Effect of treatment with phosphate, casein phosphopeptide and fluoride on the remineralization: in vitro study.

This study aimed to evaluate in vitro the effect protocols and anticaries agents containing casein amorphous calcium fluoride phosphopeptide-phosphate (CPP-ACPF, MI Paste Plus), sodium trimetaphosphate (TMP) and fluoride (F), in remineralization of caries lesions. Bovine enamel blocks with initial caries lesions were divided into groups (n = 12): 1) Toothpaste without F-TMP-MI Plus (Placebo); 2) Toothpaste 1100 ppm F (1100F), 3) 1100F + MI Paste Plus (1100F-MI Paste Plus), 4) Toothpaste with 1100F + Neutral gel with 4,500 ppm F + 5%TMP (1100F + Gel TMP) and 5) Toothpaste with 1100F + Neutral gel with 9,000 ppm F (1100F + Gel F). For the 4 and 5 groups the gel was applied only once for 1 minute, initially to the study. For the 3 group, after treatment with 1100F, MI Paste Plus was applied 2x/day for 3 minute. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile and depth of the subsuperficial lesion (PLM); concentrations of F, calcium (Ca) and phosphorus (P) in enamel was determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). Treatment with 1100F alone led to ~ 28% higher remineralization when compared to treatment with 1100F associated with MI Paste Plus (p < 0.001). The 1100F and 1100F + Gel F groups showed similar values for %SHR (p = 0.150). 1100F + Gel TMP treatment also remineralized the enamel surface by ~ 30% and 20% when compared to the 1100F + Gel F and 1100F groups (p < 0.001). The lower lesion depth (ΔKHN) was observed for the 1100F + Gel TMP group (p < 0.001), where it was 54% and 44% lower in comparison to the 1100F and 1100F + Gel F groups (p < 0.001). Polarized light microscopy photomicrographs showed subsurface lesions in all groups, but these lesions were present to a lower extent in the 1100F + Gel TMP group (p < 0.001). Treatment with 1100F + Gel TMP promoted an increase in the concentration of Ca in the enamel by ~ 57% and ~ 26% when compared to the 1100F and 1100F + MI Paste Plus groups (p < 0.001), respectively. There were no significant differences between the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001). Similar values of P in the enamel were observed in the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001), except for the 1100F + Gel TMP group, which presented a high concentration (p < 0.001). We conclude that the 1100F+TMP gel treatment/protocol led to a significant increased remineralization when compared to the other treatments/protocols and may be a promising strategy for patients with early caries lesions.

Inhibition of incipient caries lesion progression by different fluoridated varnishes.

The aim of this in vitro study was to evaluate the potential of different fluoridated varnishes to inhibit the progression of incipient caries lesions after cariogenic challenge. Seventy-five enamel specimens of bovine teeth were prepared and selected based on the initial surface microhardness (SMH). The specimens were first subjected to artificial demineralization (in buffer solution) after which SMH was re-analyzed (SM1). They were then randomly assigned to five experimental groups: 1- CONTROL (pH cycling), 2 - MI VAR (MI Varnish with RECALDENTTM - CPP-ACP), 3 - PROFL (Profluorid®), 4 - CLIN (ClinproTM White Varnish with TCP), and 5 - DUR (Duraphat®) (n=15). The varnishes were applied in a thin layer and the specimens were then subjected to pH cycling for eight days. The SMH and cross-sectional microhardness (CSMH) were then analyzed (SM2). The fluoride and calcium ion concentrations in the solution were analyzed by the indirect method and atomic absorption spectrophotometry, respectively. Data were statistically analyzed by Student's t-test, ANOVA/Tukey-Kramer, or Kruskall-Wallis/Dunn tests for individual comparisons (p˂0.05). All varnishes led to significantly higher surface and subsurface remineralization compared with the control group but did not differ from each other. The varnishes with the highest fluoride release were: PROFL and CLIN, followed by MI VAR and DUR. The varnishes with significantly higher release of calcium were: DUR, CLIN, and PROFL. In conclusion, all commercial fluoridated varnishes tested have good potential to inhibit the progression of demineralization, regardless of the ion release mechanisms.

Arginine and sodium fluoride affect the microbial composition and reduce biofilm metabolism and enamel mineral loss in an oral microcosm model.

