Análise do efeito de adição do marcador Rodamina B em propriedades mecânicas de sistemas adesivos não simplificados / Analysis of the effect of addition of Rhodamine B marker on mechanical properties of non-simplified adhesives

Este estudo in vitro avaliou o efeito da adição de rodamina B dissolvida em etanol nas concentrações de 0,02mg/mL e 0,10mg/mL, nas propriedades mecânicas dos sistemas adesivos não simplificados considerados padrão-ouro. 96 coroas de terceiros molares humanos hígidos foram seccionadas transversalmente no terço oclusal para remoção do esmalte e exposição da dentina. Os espécimes foram divididos de acordo com os sistemas adesivos Adper Scotchbond Multi-Purpose (MP) - convencional de três passos ou Clearfil SE Bond (SE) - autocondicionante de dois passos: MP-C e SE-C (MP e SE controles); MP-C1 e SE-C1 (MP e SE com rodamina B 0,02mg/mL); MP-C2 e SE-C2: (MP e SE com rodamina B 0,10mg/mL). Para o teste de RU, os espécimes (n=10) foram submetidos ao desgaste com lixas de granulação 320 e 600. A dentina foi tratada de acordo com as instruções de cada fabricante dos sistemas adesivos e restaurada com resina composta FiltekTM Z250. Após o armazenamento em saliva artificial (7dias/37oC), os espécimes foram seccionados para obtenção de palitos com 0,64 mm2 de área média e submetidos ao teste de microtração em máquina de teste universal a 0,5 mm/min, que foram analisados após 7 dias e 6 meses. O modo de fratura dos espécimes foi analisado com estereomicroscópio digital (x200) e classificado em: adesiva, coesiva em dentina, coesiva em resina e mista. Para o teste de MS, as coroas seccionadas (n=6) foram planificadas com lixa de granulação 600. A dentina foi tratada de acordo com as instruções de cada fabricante dos sistemas adesivos e os espécimes foram mantidos secos em estufa a 37oC durante 48 horas. O teste de MS foi realizado utilizando ponta Knoop (Microdurômetro Shimadzu HMV-2), a 10x e carga estática de 25gF por 10 segundos. Os resultados obtidos foram analisados por análise de variância (ANOVA-2 critérios) e teste de Bonferroni para comparações múltiplas (p<0,05). A análise de acordo com o tempo foi realizada com o teste de t-student. Os valores médios de RU...

This in vitro study evaluated the effect of addition of rhodamine B dissolved in ethanol in concentrations of 0.02mg/mL and 0.10mg/mL, the mechanical properties of non-simplified adhesive systems. 96 crowns of human third molars were transversely sectioned on the oclusal third to remove the enamel and exposure the dentin. The specimens were divided according to the adhesive systems Adper Scotchbond Multi-Purpose (MP) 3-step-etch-andrinse or Clearfil SE Bond (SE) 2-step-self-ecthing: MP-C and SE-C (MP and SE controls); MP-C1 and SE-C1 (MP and SE with 0.02mg/mL rhodamine B); MP-C2 and SE-C2: (MP and SE with 0.10mg/mL rhodamine B). For the ìTBS test, the specimens (n=10) were ground with 320- to 600-grit silicon carbide paper. The dentin was treated according to the instructions of each manufacturer and restored with composite resin FiltekTM Z250. The specimens were stored in artificial saliva (7 days/37oC), and then sectioned to obtain sticks with an average of 0.64 mm2 area and submitted to ìTBS test at a universal testing machine at 0.5 mm/min, which were analyzed immediately after 7 days and 6 months. The mode of fracture of the specimens was analyzed with digital stereomicroscope (x200) and classified as: adhesive, cohesive in dentine, cohesive in resin and mixed. For the SM test, the sectioned crowns (n=6) were flattened with 600-grit silicon carbide paper. The dentin was treated according to the manufacturers instructions for each adhesive system and the specimens were stored in dry condition at 37oC during 48 hours. The SM test was performed with Knoop indenter (Shimadzu HMV-2 hardness tester), at 10x and 25gF of load for 10 seconds. The results were analyzed by two-way analysis of variance tests and the Bonferroni test for multiple comparisons (p<0.05). The analysis regarding time was checked with t-student test. The mean ìTBS and standard deviation (MPa±dp; 7 days / 6 months) were...

Influência da estratificação térmica no volume útil e no comportamento hidrodinâmico de lagoa de estabilização: determinação experimental e teórica / Influence of thermal stratification in useful volume and in hydrodinamic behavior of stabilization pond: theoretical and experimental evaluation

Lagoas de estabilização localizadas em regiões com variações elevadas de temperatura ao longo do dia tendem a apresentar estratificação térmica, um fenômeno que altera o volume útil da lagoa. Neste trabalho, apresentam-se resultados experimentais obtidos em duas lagoas, facultativa e maturação, construídas na região central do estado de São Paulo. O acompanhamento do perfil de temperatura mostrou a ocorrência de estratificação térmica com ciclo nictimeral nas duas lagoas. Os ensaios hidrodinâmicos indicaram comportamento semelhante ao de reatores com mistura completa, com zonas mortas, volume útil de aproximadamente 60 por cento na lagoa facultativa e 30 por cento na lagoa de maturação. Os experimentos corroboraram os resultados teóricos obtidos com o modelo matemático para previsão da estratificação térmica.

Stabilization ponds located in places that present high temperature variations along the day have a tendency to present thermal stratification, a phenomenon that changes the useful volume of the pond. This paper presents experimental results from two stabilization ponds, facultative and maturation, built in the central area of the state of São Paulo, Brazil. The observation of the temperature profile showed the occurrence of thermal stratification with the nictimeral cycle in both ponds. Hydrodynamic tests showed a pattern that resembles the behavior of complete mixing reactors with dead zones, resulting in useful volumes close to 60 percent for the facultative pond and 30 percent for the maturation pond. The experiments confirm the theoretical results obtained based on a mathematical model to predict thermal stratification.