Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

A new method of adhesive system application improves the bond strength between fiber post and root dentin.

This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

Can a dentin bonding agent prevent color change in regenerative endodontic procedures? An in vitro evaluation.

This in vitro study aimed to determine the efficacy of dentin bonding agents in preventing color changes following Regenerative Endodontic Procedures. One hundred twenty bovine incisors were endodontically prepared and randomly assigned to a two main factors design: application of a dentin bonding agent (Scotchbond Adper, 3M ESPE, St Paul, MN, USA) in the pulp chamber (Group 1, n=60) versus no bonding intervention (Group 2, n=60), and five levels of intracanal medication (n=12/subgroup): Triple antibiotic paste (TAP), double antibiotic paste (DAB), calcium hydroxide (CH), modified triple antibiotic paste (TAPM), and Control (CTL). Color changes were measured over 28 days at multiple time points (1, 3, 7, 14, 21, and 28 days) using the CIEDE2000 formula to calculate the color difference (ΔE00) from baseline (T0). The ΔE00 quantifies the perceptible color difference between the initial and final tooth color, with lower values indicating less discoloration. The results were analyzed using repeated measures ANOVA-2 and post-hoc Holm-Sidak tests. The TAP subgroups, both with and without the bonding agent, exhibited the highest color variation. However, a pulp chamber seal with a bonding agent showed a protective effect against discoloration compared to no seal, even though complete prevention was not achieved. All groups demonstrated ΔE00 values beyond acceptable interpretation thresholds for clinical application, primarily driven by a reduction in lightness (L*) and a decrease in redness (a* value, shifting towards green). In conclusion, while the pulp chamber seal with a bonding agent mitigated TAP-induced discoloration, it did not eliminate it.

The Influence of Erbium Laser Pretreatment on Dentin Shear Bond Strength and Bond Failure Modes: A Systematic Review and Network Meta-Analysis.

PURPOSE: To systematically review in-vitro studies that evaluated the influence of erbium laser pretreatment on dentin shear bond strength (SBS) and bond failure modes. MATERIALS AND METHODS: Electronic databases (PubMed, Cochrane Central, Embase, and Web of Science) were searched. Only in-vitro studies involving erbium laser irradiation of the dentin surface and SBS testing of the bonded resin block were included. The three common modes of bond failure (1. adhesive, 2. cohesive, and 3. mixed) were observed and analyzed. The network meta-analysis (NMA) was performed by Stata 15.0 software, the risk of bias was evaluated, and the certainty of the evidence was assessed by the Confidence in Network Meta-analysis (CINeMA). RESULTS: Forty studies with nine pretreatments (1. blank group: BL; 2. phosphoric acid etch-and-rinse: ER; 3. self-etch adhesive: SE; 4. Er:YAG laser: EL; 5. Er,Cr:YSGG laser: ECL; 6. ER+EL; 7. ER+ECL; 8. SE+EL; 9. SE+ECL) were included in this analysis. The NMA of SBS showed that ER+EL [SMD = 0.32, 95% CI (0.11, 0.98)] had the highest SBS next to ER, especially when using one of the 3M ESPE adhesives, followed by EL, ECL, SE and SE+EL. The Ivoclar Vivadent adhesives significantly increased the SBS of the ECL [SMD = 0.37, 95% CI (0.16,0.90)] and was higher than ER+EL [SMD = 0.25,95% CI (0.07,0.85)]. Finally, the surface under the cumulative ranking curve (SUCRA) value indicated that ER+EL (SUCRA = 71.0%) and EL (SUCRA = 62.9%) were the best treatments for enhancing dentin SBS besides ER. ER+EL (SUCRA = 85.3%), ER (SUCRA = 83.7%) and ER (SUCRA = 84.3%) had the highest probability of occurring in adhesive, cohesive and mixed failure modes, respectively. CONCLUSION: Er:YAG and Er,Cr:YSGG lasers improved dentin SBS compared to the blank group, especially when the acid etch-and-rinse pretreatment was combined with Er:YAG laser. Shear bond strength and failure mode do not appear to be directly related.

Effect of dentin surface conditions and curing mode of resin cement on the dentin bond strength.