OBJECTIVE: To assess the effects of arginine, with or without sodium fluoride (NaF; 1,450 ppm), on saliva-derived microcosm biofilms and enamel demineralization. METHODS: Saliva-derived biofilms were grown on bovine enamel blocks in 0.2 % sucrose-containing modified McBain medium, according to six experimental groups: control (McBain 0.2 %); 2.5 % arginine; 8 % arginine; NaF; 2.5 % arginine with NaF; and 8 % arginine with NaF. After 5 days of growth, biofilm viability was assessed by colony-forming units counting, laser scanning confocal microscopy was used to determine biofilm vitality and extracellular polysaccharide (EPS) production, while biofilm metabolism was evaluated using the resazurin assay and lactic acid quantification. Demineralization was evaluated by measuring pH in the culture medium and calcium release. Data were analyzed by Kruskal-Wallis' and Dunn's tests (p < 0.05). RESULTS: 8 % arginine with NaF showed the strongest reduction in total streptococci and total microorganism counts, with no significant difference compared to arginine without NaF. Neither 2.5 % arginine alone nor NaF alone significantly reduced microbial counts compared to the control, although in combination, a reduction in all microbial groups was observed. Similar trends were found for biofilm vitality and EPS, and calcium released to the growth medium. CONCLUSIONS: 8 % Arginine, with or without NaF, exhibited the strongest antimicrobial activity and reduced enamel calcium loss. Also, NaF enhanced the effects of 2.5 % arginine, yielding similar results to 8 % arginine for most parameters analyzed. CLINICAL SIGNIFICANCE: The results provided further evidence on how arginine, with or without NaF, affects oral microcosm biofilms and enamel mineral loss.

In vitro effect of fluoride gels supplemented with nano-sized sodium trimetaphosphate on enamel erosive wear.

OBJECTIVE: To assess the protective effect of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) against enamel erosion in vitro. METHODS: Bovine enamel blocks (n = 140) were selected according to their surface hardness, and randomly divided into seven groups (n = 20/group), according to the gels tested: Placebo (without F/TMP), 4,500 µg F/g (4500F), 9,000 µg F/g (9000F), 4500F plus 2.5 % TMPnano (2.5 % Nano), 4500F plus 5 % TMPnano (5 % Nano), 4500F plus 5 % TMPnano (Micro 5 %) and 12,300 µg F/g (Acid gel). Blocks were treated once during one minute with the gels, and submitted to erosive (ERO, n = 10/group) or erosive plus abrasive (ERO+ABR, n = 10/group) challenges 4 times/day, for 90 s for each challenge (under reciprocating agitation), during consecutive 5 days. Blocks were analyzed by profilometry, and by surface (SH) and cross-sectional hardness (∆KHN). Data were submitted to two-way ANOVA, and Fisher's LSD test (p < 0.05). RESULTS: For ERO, both TMPnano-containing gels promoted enamel wear significantly lower than Placebo and 4500F, reaching levels similar to both positive controls (9000F and acid gel); significantly lower softening was observed for enamel treated with 4500F+5 % Micro and 4500F+2.5 % Nano. Also, the lowest ∆KHN values were observed for 4500F+2.5 % TMPnano among the TMP-containing gels. For ERO+ABR, the lowest enamel wear was achieved by the use of 4500F+5 % Nano among all gels, including both positive controls; lower softening was observed for Placebo and 9000F groups. CONCLUSION: The addition of 5 % nano-sized TMP to a low-fluoride gel produced superior protective effects for enamel under both challenges conditions, when compared with micrometric TMP, reaching values similar to or superior than both positive controls, respectively for ERO and ERO+ABR. CLINICAL SIGNIFICANCE: The supplementation of low-F gels with TMP was shown to significantly improve their effects on enamel erosive wear, and the use of nano-sized TMP further enhances this protective action.

Comparison of the effects of fluoride varnish containing silver nanoparticles and conventional fluoride varnish on the surface microhardness of tooth enamel.

BACKGROUND: Nano-silver fluoride (NSF) has been introduced to improve enamel lesions. The effective use of varnishes is important in the prevention of dental caries. OBJECTIVES: The study aimed to compare the effect of conventional sodium fluoride varnish with the same varnish containing 1% and 2% silver nanoparticles (AgNP) on the surface microhardness of enamel. MATERIAL AND METHODS: The baseline surface microhardness of 40 premolar teeth was measured using a Vickers microhardness tester. After immersing the samples in a demineralizing agent for 24 h, the microhardness was measured again. In group B, a layer of conventional fluoride varnish was applied to the tooth surfaces using a microbrush with soft bristles, following the manufacturer's instructions. Groups C and D were treated with 1% and 2% NSF varnishes, respectively, while group A received no varnish. Surface microhardness tests were conducted on all specimens, including those previously tested. RESULTS: The microhardness of the enamel surface increased significantly in all 3 test groups compared to the microhardness after demineralization (p < 0.05). CONCLUSIONS: Conventional fluoride varnish and fluoride varnishes containing 1% and 2% AgNP are equally effective in remineralizing initial caries.

