC > CGIC >RMGIC, p<0.05). The mean ± SD of accumulative silver releasing in SDF+CGIC, CGIC, SDF+RMGIC and RMGIC for 2 years were 0.03±0.009 mg, 0.00±0.00 mg, 0.01±0.003 mg, and 0.00±0.00 mg, respectively (Groups SDF+CGIC > SDF+RMGIC > CGIC&RMGIC, p<0.05). Groups SDF+CGIC and SDF+RMGIC showed sustainably higher fluoride and silver releasing compared to Groups CGIC and RMGIC (p<0.05). XRD analysis indicated the fluorapatite and silver chloride were observed only in Groups SDF+CGIC and SDF+RMGIC, but not in Groups CGIC and RMGIC. SEM images of the cross-sectional view of the dentin blocks showed silver crystals within dentinal tubules 1 week and 2-year in Groups with SDF pretreatment. CONCLUSION: The 38% SDF dentin pretreatment sustainably increased the fluoride and silver release of GIC and RMGIC restorations for up to 2 years.

Synergistic Bactericidal Effect of Zn2+ Ions and Reactive Oxygen Species Generated in Response to Either UV or X-ray Irradiation of Zn-Doped Plasma Electrolytic Oxidation TiO2 Coatings.

Zn-containing TiO2-based coatings with Na, Ca, Si, and K additives were obtained by plasma electrolytic oxidation (PEO) of Ti in order to achieve an effective and broad bactericidal protection without compromising biocompatibility. A protocol has been developed for cleaning the coating surface from electrolyte residues, ensuring the preservation of the microstructure and composition of the surface layer. Using high-resolution transmission electron microscopy, three characteristic microstructural zones in the PEO-Zn coating are well documented: zone 1 with a TiO2-based nanocrystalline structure, zone 2 with an amorphous structure, and zone 3 around pores with an amorphous-nanocrystalline structure. The excellent cytocompatibility of PEO-Zn samples was confirmed by three different methods: monitoring the proliferation of MC3T3-E1 cells, assessing the viability of sheep osteoblast cells using calcein-AM staining and fluorescence microscopy, and incubation with spheroids based on primary osteoblast cells and mouse embryonic fibroblast NIH3T3 cells. The PEO-Zn coatings absorb >60% of the incident light over the UV and Vis-NIR spectral ranges. After 24 h, the PEO-Zn coatings completely inactivate four types of strains: Gram-positive Staphylococcus aureus CSA154 and ATCC29213 and Gram-negative Escherichia coli K261 and U20, and also prevent E. coli U20 and K261 biofilm formation. The superior antibacterial activity is associated with the synergistic effect of Zn2+ ions in safe concentration and reactive oxygen species (ROS) generated in response to either UV irradiation or soft short-term X-ray irradiation. The X-ray irradiation-induced ROS formation by a PEO coating is reported for the first time. The enhanced bactericidal activity after X-ray irradiation compared to UV illumination is attributed to the more intense ROS generation in the first few hours. The results obtained significantly expand the possibilities of using PEO coatings on the surfaces of titanium implants.

Ion Release and Apatite Formation of Resin Based Pit and Fissure Sealants Containing 45S5 Bioactive Glass.

The purpose of this study was to evaluate a resin based pit and fissure sealant containing 45S5 bioactive glass (BAG) by examining its ion release, pH variation, and apatite-forming properties. To prepare the experimental materials, 45S5 BAG, used as a filler, was incorporated into the light curable resin matrix at concentrations of 0 (control), 12.5, 37.5, and 50.0 wt.%. Ion release, pH variation, and apatite formation (Raman spectrometer and scanning electron microscopy-energy-dispersive X-ray spectrometry measurements) were performed. While no ions were released from the control group, the experimental groups containing 45S5 BAG showed an increased release of Ca and P ions with increasing amounts of 45S5 BAG (p < 0.05). The pH of the experimental group remained high and was significantly different from the control group (p < 0.05). Unlike the control group, it was confirmed that the apatite peak was formed in the 50.0 wt.% BAG group for 90 days, and the apatite layer consisting of Ca and P was deposited on the surface. Thus, a resin based pit and fissure sealant containing 45S5 BAG is a promising material for preventing secondary caries by releasing ions and forming apatite.

Evaluation of setting kinetics, mechanical strength, ion release, and cytotoxicity of high-strength glass ionomer cement contained elastomeric micelles.