This study investigates the effects of dentin's drying time, roughness, and curing modes of resin cement on bond strength. Forty human teeth were divided into eight groups based on three experimental factors: dentin's roughness by 240-or 600-grit SiC paper (coarse or fine), dentin wetness with air-drying time (5-s or 10-s), and Single Bond Universal adhesive's curing mode by co-curing with RelyX Ultimate cement or light-curing separately (co-curing or light-curing). The micro-tensile bond strength of fifteen resin-dentin stikcs per groups was measured. Failure mode and adhesive layers were observed using stereoscopic and confocal laser scanning microscopy, respectively. The curing mode of the adhesive layer affected the bond strength of the dentin-resin cement (p<0.05). In particular, the light-curing mode exhibited a significantly higher bond strength than the co-curing one (p<0.05). The bond strength between the resin cement and dentin was improved in the 5-s drying groups than in the 10-s drying groups.

Effects of dentin bonding agents and silanization on bond strength between 3D printed resin and composite resin.

This study aimed to evaluate the effects of dentin bonding agents and silanization on the bond strength between 3D printed resin and composite resin and compare it with a conventional composite resin. 3D printed resin cylinders (PCB) and composite resin substrates (Z250) were prepared and divided into eight subgroups based on the bonding agents used (n=12). The shear bond strength was measured using a universal testing machine, and the failure modes were evaluated. The bond strength was found to vary significantly among the bonding agents and substrate types. Silane application did not significantly improve the bond strength. Among the bonding agents, the universal adhesives exhibited the highest bond strengths for both substrates. Compared to PCB, Z250 demonstrated stronger bonds and exhibited more cohesive failures. Further research is needed to optimize the surface treatments and resin formulations for enhanced bond strength and durability between 3D printed and composite resins.

Equivalence study of the resin-dentine interface of internal tunnel restorations when using an enamel infiltrant resin with ethanol-wet dentine bonding.

This preregistered ex vivo investigation examined the dentinal hybrid layer formation of a resinous infiltrant (Icon), with reference to both thickness (HLT) and homogeneity when combined with modified tunnel preparation (occlusal cavity only) and internal/external caries infiltration. The adhesives Syntac and Scotchbond MP were used as controls (Groups 1 and 3) or in combination with Icon (Groups 2 and 4). A split-tooth design using healthy third molars from 20 donors resulted in 20 prepared dentine cavities per experimental group. The cavity surfaces (n = 80) were etched (37% H3PO4), rinsed, and air-dried. Rewetting with ethanol was followed by application of the respective primers. After labeling with fluorescent dyes, either Syntac Adhesive/Heliobond or Scotchbond MP Adhesive was used alone or supplemented with Icon. HLT, as evaluated by scanning electron microscopy, did not significantly differ (P > 0.05), and confocal laser scanning microscopy revealed homogeneously mixed/polymerized resin-dentine interdiffusion zones in all groups. Icon can be successfully integrated into an ethanol-wet dentine bonding strategy, and will result in compact and homogeneous hybrid layers of comparable thickness considered equivalent to the non-Icon controls, thus allowing for preservation of the tooth's marginal ridge and interdental space in the case of internal/external infiltration of proximal caries.

Evaluation of Microbiological Susceptibility and Long-term Adhesive Properties to Dentin of Primers with Terminalia catappa Linn.