Fluoride-amorphous calcium phosphate and biomimetic nano-hydroxyapatite for enamel remineralization: An in-vitro study of surface microhardness and composition.

AIM: Fluoride-Amorphous Calcium Phosphate and Biomimetic Nano-Hydroxyapatite for Enamel Remineralization; An In-Vitro Study of Surface Microhardness and Composition. MATERIAL AND METHODS: Ninety-six extracted human premolars with sound buccal surface were divided using a randomization computer-generating software into four groups; Group I (control) sound untreated enamel, Group II (demineralized) demineralized to create white spot lesions, Group III (biom-n-HA) demineralized and then treated with biomimetic nanohydroxyapatite cream, and Group IV (F-ACP) demineralized and then treated using Fluoride-Amorphous Calcium Phosphate varnish. Each group was divided into two subgroups; subgroup "A" evaluated for mineral content using energy dispersive x-ray spectroscopy (EDX) and for surface microhardness using the Vickers microhardness test and Subgroup "B" evaluated for white spot lesion depth using a polarized light microscope (PLM). RESULTS: The highest microhardness (VHN) was found in the (F-ACP) group (mean=428.61±54.43) and then in the (Biom-n-HA) group (mean=408.11±70.16) followed by the (Control) group (mean=402.13±53.40) with no significant difference between them and finally in the significantly different (Demineralized) group (mean=256.99±45.83). The weight percentage of Ca (30.29±1.04 and 33.44±1.07) and Ca/P ratio (1.87±0.06 and 2.03±0.05) were significantly different between Group III and Group IV respectively. PLM measurements in Group II (198.83µm), Group III (60.17µm), and Group IV (26.33µm) were significantly different. CONCLUSIONS: Both the (Biom-n-HA) cream and the (F-ACP) varnish showed promising results for enamel remineralization. The increased enamel surface microhardness was consistent with the mineral content and the changes in the birefringence.

Effect of adhesive components in experimental fluoride varnish on fluoride release within 30 days in vitro study.

We aimed to determine whether adhesive components could increase the release time of effective fluoride concentration from an experimental fluoride varnish applied to bovine teeth. An experimental fluoride varnish containing 5% sodium fluoride (EX1) was prepared and combined with 35% hydroxyethyl methacrylate (HEMA) (EX2), 5% glutaraldehyde (EX3), or 35% HEMA/5% glutaraldehyde mixture (EX4). Two commercially available fluoride varnishes were used for comparison. Each group was applied to bovine incisors, and the fluoride release and pH were monitored for 30 days. Cell viability analysis, scanning electron microscopy, and energy-dispersive spectroscopy were performed. EX4 released the highest and most effective concentration of fluoride for the longest period and reached neutral pH at the earliest; the release was maintained for up to 30 days without cytotoxicity. In conclusion, EX4 is considered to be the most effective varnish to prevent dental caries.

Amelogenin-inspired peptide, calcium phosphate solution, fluoride and their synergistic effect on enamel biomimetic remineralization: an in vitro pH-cycling model.

BACKGROUND: Several methods were introduced for enamel biomimetic remineralization that utilize a biomimetic analogue to interact and absorb bioavailable calcium and phosphate ions and induce crystal nucleation on demineralized enamel. Amelogenin is the most predominant enamel matrix protein that is involved in enamel biomineralization. It plays a major role in developing the enamel's hierarchical microstructure. Therefore, this study was conducted to evaluate the ability of an amelogenin-inspired peptide to promote the remineralization potential of fluoride and a supersaturated calcium phosphate solution in treating artificially induced enamel carious lesions under pH-cycling regimen. METHODS: Fifty enamel slices were prepared with a window (4*4 mm2 ) on the surface. Five samples were set as control healthy enamel and 45 samples were subjected to demineralization for 3 days. Another 5 samples were set as control demineralized enamel and 40 enamel samples were assigned into 8 experimental groups (n=5) (P/I, P/II, P/III, P/AS, NP/I, NP/II, NP/III and NP/AS) according to peptide treatment (peptide P or non-peptide NP) and remineralizing solution used (I; calcium phosphate solution, II; calcium phosphate fluoride solution, III; fluoride solution and AS; artificial saliva). Samples were then subjected to demineralization/remineralization cycles for 9 days. Samples in all experimental groups were evaluated using Raman spectroscopy for mineral content recovery percentage, microhardness and nanoindentation as healthy, demineralized enamel and after pH-cycling. Data were statistically analysed using two-way repeated measures Anova followed by Bonferroni-corrected post hoc test for pairwise multiple comparisons between groups. Statistical significance was set at p= 0.05. Additionally, XRD, FESEM and EDXS were used for crystal orientation, surface morphology and elemental analysis after pH-cycling. RESULTS: Nanocrystals clumped in a directional manner were detected in peptide-treated groups. P/II showed the highest significant mean values in mineral content recovery (63.31%), microhardness (268.81±6.52 VHN), elastic modulus (88.74±2.71 GPa), nanohardness (3.08±0.59 GPa) and the best crystal orientation with I002/I300 (1.87±0.08). CONCLUSION: Despite pH changes, the tested peptide was capable of remineralizing enamel with ordered crystals. Moreover, the supplementary use of calcium phosphate fluoride solution with peptide granted an enhancement in enamel mechanical properties after remineralization.