BACKGROUND: Low mechanical properties are the main limitation of glass ionomer cements (GICs). The incorporation of elastomeric micelles is expected to enhance the strength of GICs without detrimentally affecting their physical properties and biocompatibility. This study compared the chemical and mechanical properties, as well as the cytotoxicity, of elastomeric micelles-containing glass ionomer cement (DeltaFil, DT) with commonly used materials, including EQUIA Forte Fil (EF), Fuji IX GP Extra (F9), and Ketac Molar (KT). METHOD: Powder particles of GICs were examined with SEM-EDX. Setting kinetics were assessed using ATR-FTIR. Biaxial flexural strength/modulus and Vickers surface microhardness were measured after immersion in water for 24 h and 4 weeks. The release of F, Al, Sr, and P in water over 8 weeks was analyzed using a fluoride-specific electrode and ICP-OES. The toxicity of the material extract on mouse fibroblasts was also evaluated. RESULTS: High fluoride levels in the powder were detected with EF and F9. DT demonstrated an initial delay followed by a faster acid reaction compared to other cements, suggesting an improved snap set. DT also exhibited superior flexural strength than other materials at both 24 h and 4 weeks but lower surface microhardness (p < 0.05). EF and F9 showed higher release of F, Al, and P than DT and KT. There was no statistically significant difference in fibroblast viability among the tested materials (p > 0.05). CONCLUSIONS: Elastomeric micelles-containing glass ionomer cement (DT) exhibited satisfactory mechanical properties and cytocompatibility compared with other materials. DT could, therefore, potentially be considered an alternative high-strength GIC for load-bearing restorations.

Preparation and Characterization of Nanofiber Coatings on Bone Implants for Localized Antimicrobial Activity Based on Sustained Ion Release and Shape-Preserving Design.

Titanium (Ti), as a hard tissue implant, is facing a big challenge for rapid and stable osseointegration owing to its intrinsic bio-inertness. Meanwile, surface-related infection is also a serious threat. In this study, large-scale quasi-vertically aligned sodium titanate nanowire (SNW) arrayed coatings incorporated with bioactive Cu2+ ions were fabricated through a compound process involving acid etching, hydrothermal treatment (HT), and ion exchange (IE). A novel coating based on sustained ion release and a shape-preserving design is successfully obtained. Cu2+ substituted Na+ in sodium titanate lattice to generate Cu-doped SNW (CNW), which maintains the micro-structure and phase components of the original SNW, and can be efficiently released from the structure by immersing them in physiological saline (PS) solutions, ensuring superior long-term structural stability. The synergistic effects of the acid etching, bidirectional cogrowth, and solution-strengthening mechanisms endow the coating with higher bonding strengths. In vitro antibacterial tests demonstrated that the CNW coatings exhibited effective good antibacterial properties against both Gram-positive and Gram-negative bacteria based on the continuous slow release of copper ions. This is an exciting attempt to achieve topographic, hydrophilic, and antibacterial activation of metal implants, demonstrating a paradigm for the activation of coatings without dissolution and providing new insights into insoluble ceramic-coated implants with high bonding strengths.

The Effect of Implantoplasty on the Fatigue Behavior and Corrosion Resistance in Titanium Dental Implants.

Implantoplasty is a technique increasingly used to remove the biofilm that causes peri-implantitis on dental implants. This technique of mechanization of the titanium surface makes it possible to eliminate bacterial colonies, but it can generate variations in the properties of the implant. These variations, especially those in fatigue resistance and electrochemical corrosion behavior, have not been studied much. In this work, fatigue tests were performed on 60 dental implants without implantoplasty, namely 30 in air and 30 in Hank's solution at 37 °C, and 60 with implatoplasty, namely 30 in air and 30 in Hank's solution at 37 °C, using triaxial tension-compression and torsion stresses simulating human chewing. Mechanical tests were performed with a Bionix servo-hydraulic testing machine and fracture surfaces were studied by scanning electron microcopyElectrochemical corrosion tests were performed on 20 dental implants to determine the corrosion potentials and corrosion intensity for control implants and implantoplasty implants. Studies of titanium ion release to the physiological medium were carried out for each type of dental implants by Inductively Coupled-Plasma Mass Spectrometry at different immersion times at 37 °C. The results show a loss of fatigue caused by the implantoplasty of 30%, observing that the nucleation points of the cracks are in the areas of high deformation in the areas of the implant neck where the mechanization produced in the treatment of the implantoplasty causes an exaltation of fatigue cracks. It has been observed that tests performed in Hank's solution reduce the fatigue life due to the incorporation of hydrogen in the titanium causing the formation of hydrides that embrittle the dental implant. Likewise, the implantoplasty causes a reduction of the corrosion resistance with some pitting on the machined surface. Ion release analyses are slightly higher in the implantoplasted samples but do not show statistically significant differences. It has been observed that the physiological environment reduces the fatigue life of the implants due to the penetration of hydrogen into the titanium forming titanium hydrides which embrittle the implant. These results should be taken into account by clinicians to determine the convenience of performing a treatment such as implantoplasty that reduces the mechanical behavior and increases the chemical degradation of the titanium dental implant.