PURPOSE: To investigate the antibacterial effects of Terminalia catappa Linn (TCL) leaf extracts at different concentrations and the effects of these extracts used as primers on the long-term adhesive properties of two universal adhesives. MATERIALS AND METHODS: After extract preparation, the antimicrobial and antibacterial activities of TCL against Streptococcus mutans (UA 159) were assessed in microdilution assays to provide the minimal inhibitory concentration (MIC) and minimal bactericidal concentration (MBC). Additionally, to provide quantitative data on the ability of TCL extract to reduce cell viability, colony forming units (CFU) were counted. To examine adhesive properties, 288 human molars were randomly assigned to 32 experimental conditions (n = 9) according to the following variables: (1) treatment agent: negative control (untreated surface), and primers at concentrations of 1xMIC, 5xMIC, and 10xMIC; (2) adhesives: Scotchbond Universal (SBU) and Futurabond Universal (FBU); (3) adhesive strategy: etch-and-rinse (ER) or self-etch (SE); and (4) storage time: 24 h or after 2 years. Primers were applied for 60 s, upon which the teeth were incrementally restored and sectioned into adhesive-dentin bonded sticks. These were tested for microtensile bond strength (µTBS) and nanoleakage (NL) after 24-h and 2-year water storage, as well as in-situ degree of conversion (DC) at 24 h. The chemical profile of the hybrid layer was determined via micro-Raman spectroscopy. Biofilm assay data were analyzed using the Kruskal-Wallis test; the pH of culture media and the chemical profile were analyzed by one-way ANOVA. The adhesive properties (µTBS, NL, DC) were evaluated using a four-way ANOVA and Tukey's test. Significance was set at 5%. RESULTS: Similar values of MIC and MBC were observed (2 mg/ml), showing bactericidal potential. CFU analysis demonstrated that concentrations of 5xMIC and 10xMIC significantly inhibited biofilm formation (p < 0.001). The application of the TCL primer at all concentrations significantly increased the immediate µTBS and DC, and decreased the immediate NL values when compared to the control group (p < 0.05), regardless of the adhesive and adhesive strategies. Despite an increase in the NL values for all groups after 2 years (p > 0.05), in groups where the TCL primer was applied, the µTBS remained constant after 2 years for both adhesives, while a decrease in the µTBS was observed in the control groups (p < 0.05). Usually, 10xMIC showed better results than 1xMIC and 5xMIC (p < 0.05). The application of TCL promoted cross-linking; cross-linking rates increased proportionally to the concentration of TCL (p < 0.05). CONCLUSION: Primers containing TCL promoted bactericidal and bacteriostatic action, as well as cross-linking with dentin, while maintaining the adhesive properties of the adhesive-dentin interface after 2 years of water storage.

Assessment of physical properties of bioactive glass-modified universal multimode adhesive and its bonding potential to artificially induced caries affected dentin.

BACKGROUND: To evaluate the physical properties of bioactive glass-modified universal multimode adhesive and its micro-tensile bond strength (µTBS) to artificially induced caries-affected dentin. METHODS: All bond universal adhesive was used in the study. Specimens were divided into 2 main groups: control unmodified adhesive and 5 wt% BAG modified adhesive. The degree of conversion, pH, bioactivity, and viscosity of the adhesives were tested with n = 5 for each test. Micro-tensile bond strength evaluation was done in etch & rinse (ER) and selective-etch (SE) modes, where 24 human molar teeth were used (n = 3), 12 teeth for immediate bond strength, and the other 12 were tested after 6 months of storage in simulated body fluid (SBF). RESULTS: No significant difference was found between the control and the 5wt% BAG groups regarding the degree of conversion (61.01 ± 0.43 and 60.44 ± 0.61 respectively) and the viscosity (109.77 ± 22.3 and 124.3 ± 9.92 respectively). The control group revealed significantly lower pH values than the 5wt% BAG group (3.16 ± 0.5 and 4.26 ± 0.09 respectively). Immediate bond strength results revealed that the 5wt% BAG in the ER mode had the highest bond strength followed by the control group in the ER mode (44.16 ± 7.53 and 44.00 ± 7.96 respectively). SE groups showed that the immediate strength of the 5wt% BAG group was higher than the control group (42.09 ± 6.02 and 39.29 ± 6.64 respectively). After 6 months of storage, bond strength results revealed a decrease in bond strength values for the control groups but not for the 5wt% BAG in both application modes. CONCLUSIONS: The incorporation of BAG (5wt%) improved the universal adhesive micro-tensile bond strength and bond durability for both adhesive application modes without affecting its degree of conversion or viscosity.

Use of marine occurrent extracts to enhance the stability of dentin extracellular matrix.

