Welding strength of NiTi wires

ABSTRACT Objective: To identify the appropriate power level for electric welding of three commercial brands of nickel-titanium (NiTi) wires. Methods: Ninety pairs of 0.018-in and 0.017 × 0.025-in NiTi wires were divided into three groups according to their manufacturers - GI (Orthometric, Marília, Brazil), GII (3M OralCare, St. Paul, CA) and GIII (GAC,York, PA) - and welded by electrical resistance. Each group was divided into subgroups of 5 pairs of wires, in which welding was done with different power levels. In GI and GII, power levels of 2.5, 3, 3.5, 4, 4.5 and 5 were used, while in GIII 2.5, 3, 3.5 and 4 were used (each unit of power of the welding machine representing 500W). The pairs of welded wires underwent a tensile strength test on an universal testing machine until rupture and the maximum forces were recorded. Analysis of variance (ANOVA) and post-hoc tests were conducted to determine which subgroup within each brand group had the greatest resistance to rupture. Results: The 2.5 power exhibited the lowest resistance to rupture in all groups (43.75N for GI, 28.41N for GII and 47.57N for GIII) while the 4.0 power provided the highest resistance in GI and GII (97.90N and 99.61N, respectively), while in GIII (79.28N) the highest resistance was achieved with a 3.5 power welding. Conclusions: The most appropriate power for welding varied for each brand, being 4.0 for Orthometric and 3M, and 3.5 for GAC NiTi wires.

RESUMO Objetivo: identificar a potência mais adequada para solda elétrica em três marcas comerciais de fios de níquel-titânio (NiTi). Métodos: noventa pares de fios ortodônticos de NiTi, de dimensões 0,018" e 0,017" × 0,025'', foram soldados por resistência elétrica e distribuídos em três grupos: GI (Orthometric, Marília, São Paulo, Brasil), GII (3M, São José do Rio Preto, São Paulo, Brasil) e GIII (GAC, Yorque, Pensilvânia, Estados Unidos). Cada grupo foi dividido em subgrupos de cinco pares de fios soldados com diferentes níveis de potência. Nos GI e GII, os fios foram soldados com níveis de potência de 2.5, 3, 3.5, 4, 4.5 e 5; enquanto no GIII as potências utilizadas foram de 2.5, 3, 3.5 e 4. Os pares de fios foram submetidos a um teste de tração até sua ruptura, com registro das forças máximas. Análises de variância (ANOVA) e testes post-hoc foram realizados para determinar qual subgrupo, dentro de cada grupo, obteve a maior força de resistência. Resultados: a potência 2.5 exibiu a menor resistência à ruptura para todos os grupos (43,75 N para o GI; 28,41 N para o GII e 47,57 N para o GIII). A potência 4 mostrou maior resistência à ruptura nos GI e GII (97,90 N e 99,61 N, respectivamente), enquanto no GIII (79,28 N) foi a potência 3.5. Conclusões: os níveis de potência mais adequados variaram para as marcas comerciais, sendo identificados como 4 para Orthometric e 3M, e 3.5 para GAC.

Reabilitação oral implantossuportada de arco totalmente desdentado com a técnica da solda intraoral: caso clínico com dois anos de acompanhamento / Implant-supported oral rehabilitation of fully edentulous arch with an intraoral welding technique: clinical case with 2 years of follow-up

A reabilitação provisória rígida implantossuportada tem sido reconhecida por ter um impacto significativo sobre a resposta do tecido peri-implantar em carga imediata, uma vez que reduz a tensão mecânica exercida sobre cada implante. Um protocolo de sucesso para a carga imediata com implantes múltiplos depende de uma fixação adequada e da ausência de mobilidade dos implantes para evitar o risco de micromovimentos em relação ao osso circundante. O objetivo deste artigo foi demonstrar um conceito de prótese implantossuportada com uma esplintagem rígida rápida de vários implantes cone-morse com carregamento imediato para o mesmo dia da cirurgia, com uma reabilitação provisória reforçada por uma liga metálica, usando uma técnica de soldagem dos pilares de implantes diretamente na cavidade bucal com uma barra de titânio pré-fabricada.

The rigid implant-supported provisional rehabilitation has been recognized to have a significant impact on the peri-implant tissue response in immediate implant loading since it reduces the mechanical stress exerted on each implant. A successful protocol for immediate loading of multiple implants depends on an adequate fixation and immobility of the implants to prevent the risk of micromovements in relation to the surrounding bone. The objective of this article was show a implant-supported rehabilitation concept with a fast rigid splinting of multiple tapered connection implants for same-day immediate loading with metal-reinforced provisional restorations using a technique of welding implant abutments with a prefabricated titanium bar directly in the oral cavity.

Avaliação da adaptação das infraestruturas metálicas em próteses fixas: monobloco versus solda ( revisão de literatura) / Adaptation assessment of infra structures in fixed prosthesis: monobloco versus welding

A adaptação das infraestruturas metálicas representa um passo fundamental na longevidade das próteses fixas dentossuportadas e, principalmente, implantossuportadas. A comparação dos diferentes métodos de obtenção das infraestruturas se faz necessário para compreendermos as limitações inerentes a cada um desses processos. A literatura atual enfatiza os menores índices de desadaptação das infraestruturas soldadas, em comparação com as infraestruturas em monobloco, apesar de encontrarmos autores que apresentam dados que contestam essa superioridade dos sistemas de solda