Environmental factors modify silver nanoparticles ecotoxicity in Chydorus eurynotus (Cladocera).

Silver nanoparticles (AgNPs) are among the most produced nanomaterials in the world and are incorporated into several products due to their biocide and physicochemical properties. Since freshwater bodies are AgNPs main final sink, several consequences for biota are expected to occur. With the hypothesis that AgNPs can interact with environmental factors, we analyzed their ecotoxicity in combination with humic acids and algae. In addition to the specific AgNPs behavior in the media, we analyzed the mortality, growth, and phototactic behavior of Chydorus eurynotus (Cladocera) as response variables. While algae promoted Ag+ release, humic acids reduced it by adsorption, and their combination resulted in an intermediated Ag+ release. AgNPs affected C. eurynotus survival and growth, but algae and humic acids reduced AgNPs lethality, especially when combined. The humic acids mitigated AgNP effects in C. eurynotus growth, and both factors improved its phototactic behavior. It is essential to deepen the study of the isolated and combined influences of environmental factors on the ecotoxicity of nanoparticles to achieve accurate predictions under realistic exposure scenarios.

Controllable silver release for efficient treatment of drug-resistant bacterial-infected wounds.

The use of traditional Ag-based antibacterial agents is usually accompanied by uncontrollable silver release, which makes it difficult to find a balance between antibacterial performance and biosafety. Herein, we prepared a core-shell system of ZIF-8-derived amorphous carbon-coated Ag nanoparticles (Ag@C) as an ideal research model to reveal the synergistic effect and structure-activity relationship of the structural transformation of carbon shell and Ag core on the regulation of silver release behavior. It is found that Ag@C prepared at 600 °C (AC6) exhibits the best ion release kinetics due to the combination of relatively simple shell structure and lower crystallinity of Ag core, thereby exerting stronger antibacterial properties (> 99.999%) at trace doses (20 µg mL-1) compared with most other Ag-based materials. Meanwhile, the carbon shell prevents the metal Ag from being directly exposed to the organism and thus endows AC6 with excellent biocompatibility. In animal experiments, AC6 can effectively promote wound healing by inactivating drug-resistant bacteria while regulating the expression of TNF-α and CD31. This work provides theoretical support for the scientific design and clinical application of controllable ion-releasing antibacterial agents.

Investigating Bioactive-Glass-Infused Gels for Enamel Remineralization: An In Vitro Study.

OBJECTIVE: Dental hypersensitivity remains widespread, underscoring the need for materials that can effectively seal dental tubules. This study evaluated the potential of bioactive-glass-infused hydroxyethyl cellulose gels in this context. METHODS: Five gels were synthesized, each containing 20% bioactive glass (specifically, 45S5, S53P4, Biomin F, and Biomin C), with an additional blank gel serving as a control. Subjected to two months of accelerated aging at 37 ± 2 °C, these gels were assessed for key properties: viscosity, water disintegration time, pH level, consistency, adhesion to glass, and element release capability. RESULTS: Across the board, the gels facilitated the release of calcium, phosphate, and silicon ions, raising the pH from 9.00 ± 0.10 to 9.7 ± 0.0-a range conducive to remineralization. Dissolution in water occurred within 30-50 min post-application. Viscosity readings showed variability, with 45S5 reaching 6337 ± 24 mPa/s and Biomin F at 3269 ± 18 mPa/s after two months. Initial adhesion for the blank gel was measured at 0.27 ± 0.04 Pa, increasing to 0.73 ± 0.06 Pa for the others over time. Gels can release elements upon contact with water (Ca- Biomin C 104.8 ± 15.7 mg/L; Na- Biomin F 76.30 ± 11.44 mg/L; P- Biomin C 2.623 ± 0.393 mg/L; Si- 45S5-45.15 ± 6.77mg/L, F- Biomin F- 3.256 ± 0.651mg/L; Cl- Biomin C 135.5 ± 20.3 mg/L after 45 min). CONCLUSIONS: These findings highlight the gels' capacity to kickstart the remineralization process by delivering critical ions needed for enamel layer reconstruction. Further exploration in more dynamic, real-world conditions is recommended to fully ascertain their practical utility.