Chitosan (CS) and phloroglucinol (PhG), two extracts abundantly found in marine life, were investigated for their ability to biomodify demineralized dentin by enhancing collagen crosslinks and improving dentin extracellular matrix (ECM) mechanical and biochemical stability. Dentin obtained from non-carious extracted human molars were demineralized with phosphoric acid. Baseline Fourier-transform infrared (FTIR) spectra, apparent flexural elastic modulus (AE) and dry mass (DM) of each specimen were independently acquired. Specimens were randomly incubated for 5 min into either ultrapure water (no-treatment), 1% glutaraldehyde (GA), 1% CS or 1% PhG. Water and GA were used, respectively, as a negative and positive control for collagen crosslinks. Specimens' post-treatment FTIR spectra, AE, and DM were obtained and compared with correspondent baseline measurements. Additionally, the host-derived proteolytic activity of dentin ECM was assessed using hydroxyproline assay (HYP) and spectrofluorometric analysis of a fluorescent-quenched substrate specific for matrix metalloproteinases (MMPs). Finally, the bond strength of an etch-and-rinse adhesive was evaluated after application of marine compounds as non-rinsing dentin primers. Dentin specimens FTIR spectral profile changed remarkably, and their AE increased significantly after treatment with marine compounds. DM variation, HYP assay and fluorogenic substrate analysis concurrently indicated the biodegradation of CS- and PhG-treated specimens was significantly lesser in comparison with untreated specimens. CS and PhG treatments enhanced biomechanical/biochemical stability of demineralized dentin. These novel results show that PhG is a primer with the capacity to biomodify demineralized dentin, hence rendering it less susceptible to biodegradation by host-proteases.

Micro-shear Bond Strength of an Alternative Self-etch Application of "No Wait" Universal Adhesive to Caries-affected and Sound Dentin in Permanent and Primary Teeth.

OBJECTIVE: This study aimed to compare the micro-shear bond strength (µSBS) of caries-affected dentin (CAD) and sound dentin (SoD) in primary and permanent teeth using an alternative self-etch application of "no wait" universal adhesive. METHODS AND MATERIALS: Flat midcoronal dentin surfaces from 72 permanent third molars and 72 second primary molars were distributed randomly into 12 groups according to the substrate SoD and artificially-created CAD (pH cycling for 14 days) and the adhesive system (GLUMA Bond5, a two-step etch & rinse adhesive, GLUMA Bond, a one-step self-etch adhesive, and Tokuyama Universal Bond, a one-step self-etch adhesive) (n=12). Bonded dentin resin discs were put through micro-shear bond strength testing after 10,000 thermocycles. The results were evaluated using two-way ANOVA and the Bonferroni test with a significance level of α = 0.05. RESULTS: When compared to SoD, the etch & rinse system's test results on artificially created CAD showed a statistically significant poorer bonding performance in both permanent and primary teeth in all groups (p<0.05). While the bond strengths of permanent teeth using total-etch adhesive on sound dentin were statistically significantly higher than those using Tokuyama Universal Bond adhesive (p<0.05), there was no significant difference in sound dentin in primary teeth (p>0.05). CONCLUSIONS: The etch & rinse system performed the poorest of all adhesive systems on CAD. The Tokuyama Universal Bond's adhesive strength was similar in SoD and CAD on primary teeth. The use of Tokuyama Universal Adhesives can speed up restorative treatment in pediatric dentistry.

A scoping review of the influence of clinical contaminants on bond strength in direct adhesive restorative procedures.

OBJECTIVE: Clinical contamination during direct adhesive restorative procedures can affect various adhesive interfaces differently and contribute to bulk failure of the restorations. This review aims to summarise the current knowledge on the influence of a variety of clinical contaminants on the bond strength at various adhesive interfaces during adhesive restorative procedures and identify gaps in the literature for future research. DATA AND SOURCES: An electronic database search was performed in PubMed and EMBASE to identify articles that investigated the influence of contaminants on direct restorative bonding procedures. A data-charting form was developed by two researchers to capture the key characteristics of each eligible study. STUDY SELECTION: The initial search yielded 1,428 articles. Fifty-seven articles published between 1 Jan 2007 and 25 Oct 2023 were included in the final review. Thirty-three of the articles examined the influence of saliva contamination, twelve articles examined the influence of blood contamination, and twenty-five articles examined the influence of other contaminants. CONCLUSION: Saliva contamination exerted less influence on the decrease in bond strength when self-etch systems were used, compared to when etch-and-rinse systems were used. Blood contamination adversely affected the bond strength at the interface between resin composite and dentine, and resin composite and resin-modified glass ionomer cement. Treating contaminated surfaces with water spray for 10-30 s followed by air drying could be effective in recovering bond strength following saliva and blood contamination. CLINICAL SIGNIFICANCE: This scoping review provides a valuable overview of the range of potential clinical contaminants that can influence the bond strength between different interfaces in direct adhesive restorative procedures. Additionally, it identifies potential decontamination protocols that can be followed to restore and enhance bond strength.