Remineralisation of enamel and dentine with stabilised stannous fluoride dentifrices in a randomised cross-over in situ trial.

OBJECTIVES: To compare the remineralisation efficacy and ion bioavailability of two novel SnF2-containing dentifrices in a blinded, cross-over, randomised in situ clinical study. METHODS: Six participants wore removal palatal appliances holding human enamel and dentine blocks with subsurface lesions. Appliances were worn for two treatment periods of 14 consecutive days each, with a one-week washout period in-between. Participants were randomly allocated to rinse with a 1:5 diluted coded slurry of one of two dentifrices containing either 5 % casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) +1100 ppm F as SnF2 [MIPOP], or 1100 ppm F as SnF2 [CT], for 1 min, four times a day. Saliva was collected post-treatment and analysed for tin, calcium, inorganic phosphate and fluoride ions using atomic absorption spectrophotometry and ion chromatography. Enamel and dentine lesions were analysed for percent remineralisation (%R) using transverse microradiography and percent surface microhardness recovery (%SMHR). RESULTS: MIPOP released significantly higher F (3.00 ± 0.27 mM), Ca (15.23 ± 3.23 mM) and Sn (1.18 ± 0.13 mM) into saliva whereas CT released 2.89 ± 0.32 mM F and only 0.84 ± 0.11 mM Ca and 0.28 ± 0.10 mM Sn. MIPOP produced significantly higher %R than CT: 25.6 ± 1.5 % compared to 15.2 ± 0.7 % in enamel, and 33.6 ± 3.1 % compared to 20.6 ± 1.1 % in dentine. Additionally, MIPOP produced significantly higher %SMHR (18.2 ± 7.9 %) compared to CT (4.1 ± 0.6 %). CONCLUSIONS: Both dentifrices promoted remineralisation, but the MIPOP dentifrice with added CPP-ACP and the ion-stabilising effects of CPP released higher amounts of bioavailable tin and produced significantly higher remineralisation and surface microhardness recovery. CLINICAL SIGNIFICANCE: Modern dentifrices contain SnF2 for a range of oral health benefits. Challenges associated with stability of these formulations can affect ion bioavailability, reducing efficacy. Two dentifrices with SnF2 promoted remineralisation in situ, however the dentifrice with the added saliva biomimetic CPP-ACP was superior and therefore may produce greater health benefits.

Xylitol associated or not with fluoride: Is the action the same on de- and remineralization?

OBJECTIVES: This study evaluated the effect of xylitol combined or not with fluoride (F) on reduction of demineralization and increase of remineralization of shallow and deep artificial enamel lesions. METHODS: Bovine enamel samples were allocated to the following solutions groups: no xylitol (negative control), 5% xylitol, 10% xylitol, 20% xylitol, 500 ppm F (as NaF), 5% xylitol+F, 10% xylitol+F or 20% xylitol+F (n = 12-15). For the demin study, a pH-cycling model (demineralization-6 h, pH 4.7/remineralization 18 h, pH 7.0) was employed for 7 days. Treatments were applied 2 × 1 min. In the remin study, specimens were pre-demineralized for 2, 5 or 10 days. Afterwards, a pH-cycling protocol was conducted (2 h demineralizing and 22 h remineralizing solution/day for 8 days) and the same treatments were done. The response variables were percentage surface hardness loss (%SHL) and transverse microradiography. Data were analyzed by RM ANOVA/Tukey or Kruskal-Wallis/Dunn (p < 0.05) RESULTS: F and Xylitol combined with F reduced the %SHL (23-30%) compared to the negative control (61.5%). The integrated mineral loss and the lesion depth were not reduced by any treatment. Surface hardness recovery was seen only for shallow lesions in case of 20% xylitol+F compared to negative control. No lesion depth recovery, but significant mineral recovery was seen for F (2-days and 10-days lesion). CONCLUSIONS: All concentrations of xylitol+F reduced enamel surface demineralization, while only 20% xylitol+F improved surface remineralization of shallow lesions in vitro. CLINICAL SIGNIFICANCE: Our results suggest that while F or any concentration of xylitol + F reduces surface demineralization, only 20% xylitol+F improves surface remineralization of shallow lesions in vitro. Therefore, xylitol may be added into oral products, combined to F, to control dental caries.