Dental Caries Management with Antibacterial Silver-Doped Prussian Blue Hydrogel by the Combined Effects of Photothermal Response and Ion Discharge.

Caries is a destructive condition caused by bacterial infection that affects the hard tissues of the teeth, significantly reducing the quality of life for individuals. Photothermal therapy (PTT) offers a noninvasive and painless treatment for caries, but the use of unsafe laser irradiance limits its application. To address this challenge, we prepared nanoparticles of silver ion-doped Prussian blue (AgPB), which was encased within cationic guar gum (CG) to form the antibacterial PTT hydrogel CG-AgPB with a photothermal conversion efficiency of 34.4%. When exposed to an 808 nm laser at a power density of 0.4 W/cm2, the hydrogel readily reached a temperature of over 50 °C in just 3 min, synchronized by the discharge of Ag+ ions from the interstitial sites of AgPB crystals, resulting in broad-spectrum and synergistic antibacterial activities (>99%) against individual oral pathogens (Streptococcus sanguinis, Streptococcus mutans, and Streptococcus sobrinus) and pathogen-induced biofilms. In vivo, CG-AgPB-mediated PTT demonstrated a capability to profoundly reduce the terminal number of cariogenic bacteria to below 1% in a rat model of caries. Given the outstanding biocompatibility, injectability, and flushability, this CG-AgPB hydrogel may hold promise as a next-generation oral hygiene adjunct for caries management in a clinical setting.

Ion release mechanisms in composites containing CaP particles and hydrophilic monomers.

OBJECTIVE: To investigate the effect of hydrophilic/permeable polymer matrices on water sorption/solubility (WS/SL), Ca2+ release, mechanical properties and hydrolytic degradation of composites containing dicalcium phosphate dihydrate (DCPD) particles. METHODS: Six composites were tested, all with 10 vol% of glass particles and either 30 vol% or 40 vol% DCPD. Composites containing 1BisGMA:1TEGDMA in mols (at both inorganic levels) were considered controls. Four materials were formulated where 0.25 or 0.5 of the BisGMA/TEGDMA was replaced by pyromellitic dianhydride glycerol dimethacrylate (PMGDM)/ polyethylene glycol dimethacrylate (PEGDMA). Composites were tested for degree of conversion (FTIR spectroscopy), WS/SL (ISO 4049) and Ca2+ release (inductively coupled plasma optical emission spectroscopy). Fracture toughness (FT) and biaxial flexural strength/modulus (BFS/FM) were determined after 24 h and 60 days in water. The contributions of diffusional and relaxational mechanisms to Ca2+ release kinetics were analyzed using the semi-empirical Salim-Peppas model. Data were analysed by ANOVA/Tukey test (alpha: 0.05). RESULTS: WS/SL was higher for composites containing PMGDM/PEGDMA compared to the controls (p < 0.001). Only at 40% DCPD the 0.5 PMGDM/PEGDMA composite showed statistically higher Ca2+ release than the control. Relaxation diffusion was the main release mechanism. Initial FT was not negatively affected by matrix composition. BFS (both DCPD fractions) and FM (30% DCPD) were lower for composites with hydrophilic/permeable networks (p < 0.01). After 60 days in water, composites with PMGDM/PEGDMA presented significant reductions in FT, while all composites had reductions in BFS/FM. SIGNIFICANCE: Increasing matrix hydrophilicity/permeability significantly increased Ca2+ release only at a high DCPD fraction.

Catalytic Dual-Mode Immunotherapy: Anisotropic AuPt Heterostructure Decorated with Starry Pt Nanoclusters for Robust Cancer Photometalloimmunotherapy.