Effect of Salvadora persica on resin-dentin bond stability.

BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Longitudinal bond strength of a universal adhesive and chemical dentin characterization under different acid etching protocols.

OBJECTIVE: This study aimed to analyze the longitudinal bond strength of a universal adhesive and chemically characterize the dentin substrate under different acid etching protocols. METHODOLOGY: Dentin samples were etched with polyacrylic acid 25% (PAA) for 10 seconds (n=3) and phosphoric acid 32% (PA) for 15 seconds (n=3) and analyzed by Fourier transform infrared spectroscopy - attenuated total reflectance (FTIR-ATR) before and after treatment. For collagen degradation, samples (n=12) were divided into 3 groups: PAA, PA, and Deionized water (control), and analyzed by the quantity of solubilized type I collagen C-terminal cross-linked telopeptides and solubilized C-terminal peptide in relation to total protein concentration (ICTPtp and CTXtp) and by their ultimate tensile strength (UTS). For the adhesive interface analysis, dentin samples (n=72) were divided into 3 groups: PAA, PA, and Self-etch (SE), and subdivided into 2 groups: 24 h (baseline) and 1 year. The following tests were performed: microtensile bond strength (µTBS) (n=48), scanning electron microscopy (SEM) (n=12), and nanoleakage (n=12). RESULTS: The FTIR of PAA showed lower reduction of the peaks in the phosphate group when compared to PA. For ICTPtp, PA showed a significantly higher value. For CTXtp, PA and PAA groups failed to statically differ from each other. UTS was significantly lower for PA. For µTBS, storage time significantly affected bond strength. The results were unaffected by the etching protocol. For SEM, after 1 year, PA had little evidence of degradation in the upper third of the adhesive interface in comparison to the other groups. Nanoleakage showed no considerable silver impregnation after 1 year in the SE group. CONCLUSION: The use of PAA prior to a universal adhesive (when compared to PA) represents a less aggressive type of etching to dentin. However, self-etching still seems to be the best option for universal adhesive systems that have functional monomers in their composition.

Influence of airborne particle abrasion on dentin bonding effectiveness of a 2-step universal adhesive.

OBJECTIVE: To determine the effect of airborne particle abrasion (APA) on micro-tensile bond strength (µTBS) to dentin using different air-abrasion/polishing powders. METHODS: The bonding effectiveness of G2 Bond Universal (G2B), used in etch-and-rinse (E&R) and self-etch mode (SE), was tested on bur-cut dentin and dentin air abraded/polished using six different powders (aluminum oxide 29 µm (AO29) and 53 µm (AO53), aluminum trihydroxide (AT), sodium bicarbonate (SB), sodium bicarbonate soft (SBsoft) and bioactive glass (BG); Velopex). Adhesive-composite resin specimens were immersed in distilled water at 37 °C for one week and cut into microspecimens. Half of the specimens were subjected to 50,000 thermocycles (aged). Immediate and aged µTBS to dentin were measured. Statistical analysis was performed using linear mixed-effects (LME) modeling (p < 0.05). RESULTS: Comparing the aged bond strengths to air-abraded/polished dentin with bur-cut dentin, pretreatment with SB and SBsoft in combination with G2B used in E&R mode, and BG air polishing in combination with both application modes (E&R, SE), resulted in a significantly higher bond strength. Dentin bond strength was only significantly lower when air abraded with AO29 and using G2B in SE mode. Aging did not significantly influence bond strength for both application modes (E&R, SE), except for AO29 and AT-treated dentin, where bond strengths decrea sed significantly using G2B in SE mode. In general, G2B reached significantly higher bond strengths on air-abraded/polished dentin in E&R mode than in SE mode. CONCLUSION: Air-abrasion/polishing did not impair dentin bond strength using G2B, except when dentin was air abraded with AO29 and using G2B in SE mode. Air polishing positively influenced the bond strength to dentin in specific groups. CLINICAL SIGNIFICANCE: APA is safe concerning bonding to dentin. The E&R application mode is preferred using G2B as adhesive on air-abraded/polished dentin. Air polishing with BG positively influenced dentin bond strength for both application methods.