Adaptation of metallic infrastruture is a key step in the longevity of dentossuportadas ans mainly implant-fixed prostheses. The comparison between the different methods of obtaining infrastructure is needed to understand the limitations inherent in each of these processes. Current literature emphasizes the smaller indices mismatch welded infrastructure compared with infrastructure one-piece cast, although we found that authors who challenge the superiority of welding systems

Análise comparativa do grau de rotação de parafusos para sistema UCLA em estruturas fundidas em monobloco, soldadas com solda TIG e solda convencional / Comparative analysis of the degree of rotation of screws for UCLA system in one-piece cast structures welded with TIG and Conventional welding

Com disseminação dos implantes osseointegrados na pratica clinica a ocorrência de complicações mecânicas tornam-se comuns, causando problemas para pacientes e profissionais. O objetivo deste estudo foi comparar o grau de rotação de parafusos de titânio (grau 5), durante testes de torque, re-torque e os valores de destorque (Ncm), sobre infra-estruturas fundidas em monobloco, soldadas com solda TIG e solda Convencional, a partir de abutments tipo UCLA com cinta usinada em Co-Cr. Um dispositivo leitor da quantidade de graus foi especialmente desenvolvido para este estudo, juntamente com um software. Seis implantes Titaniun Fix de 3,75 mm de diâmetro e 13 mm de comprimento e hexágono externo foram montados na base de um dispositivo e diretamente sobre eles foram obtidos os padrões para fundição dos corpos de prova. Para os grupos que foram submetidos a soldagem os corpos foram montados à análogos de implantes Titaniun Fix, e vazados blocos de gesso especial tipo IV (Durone) para serem seccionados e fundidos. Cada corpo de prova foi formado por dois abutments tipo UCLA com cinta em Co-Cr, interligados por uma barra acrílica. Foram obtidos 10 corpos de prova para cada grupo e 60 parafusos de titânio (Grau 5- Titaniun Fix) foram usados para os testes. Obteve-se então a medição do ângulo criado durante o aperto e re-aperto dos parafusos, sendo o re-aperto realizado após 10 minutos do aperto inicial, ambos sob torque de 30Ncm. Após o procedimento de re-aperto, o valor de destoque era imediatamente aferido e anotado em Ncm, possibilitando avaliar a quantidade de torque retido pelo parafuso após o procedimento, sendo esta seqüência realizada 3 vezes para cada corpo de prova. Sendo a análise estatística realizada para essa comparação (ANOVA) Análise de Variância a um critério de classificação, o teste Tukey, para verificar se havia diferença estatística entre os grupos. Os resultados revelaram que durante os procedimentos de torque (aperto), os...

With the spread of osseointegrated implants in clinical practice the incidence of mechanical complications have become common, causing problems for patients and professionals. The aim of this study was to compare the degree of rotation of titanium screws, during testing of torque, re-torque and destorque values (Ncm) in one-piece casting infrastructures, welded with TIG and Conventional welding, from UCLA strap machined Cr-Co abutments. A reader device for the number of degrees has been specially developed for this study, together with a software. Titaniun Fix implants (n=6) of 3.75mm in diameter and 13mm in length and external hexagon were mounted at the base of a device and they were obtained directly from the casting patterns of the specimens. Groups that were subjected to welding were mounted to the implant analogues, submitted to special plaster type IV (Durone) blocks. Each sample was formed by two UCLA type abutments with strap on Co-Cr, connected by an acrylic bar. It were obtained 10 specimens for each group and 60 titanium screws (Grade 5 - Titaniun Fix) were used for testing. The measurement of the angle created during tightening and re-tightening the screws, and re-grip performed 10 minutes after the initial torque, both under torque 30Ncm were obtained. After re-tightening procedure, the value of destoque was immediately measured and recorded in Ncm, to evaluate the amount of torque by the screw retained after the procedure, being this sequence performed three times for each specimen. The statistical analysis used were, analysis of variance (1 way - ANOVA) and the Tukey test to see whether there were differences between the groups. The results revealed that during the procedures of torque (tightening), the screws used in the one-piece infrastructure castings showed a higher degree of rotation (56,12°) compared to the screws used on targeted infrastructure and rendered separately welded with TIG (43,2°) and Conventional welding with a mean value...

Citotoxicidade de soldas ortodônticas à prata / Cytotoxic orthodontic welding of the silver

O objetivo do presente trabalho foi avaliar a citotoxicidade de soldas à prata. Foram avaliadas soldas à prata divididos em 4 grupos assim denominados: AAS (aço com aço sem polimento), AAC (aço com aço com polimento), ALS (aço com latão sem polimento) e ALC (aço com latão com polimento). Previamente, os corpos de prova foram esterilizados em luz ultravioleta (UV). Após isso os mesmos foram imersos em meio mínimo essencial de Eagle (MEM) por 24h, então procedeu-se a remoção do sobrenadante e colocação em contato com fibroblastos L929. Após contato com o meio as células foram incubadas por mais 24 h, então foram adicionados 100ml do corante vermelho neutro a 0,01%. Novamente as células foram incubadas por 3 hs para que as mesmas incorporasse o corante. Passado esse período as células foram fixadas e então realizada contagem de células viáveis em espectrofotômetro (BioTek, Winooski, Vermont, USA) em um comprimento de onda de 492nm (l = 492 nm). Os resultados demonstraram não haver diferenças estatísticas entre os grupos experimentais (AAS, AAC, ALS e ALC) (P>0.05). Diferenças estatísticas foram observadas entre os grupos C+ com os demais assim como o C- e CC com os grupos experimentais (P<0.05). Pode-se concluir com a realização desse trabalho que as soldas à prata são altamente citotoxicas e o polimento diminui sua citotoxicidade.