Combined Casein Phosphopeptide-Amorphous Calcium Phosphate and Fluoride Is Not Superior to Fluoride Alone in Early Carious Lesions: A Meta-Analysis.

There is a growing need for effective methods in the management of early stage carious lesions. Therefore, the aim of this study was to evaluate the effect of combined casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and fluoride on white spot lesions (WSLs) compared to fluoride-only interventions. This meta-analysis was performed according to PRISMA guidelines and registered in PROSPERO (CRD42021286245). The Medline, Embase, and Cochrane Central databases were searched until October 17, 2022. Eligible studies were randomized controlled trials. Outcome variables included laser fluorescence (LF), quantitative light-induced fluorescence (QLF), and lesion area scores. The random-effects model was used for analysis, and results were given as standardized mean difference (SMD) and mean difference (MD) with a 95% confidence interval. Risk of bias was assessed using the RoB 2 tool, and the level of evidence with GRADE. Our systematic search yielded 973 records after duplicate removal, 21 studies were included for qualitative synthesis, and 15 studies were eligible for quantitative analysis. No significant difference was found between CPP-ACP and fluoride versus fluoride alone in LF at 1, 3, and 6 months of use: SMD -0.30 (-0.64; 0.04); SMD -0.47 (-1.02; 0.07); SMD -0.49 (-1.13; 0.15), respectively. For QLF, the analysis did not demonstrate significant differences between these two kinds of treatment at 1 and 6 months of use: MD 0.21 (-0.30;0.71); MD 0.60 (-1.70;2.90), but at 3 months, higher QLF values were found in the fluoride-only group compared to the CPP-ACP and fluoride combination was shown regarding the WSLs: MD 0.58 (0.25;0.91). On the contrary, data showed a small but statistically significant decrease in the lesion area in favor of the CPP-ACP plus fluoride versus fluoride alone at 6 months MD -0.38 (-0.72; -0.04). None of these observed changes indicated substantial clinical relevance. The combination of CPP-ACP and fluoride did not overcome the effect of fluoride given alone. Our data suggest that fluoride itself is effective in improving WSLs. However, the certainty of evidence was very low. These results indicate that further studies and future development of more effective products than CPP-ACP are needed in addition to fluoride to achieve robust amelioration of WSLs.

The effect of silver nanoparticles in addition to sodium fluoride on remineralization of artificial root dentin caries.

BACKGROUND: Silver nanoparticle was developed to overcome the drawback of silver diamine fluoride. However, evidence is limited, especially in root caries. The aim of this study was to evaluate the remineralization effect of silver nanoparticles on root caries. MATERIALS AND METHODS: Fifty-five root human dentin slices size 5 × 5 mm2 from patients aged over 60 years old were immersed in demineralized solution to create artificial caries. Specimens were allocated into five groups according to the remineralizing agents: silver diamine fluoride (SDF), silver nanoparticles solution (AgNPs), silver nanoparticle solution followed by sodium fluoride varnish (AgNPs+NaF), sodium fluoride varnish (NaF), and tap water. After 8 days of pH-cycling challenge, the microhardness test, lesion depth evaluation, dentin surface morphology, and elemental analysis were performed. Data was analysed using F-test One-way ANOVA followed by Tukey's post hoc test and paired T-test. RESULTS: All test groups demonstrated a significantly higher microhardness value and lower lesion depth compared with the control group. AgNPs+NaF and NaF-treated groups showed lower efficacy than SDF. Crystal precipitation was presented in all groups composed of silver. CONCLUSION: Addition of fluoride varnish did not benefit for silver nanoparticles in preventing further demineralization. SDF provides the highest effectiveness in elderly root carious dentin.

Silver Compounds for Caries Management.