Adhesion of tooth fragment after trauma: effect of adhesion strategy and storage in the rescue box.

This study aims to investigate the impact of storage conditions for crown fragments (specifically, whether they were stored within a tooth rescue box or in tap water) on their adhesion to fractured teeth when subjected to two different adhesive systems (namely, total etch and self etch). Sixty maxillary premolars were sectioned to obtain tooth fragments. These fragments were stored briefly (2 hours) and reattached in the following groups: Group 1 (fragments stored in tooth rescue box and reattached with etch and rinse (E&R) technique), Group 2 (fragments stored in tap water and reattached with E&R technique), Group 3 (fragments stored in tooth rescue box and reattached with self-etch (SE) technique), and Group 4 (fragments stored in tap water and reattached SE technique). After reattachment, the bonded tooth fragments underwent thermal cycling (500 cycles, 5-55 °C) and bond strength testing using a universal testing machine. Two-way Analysis of Variance (ANOVA) and Tukey's tests were used for bond strength comparison (p ≤ 0.05). A two-parameter Weibull distribution was conducted to evaluate the reliability of the storage medium and adhesion modality on bond strength. The results showed that measured shear bond values (MPa ± Standard deviation (SD); arranged in descending order) for each group were: Group 2 (Tap water/E&R = 6.5 ± 2.1), Group 1 (Rescue box/E&R = 6.0 ± 2.5), Group 4 (Tap water/E&R = 5.1 ± 2.8), and Group 3 (Rescue box/SE = 3.6 ± 3.2). Significant differences were found only between Groups 2 and 3 (p = 0.002). In conclusion, storing crown fragments in a tooth rescue box did not significantly affect the shear bond strength of the restored tooth. However, fragments reattached using the self-etch technique showed comparable shear bond strength but a higher rate of adhesive failures compared to the E&R technique.

Effect of sodium hypochlorite, ethylenediaminetetraacetic acid, and dual-rinse irrigation on dentin adhesion using an etch-and-rinse or self-etch approach.

The aim was to investigate the influence of endodontic irrigation solutions and protocols on the micro-tensile bond strength (µTBS) to dentin using an etch-and-rinse (ER) or self-etch (SE) adhesive approach. Eighty extracted human molars were ground to dentin. After pretreating for 27 min (21 min-3 min-3 min) with five different endodontic irrigation protocols (Group 1: NaOCl-EDTA-NaOCl; Group 2: NaOCl-NaOCl-EDTA; Group 3: NaOCl-NaCl-NaOCl; Group 4: Dual Rinse-Dual Rinse-Dual Rinse; Group 5: NaCl-NaCl-NaCl), an ER (Optibond FL, Kerr) or a SE (Clearfil SE Bond, Kuraray) adhesive system was applied. After light-curing, composite build-ups were made and cut into dentin-composite sticks. µTBS and failure modes were analyzed. Nonparametric statistical analyses (α = 0.05) were performed for comparison of the five groups within each type of adhesive as well as between the two adhesive systems used. The use of an ER instead of a SE adhesive system resulted in significantly higher µTBS for all irrigation protocols except for group 1 (NaOCl-EDTA-NaOCl) and 2 (NaOCl-NaOCl-EDTA). A statistical difference between the five different endodontic irrigation protocols was only found within the SE adhesive group, where group 1 (NaOCl-EDTA-NaOCl) achieved highest values. The use of an ER adhesive system cancels out the effect of the endodontic irrigation solution. The highest µTBS was achieved when using a NaOCl-EDTA-NaOCl-irrigation protocol in combination with Clearfil SE Bond, which shows that the selection of the endodontic irrigation should match the corresponding SE adhesive system.