To overcome current limitations in photoimmunotherapy, such as insufficient tumor antigen generation and a subdued immune response, a novel photo-/metallo dual-mode immunotherapeutic agent (PMIA) is introduced for potent near-infrared (NIR) light-triggered cancer therapy. PMIA features a dumbbell-like AuPt heterostructure decorated with starry Pt nanoclusters, meticulously engineered for enhancing plasmonic catalysis through multi-dimensional regulation of Pt growth on Au nanorods. Under NIR laser exposure, end-tipped Pt nanoclusters induce efficient electron-hole spatial separation along the longitudinal axis, resulting in radial and axial electron distribution polarization, conferring unique anisotropic properties to PMIA. Additionally, starry Pt nanoclusters on the sides of Au nanorods augment the local electron enrichment field. Validated through finite-difference time-domain analysis and Raman scattering, this configuration fosters local electron enrichment, facilitating robust reactive oxygen species generation for potent photoimmunotherapy. Moreover, Pt nanoclusters facilitate Pt2+ ion release, instigating intranuclear DNA damage and inducing synergistic immunogenic cell death (ICD) for metalloimmunotherapy. Consequently, PMIA elicits abundant danger-associated molecular patterns, promotes T cell infiltration, and triggers systemic immune responses, effectively treating primary and distant tumors, inhibiting metastasis in vivo. This study unveils a pioneering dual-mode ICD amplification strategy driven by NIR light, synergistically integrating photoimmunotherapy and metalloimmunotherapy, culminating in potent cancer photometalloimmunotherapy.

Cell viability assessment and ion release profiles of GICs modified with TiO2- and Mg-doped hydroxyapatite nanoparticles.

OBJECTIVES: To assess and compare the cell viability and ion release profiles of two conventional glass ionomer cements (GICs), Fuji IX and Ketac Molar EasyMix, modified with TiO2 and Mg-doped-HAp nanoparticles (NPs). METHODS: TiO2 NPs, synthesized via a sol-gel method, and Mg-doped hydroxyapatite, synthesized via a hydrothermal process, were incorporated into GICs at a concentration of 5 wt.%. The biocompatibility of prepared materials was assessed by evaluating their effects on the viability of dental pulp stem cells (DPSCs), together with monitoring ion release profiles. Statistical analysis was performed using One-way analysis of variance, with significance level p < 0.05. RESULTS: The addition of NPs did not significantly affect the biocompatibility of GICs, as evidenced by comparable decreased levels in cell viability to their original formulations. Distinct variations in cell viability were observed among Fuji IX and Ketac Molar, including their respective modifications. FUJI IX and its modification with TiO2 exhibited moderate decrease in cell viability, while other groups exhibited severe negative effects. While slight differences in ion release profiles were observed among the groups, significant variations compared to original cements were not achieved. Fluoride release exhibited an initial "burst release" within the initial 24 h in all samples, stabilizing over subsequent days. CONCLUSIONS: The addition of NPs did not compromise biocompatibility, nor anticariogenic potential of tested GICs. However, observed differences among FUJI IX and Ketac Molar, including their respective modifications, as well as induced low viability of DPSC by all tested groups, suggest the need for careful consideration of cement composition in their biological assessments. CLINICAL SIGNIFICANCE: The findings contribute to understanding the complex interaction between NPs and GIC matrices. However, the results should be interpreted recognizing the inherent limitations associated with in vitro studies. Further research avenues could explore long-term effects, in vivo performance, and potential clinical applications.

Remediation of Metal Oxide Nanotoxicity with a Functional Amyloid.

Understanding the environmental health and safety of nanomaterials (NanoEHS) is essential for the sustained development of nanotechnology. Although extensive research over the past two decades has elucidated the phenomena, mechanisms, and implications of nanomaterials in cellular and organismal models, the active remediation of the adverse biological and environmental effects of nanomaterials remains largely unexplored. Inspired by recent developments in functional amyloids for biomedical and environmental engineering, this work shows their new utility as metallothionein mimics in the strategically important area of NanoEHS. Specifically, metal ions released from CuO and ZnO nanoparticles are sequestered through cysteine coordination and electrostatic interactions with beta-lactoglobulin (bLg) amyloid, as revealed by inductively coupled plasma mass spectrometry and molecular dynamics simulations. The toxicity of the metal oxide nanoparticles is subsequently mitigated by functional amyloids, as validated by cell viability and apoptosis assays in vitro and murine survival and biomarker assays in vivo. As bLg amyloid fibrils can be readily produced from whey in large quantities at a low cost, the study offers a crucial strategy for remediating the biological and environmental footprints of transition metal oxide nanomaterials.