Silver metal and compounds have antibacterial properties, although their action's mechanisms are not fully understood. Scientists generally consider that silver disrupts the bacterial cell wall. It causes a structural change in the bacterial cell membrane and cytoplasm. It also stops deoxyribonucleic acid replication, resulting in inactivating enzymatic activity and cell death. The antimicrobial effect of silver-containing compounds relies on the release of bioactive silver ions. Hence, silver metal and compounds have been used in medicine to prevent infection for hundreds of years. Silver metal and compounds are also used as antibacterial agents in dentistry. Studies have shown that silver compounds are effective in the management of dental caries. Fluoride-containing silver compounds have been found in experiments to be beneficial at remineralising dental cavities. Silver diamine fluoride (SDF) can assist in preventing and arresting tooth cavities. The World Health Organization included SDF in its Model List of Essential Medicine for both adults and children in 2021. Clinicians also use SDF to manage dentine hypersensitivity as well as to inhibit growth of periodontal pathogens. However, traditional silver compounds cause tooth discolouration because of the silver-staining effect. These side effects of their applications depend on the amount applied and the frequency of application. Researchers are developing nanosilver fluoride and silver nanoparticles to overcome the staining. This review gives an overview of the antibacterial mechanism of silver compounds, namely silver nitrate, silver fluoride, SDF, silver nanoparticles, and nano silver fluoride for caries management. The outlook for the future development of silver compounds will be discussed.

In vitro caries-preventive effect of a mineralization-promoting peptide combined with fluoride gel on sound primary teeth.

BACKGROUND: Mineralization-promoting peptide-3 (MPP3) is a new biomimetic remineralization agent. AIM: To assess the remineralization efficiency of MPP3, either alone or in combination with fluoride gel. DESIGN: The samples were divided into four groups: control, 1.23% fluoride gel, 10% MPP3 gel, and 1.23% fluoride gel + 10% MPP3. Following the application of remineralization agents (4 min), the samples remained in a pH-cycling model (37°C, 4 weeks). Microhardness, microcomputed tomography (micro-CT), polarized light microscopy (PLM), and field emission scanning electron microscopy (FE-SEM) analysis were conducted. RM-ANOVA, one-way ANOVA, and intraclass correlation coefficient (ICC) were used for statistical analysis, and a significance level of p < .05 was employed. RESULTS: Mineralization-promoting peptide 3 and fluoride gel + MPP3 increased the microhardness of the enamel compared with initial values in each group (p < .05). Mineralization-promoting peptide 3 successfully maintained the mineral density of enamel, although the cariogenic pH-cycling and PLM results indicated that the lesion depth (µm) was significantly lower in the fluoride gel + MPP3 group (27.0336 ± 12.53650) than in the control group (37.3907 ± 12.76002, p < .05). CONCLUSION: The combined use of MPP3 with fluoride gel enhanced the caries-protective and mineralization-promoting effects of fluoride. Mineralization-promoting peptide 3 may be a potential agent that can be employed to improve the physical properties of enamel.

Ultrastructural investigation of the effect of toothpastes containing different remineralizing agents on demineralized enamel.

OBJECTIVE: The present study aimed to evaluate the effect of remineralizing agents on demineralized enamel intended for use as fluoride substitutes or supplements for oral hygiene applications. METHODOLOGY: Enamel samples were obtained from 30 bovine teeth. The enamel blocks were stored in 20 mL of demineralization solution for 72 h. They were then brushed with the following toothpaste for the remineralization protocol: NaF, NaF/SnF2 combination, NovaMin, or nano-hydroxyapatite. SEM/EDX examinations and microhardness measurements of the samples were performed to investigate the remineralization efficacy of the studied toothpaste. One-way analysis of variance (ANOVA) with post hoc Tukey's HSD test was used to analyze the change in microhardness values in different remineralization protocols (p < 0.05). RESULTS: Differences in the mean remineralization (%RP) and hardness recovery (%HR) were determined between the groups (p < 0.05). Groups 1 and 4 showed significant differences in %RP (p < 0.05). In the SEM/EDX examinations, the samples treated with n-HAp showed an accumulation of crystal deposits on the enamel surface, although at a lower density than those treated with NaF and NaF/SnF2 combination. CONCLUSION: The remineralization strategy in toothpaste plays an important role in enamel remineralization. NovaMin-containing toothpaste showed positive effects on the enamel surface with better Ca/P ratio. Toothpastes containing n-HAp triggered less change in the increase of microhardness values compared to other toothpastes. The use of SnF2 in toothpaste in combination with NaF significantly increased the binding of fluoride to demineralized enamel compared to toothpaste containing NaF alone.

Effect of the association of microparticles and nano-sized ß-calcium glycerophosphate in conventional toothpaste on enamel remineralization: In situ study.