Effects of Nd:YAG laser irradiation at different energy densities on dentin bond durability under simulated pulpal pressure.

OBJECTIVES: To evaluate the effects of Nd:YAG laser irradiation on the microstructures of dentin surfaces and the long-term bond strength of dentin under simulated pulpal pressure. MATERIALS AND METHODS: Under simulated pulp pressure, 30 freshly extracted caries-free third molars were cut into 2-mm-thick dentin samples and then divided into five groups: the control and laser groups (93.3 J/cm2; 124.4 J/cm2; 155.5 J/cm2; 186.6 J/cm2). Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), and Vickers hardness were used to analyze the surface morphology, composition, and mechanical properties of the dentin before and after laser irradiation. Another 80 caries-free third molars were removed and treated as described above, and the resin was bonded to the dentin surface with Single Bond Universal (SBU) adhesive in self-etch mode to make stick specimens. Microtensile bond strength (µTBS), confocal laser scanning microscopy (CLSM), and interfacial silver nanoleakage tests before and after 10,000 times thermocycling were then performed to analyze the bonding properties and interfacial durability of each group. RESULTS: SEM observations revealed that the surfaces of all laser group specimens were rough with open dentin tubules. Laser irradiation altered the surface composition of dentin while removing some collagen fibers but did not affect its surface hardness or crystallographic characteristics. Furthermore, laser irradiation with an energy density of 124.4 J/cm2 significantly promoted the immediate and aging bond strengths and reduced nanoleakage compared to those of the control group. CONCLUSIONS: Under simulated pulp pressure, Nd:YAG laser pretreatment altered the chemical composition of dentin and improved the immediate and long-term bond strength. CLINICAL RELEVANCE: This study investigated the optimal parameters for Nd:YAG laser pretreatment of dentin, which has potential as a clinical method to strengthen bonding.

Effects of different surface treatments on surface topography and bond strength in the repair of fiber-reinforced dentin composite.

OBJECTIVE: This study aimed to evaluate the effects of different surface treatments on the repair bond strength between a fiber-reinforced dentin composite and a posterior composite. METHODS: Forty fiber-reinforced dentin composite resin blocks (4 mm × 4 mm × 4 mm) were separated into eight groups (n = 5) according to the surface preparation methods: (G1) negative control group, (G2) adhesive application, (G3) 50% dimethylsulfoxide (DMSO) application, (G4) 50% DMSO + adhesive application, (G5) 37% phosphoric acid etch + adhesive application, (G6) air abrasion + adhesive application, (G7) 37% phosphoric acid etch + 50% DMSO application + adhesive application, and (G8) air abrasion +50% DMSO application + adhesive application group. The composite surfaces were repaired in two layers with a posterior composite. Composite sticks were subjected to a micro tensile bond strength (µTBS) test. Fractured surfaces were evaluated using a stereomicroscope (×25). Short fiber-reinforced composite samples' surfaces were investigated by scanning electron microscope (SEM). Shapiro Wilk, one-way ANOVA, and Tukey HSD tests were used for statistical evaluation. RESULTS: The highest average (µTBS) values were observed in G8, whereas the lowest mean µTBS values were evident in the G1 group. Statistically significant µTBS values were found in all adhesive-applied groups when compared with the negative control group. Notably, the application of 50% DMSO without adhesive did not lead to a statistically significant increase in µTBS values. SEM images demonstrated that acid etching partially eliminated residues on the composite surface, while air abrasion had a detrimental effect on the integrity of fiber structures. CONCLUSION: In the repair of fiber-reinforced dentin composite with a posterior composite, adhesive application is an effective approach. The treatment of 50% DMSO without adhesive did not confer a statistically significant advantage, and the supplemental use of acid etch or air abrasion did not show an additional benefit compared to adhesive-only repairs. CLINICAL SIGNIFICANCE: Adhesive application emerges as a potent and effective strategy for the repair of bur-roughened fiber-reinforced dentin composites. With its limitations, the study highlights the efficacy of adhesive-only repairs without the necessity for additional surface treatments.