Modified Titanium Surface with Nano Amorphous Calcium Phosphate@Chitosan Oligolactate as Ion Loading Platform with Multifunctional Properties for Potential Biomedical Application.

Titanium (Ti) is widely used in medical and dental implants. Calcium phosphate (CPs) coatings enhance Ti implants' osteoinductive properties, and additives further improve these coatings. Recently, a nano amorphous calcium phosphate (nACP) coating decorated with chitosan oligolactate (ChOL) and selenium (Se) showed immunomodulatory effects. This study investigates the surface morphology, composition, bioactivity, mechanical properties, and Se-release mechanism of the nACP@ChOL-Se hybrid coating on Ti substrates. Amorphous calcium phosphate (ACP) was synthesized, and the nACP@ChOL-Se hybrid coating was deposited on Ti substrates using in situ anaphoretic deposition. Physico-chemical characterization was used to analyze the surface of the coating (scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier Transform Infrared Spectroscopy). The distribution of Se within the coating was examined with energy-dispersive X-ray spectroscopy (EDS). Bioactivity was evaluated in simulated body fluid (SBF), and adhesion was tested using a scratch test method. In vitro testing determined the release mechanism of Se. SEM images illustrated the surface morphology, while AFM provided a detailed analysis of surface roughness. XRD analysis revealed structural and phase composition, and EDS confirmed Se distribution within the coating. The coating exhibited bioactivity in SBF and showed good adhesion according to the scratch test. In vitro testing uncovered the release mechanism of Se from the coating. This study successfully characterized the surface morphology, composition, bioactivity, and Se-release mechanism of the nACP@ChOL-Se hybrid coating on Ti substrates, offering insights for developing immunomodulatory coatings for medical and dental applications.

Biocompatibility and acid resistance of preformed crowns in children: an in vitro study.

PURPOSE: To investigate the in vitro biocompatibility of human gingival fibroblasts with preformed paediatric crowns and resistance to acid exposure at levels that simulate the oral environment. METHODS: This laboratory study investigated primary HGFs viability, metabolic activity, cytotoxicity, and apoptotic events on preformed metal crown discs, composite resin-coated wells, and monolithic zirconia fragments at 24, 48, and 72 h using the ApoTox-Glo Triplex assay. The PPCs were also immersed in 0.1% lactic acid, 0.2% phosphoric acid, or 10% citric acid for 7 days at 37 °C to reproduce conditions associated with dietary intake or gastric reflux. Samples were then subject to inductively coupled plasma optical emission spectrometry to quantitate the release of ions. RESULTS: The viability of HGFs on stainless steel and CR significantly declined at 48 and 72 h, representing potential cytotoxicity (p < 0.05). Cytotoxicity of HGFs was also higher for stainless steel and ZR compared to control (p < 0.05). PMCs and ZR crowns gave minimal ion release. Meanwhile, significant quantities of metallic ions, including copper (Cu), iron (Fe), nickel (Ni), and zinc (Zn), were present in eluates from veneered-preformed metal crowns. CONCLUSION: As PPCs can be exposed to highly acidic environments for many years, thus the release of metallic ions from V-PMCs should form the further investigation in future studies.

Impacts of Differentially Shaped Silver Nanoparticles with Increasingly Complex Hydrophobic Thiol Surface Coatings in Small-Scale Laboratory Microcosms.

We investigated the impacts of spherical and triangular-plate-shaped lipid-coated silver nanoparticles (AgNPs) designed to prevent surface oxidation and silver ion (Ag+) dissolution in a small-scale microcosm to examine the role of shape and surface functionalization on biological interactions. Exposures were conducted in microcosms consisting of algae, bacteria, crustaceans, and fish embryos. Each microcosm was exposed to one of five surface chemistries within each shape profile (at 0, 0.1, or 0.5 mg Ag/L) to investigate the role of shape and surface composition on organismal uptake and toxicity. The hybrid lipid-coated AgNPs did not result in any significant release of Ag+ and had the most significant toxicity to D. magna, the most sensitive species, although the bacterial population growth rate was reduced in all exposures. Despite AgNPs resulting in increasing algal growth over the experiment, we found no correlation between algal growth and the survival of D. magna, suggesting that the impacts of the AgNPs on bacterial survival influenced algal growth rates. No significant impacts on zebrafish embryos were noted in any exposure. Our results demonstrate that the size, shape, and surface chemistry of AgNPs can be engineered to achieve specific goals while mitigating nanoparticle risks.