OBJECTIVES: This in situ study aimed to assess the remineralizing effect of a fluoride toothpaste supplemented with ß-calcium glycerophosphate in both micro (ß-CaGPm) and nano-sized forms (ß-CaGPn). METHODS: This blind and cross-over study was performed in 4 phases, each spanning 3 days. Twelve volunteers utilized palatal appliances containing four bovine enamel blocks with artificial caries lesions. Volunteers were randomly assigned to the following treatment groups: Placebo (no F-ß-CaGPm-ß-CaGPn); 1100 ppm F alone (1100F); 1100F plus 0.5% micrometric ß-CaGP (1100F-0.5%ß-CaGPm); and 1100F plus 0.25%nano-sized ß-CaGP (1100F-0.25%ß-CaGPn). Participants were instructed to brush their natural teeth with the palatal appliances in the mouth for 1 min (3 times/day), ensuring that the enamel blocks were exposed to the natural toothpaste slurries. Following each phase, evaluations were conducted to determine the percentage of surface hardness recovery (%SHR), integrated recovery of subsurface hardness (ΔIHR), profile subsurface lesion through polarized light microscopy (PLM), as well as fluoride (F), calcium (Ca), and phosphorus (P) concentrations within the enamel. Data were analyzed by ANOVA and Student-Newman-Keuls test (p < 0.001). RESULTS: Treatment with 1100F-0.25%ß-CaGPn resulted in %SHR ∼69 % and ∼40 % higher when compared to 1100F and 1100F-0.5%ß-CaGPm (p < 0.001). The reduction in lesion body (ΔIHR; PLM) was ∼40 % higher with 1100F-0.25%ß-CaGPn (p < 0.001) compared to 1100F. The addition of ß-CaGPm and ß-CaGPn did not influence enamel F concentration (p > 0.001). Treatment with 1100F-0.25%ß-CaGPn led to an increase in the concentration of Ca and P in the enamel (p < 0.001). CONCLUSION: The addition of 0.25%ß-CaGPn into 1100F formulation increased the bioavailability of calcium and phosphate, promoting a higher remineralizing effect. CLINICAL SIGNIFICANCE: Toothpaste containing 1100F-0.25%ß-CaGPn showed a potential of higher remineralization to 1100 ppm F and 1100 ppm F micrometric ß-CaGP could be a strategy for patients at caries activity.

Fluoride varnishes supplemented with nano-sized sodium trimetaphosphate reduce enamel erosive wear in vitro.

OBJECTIVE: To evaluate the effect of fluoride (F) varnishes with sodium trimetaphosphate (TMP) on erosive tooth wear (ETW) in vitro. METHODS: Enamel blocks (n = 100) were divided into 5 experimental groups (n = 20/group): Placebo (Pla - without F/TMP); 5 % NaF (NaF); 5 % NaF + 5 % micrometric TMP (NaF+5 %MICRO); 5 % NaF + 2.5 % nano-sized TMP (NaF+2.5 %NANO), and 5 % NaF + 5 % nano-sized TMP (NaF+5 %NANO). Blocks received a single varnish application (6 h contact), and were submitted to 4 daily erosive challenges (ERO, 0.05 M citric acid, pH 3.2, 90 s, under agitation), for 5 days. After ERO, half of the blocks (n = 10/group) were subjected to brushing abrasion (ERO+ABR). Profilometry, surface hardness (SH), and cross-sectional hardness (ΔKHN) were determined. The data were submitted to 2-way ANOVA and Fisher's LSD test (p < 0.05). RESULTS: Enamel wear was significantly lower for ERO compared with ERO+ABR for all varnishes tested (p < 0.001), following the pattern NaF+5 %NANO < NaF+5 %MICRO < NaF < NaF+2.5 %NANO < Pla (both for ERO and ERO+ABR). The highest SH loss was observed for Pla and the lowest for NaF (ERO) and NaF+2.5 %NANO (ERO+ABR), without significant differences among NaF+2.5 %NANO, NaF, and NaF+5 %MICRO. The highest ΔKHN values were observed for NaF+5 %MICRO and NaF+5 %NANO at 5-30 µm, with less marked differences among the groups at 30-70 µm (ERO and ERO+ABR). CONCLUSIONS: The addition of TMP to F varnishes significantly improves protection against ETW in vitro. The use of 5 % nano-sized TMP further enhances such effects. CLINICAL SIGNIFICANCE: F varnishes containing TMP can reduce enamel loss caused by ERO or ERO+ABR.

Enamel remineralization potential and antimicrobial effect of a fluoride varnish containing calcium strontium silicate.