Novel pit and fissure sealant with nano-CaF2 and antibacterial monomer: Fluoride recharge, microleakage, sealing ability and cytotoxicity.

Conventional resin-based sealants release minimal fluoride ions (F) and lack antibacterial activity. The objectives of this study were to: (1) develop a novel bioactive sealant containing calcium fluoride nanoparticles (nCaF2) and antibacterial dimethylaminohexadecyl methacrylate (DMAHDM), and (2) investigate mechanical performance, F recharge and re-release, microleakage, sealing ability and cytotoxicity. Helioseal F served as commercial control. The initial F release from sealant containing 20% nCaF2 was 25-fold that of Helioseal F. After ion exhaustion and recharge, the F re-release from bioactive sealant did not decrease with increasing number of recharge and re-release cycles. Elastic modulus of new bioactive sealant was 44% higher than Helioseal F. The new sealant had excellent sealing, minimal microleakage, and good cytocompatibility. Hence, the nanostructured sealant had substantial and sustained F release and antibacterial activity, good sealing ability and biocompatibility. The novel bioactive nCaF2 sealant is promising to provide long-term F ions for caries prevention.

Characterisation of experimental flowable composites containing fluoride-doped calcium phosphates as promising remineralising materials.

OBJECTIVE: Remineralising composites with antibacterial properties may seal the cavity and prevent secondary caries. This study aimed at developing experimental flowable composites containing different concentrations of fluoride-doped calcium phosphate fillers and evaluating their remineralising and antibacterial properties. METHODS: Experimental resin-based composites containing different concentrations (0-20 %) of fluoride-doped calcium phosphate fillers (VS10/VS20) were formulated. The release of calcium (Ca), phosphate (PO) and fluoride (F) ions was assessed for 30 days. Remineralisation properties were evaluated through ATR-FTIR and SEM/EDX after storage in simulated body fluid (SBF). The metabolic activity and viability of Streptococcus gordonii was also evaluated through ATP, CFU and live/dead confocal microscopy. The evaluation of specific monomer elution from the experimental composites was conducted using high-performance liquid chromatography (HPLC). RESULTS: The composites containing VS10 showed the highest release of Ca, those containing VS20 released more F over time (p < 0.05), while there was no significant difference in terms of PO ions release between the groups (p > 0.05). A quick 7-day mineral precipitation was observed in the tested composites containing VS10 or VS20 at 10 %; these materials also showed the greatest antibacterial activity (p < 0.05). Moreover, the tested composites containing VS10 presented the lowest elution of monomers (p < 0.05). CONCLUSIONS: Innovative composites were developed with low monomers elution, evident antibacterial activity against S. gordonii and important remineralisation properties due to specific ions release. CLINICAL SIGNIFICANCE: Novel composites containing fluoride-doped calcium phosphates may be promising to modulate bacteria growth, promote remineralisation and reduce the risk of cytotoxicity related to monomers' elution.

Advancements in Biomedical Applications of Calcium Phosphate Glass and Glass-Based Devices-A Review.

Calcium phosphate (CaP) glass has recently gained popularity as a promising material for a wide range of biomedical applications. Recent developments have seen CaP glasses moving from a passive implant material to an active degradable material, particularly as a major constituent of bioresorbable photonic devices. This holds great promise in advanced biomedical applications, since the main constituents of CaP glasses are present in the human body. In this review, the progressive advancements in the biomedical applications of calcium phosphate glass-based devices over the past 50 years are discussed. An overview of their role as reinforcing agents and the studies on doping their matrices for ion releasing and drug and gene delivery are reviewed. Recent applications of CaP glass and fibers in soft-tissue engineering and their potential for optical quality bioresorbable devices are then discussed along with the current challenges and potential future directions, emphasizing the promising role of CaP glass in the next generation of biomaterials. Considering their progress and potential in performing several biomedical functionalities over time, CaP glass-based devices hold promise for becoming enabling tools as an implantable, bioresorbable, multifunctional class of devices in future biomedicine.