OBJECTIVES: To investigate enamel remineralization and antimicrobial effect of sodium fluoride (NaF) varnish containing calcium strontium silicate (CSR). METHODS: CSR was synthesized by sol-gel process and incorporated in 5 % NaF varnish at three different concentrations (1 %, 2 %, and 4 % w/v). The treatment/control groups were: 1 % CSR+NaF, 2 % CSR+NaF, 4 % CSR+NaF, NaF, and no treatment. Strontium and fluoride release from the varnishes was evaluated. Sound enamel specimens (n = 6) were demineralized, varnish-treated, and subjected to remineralization cycle. Mineral density of enamel specimens was evaluated using micro-CT. Antimicrobial effect of the varnishes on Streptococcus mutans and Lactobacillus acidophilus biofilms was assessed using confocal laser scanning microscopy. The HGF-1 cytotoxicity of the varnishes was examined using CCK-8 assay. RESULTS: Both 2 % and 4 % CSR+NaF varnishes showed significantly higher F release and remineralization potential than NaF varnish (p < 0.05). Dead bacterial proportion of 4 % CSR+NaF varnish was significantly higher than NaF varnish (p < 0.05). The CFUs values of both S. mutans and L. acidophilus were significantly lower in 4 % CSR+NaF group than NaF group (p < 0.05). No significant difference in cell viability was observed among the groups (p > 0.05). CONCLUSIONS: Incorporation of 4 % CSR in a NaF varnish significantly enhanced its enamel remineralization and antimicrobial potential with no cytotoxic effect. CLINICAL SIGNIFICANCE: Dental caries is a major public health problem globally. The study highlights the great potential of CSR-doped NaF varnish as a novel anti-caries agent with synergistic remineralizing and antimicrobial properties to combat early enamel caries lesions in the general population.

Immediate and Sustained Root Caries Prevention of Fluoride Varnish Combined with Toothpastes.

The aim of this study was to determine the immediate and sustained effect of a fluoride varnish and its combinations with toothpastes in preventing root caries development using a salivary microcosm in vitro model. Human root dentin specimens (n = 150) were randomly divided into 5 experimental protocols (n = 30): (1) Fluoride Varnish (V); (2) V followed by Paste One (V + PO); (3) V followed by Paste Plus (V + PP); (4) V followed by PO and PP (V + PO + PP); and (5) No treatment (control). One varnish layer was applied on the specimens (except for the control group) and kept for 18 h. Then, the varnish was removed and toothpaste treatments were initiated according to experimental groups. For the short-term incubation model (n = 15), the specimens were also immediately subjected to 7-day cariogenic challenge. For that, human saliva was used as bacterial inoculum and McBain artificial saliva containing 2% sucrose as growth medium. The other half of the specimens (n = 15) were used to study the varnish's sustained effect by long-term incubation (8 weeks) before cariogenic challenge. The protocols' anti-caries properties were evaluated by dentin porosity (rhodamine intensity; RI) and mineral density, while their anti-biofilm effects were evaluated using biofilm's biomass and viability assays. For short- and long-term incubation models, all experimental regimens resulted in statistically significant decreases (p < 0.05) in the RI (up to 180 µm and 120 µm, respectively) as well as higher mineral density compared to No treatment (p < 0.001). V + PO + PP and/or V + PO resulted in statistically lower RI compared to V for some depths (p < 0.05) in both models. There were changes in RI and mineral density within groups over time. All experimental treatments exhibited anti-biofilm effects. All prevention protocols exhibited immediate and sustained anti-caries effect against root caries development. The combination of a fluoride varnish with PO resulted in superior additional anti-caries effects.

Anti-erosion effect of an experimental varnish on eroded dentin.

This in vitro study evaluated the effect of an experimental varnish containing 20% nano-hydroxyapatite (nHAP) associated with 5% stannous chloride (SnCl2) against erosive-abrasive wear on bovine dentin. Samples of bovine cervical dentin were pre-eroded (0.3% citric acid, pH 2.6 for 10 minutes) and randomized into 4 groups (n=10): Control group - experimental varnish without active ingredient (CG); experimental varnish containing 20% nHAP (nHG); experimental varnish containing 5% SnCl2 (24.800 ppm Sn2+) (SnG); experimental varnish containing 20% nHAP associated with 5% SnCl2 (18.300 ppm Sn2+) (nHSnG). After applying the materials, the erosive-abrasive challenges were performed for five days. Erosive dentin loss and analysis of the pattern of dentinal obliteration were performed by 3D confocal laser microscopy. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The SnG and nHSnG experimental groups presented more effectiveness in preventing erosive wear when compared to the other groups (p<0.05). There was no statistically significant difference between the SnG and nHSnG groups (p = 0.731) in tooth structure dentin loss. Regarding the amount of open dentinal tubules, the highest amount of obstructed dentinal tubules was demonstrated in SnG and nHSnG (p < 0.05) when compared to the others. Between SnG and nHSnG there was no significant difference (p = 0.952) in the amount of closed dentinal tubules in the dentin. Experimental varnishes containing 5% SnCl2 associated or not with 20% nHAP showed to be a promising strategy in preventing erosive-abrasive wear of dentin. In addition, nHSnG was able to obliterate dentinal tubules.