Eucalyptus Concoction Mediated Synthesis of Gold Nanoparticles and Its Bioactive Role Explored via Antimicrobial and Cytotoxic Studies.

Biosynthesis of nanoparticles has now become a novel trend in addressing some of the environmental issues by adopting eco-friendly approaches in manoeuvring nanoparticles for various applications. Plants and micro-organisms have been the potential sources of the biological mode of synthesizing nanoparticles as part of their bioremediation process. This principle has been harnessed for synthesizing nanoparticles either extra or intracellularly. In this line of phyto-mediated synthesis, eucalyptus buds have been used for synthesizing gold nanoparticles (Au NPs) under optimized laboratory conditions. The UV-visible spectrum of the Au NPs showed typical surface plasmon resonance at 550 nm (λmax) with a crystalline phase measuring <100 nm in size and monodispersed as revealed from XRD, FESEM, and AFM analyses. The biological role of phytochemical concoction in reducing and stabilizing the Au NPs was clearly identified from FT-IR studies. The antimicrobial effect of the Au NPs against clinically important pathogens viz. Staphylococcus sp., Pseudomonas sp., Bacillus sp. and E. coli determined using the disk diffusion method showed no significant antibacterial effect at all concentrations. Cytotoxicity studies were carried using Vero and HEp-2 cell lines and the 50% inhibition concentration (IC50) was determined to be 1.25 mg and 0.625 mg/mL respectively. Au NPs with potential antimicrobial and anti-proliferative effects could found profound implications in the field of nanomedicine once the toxicity in vivo has been investigated.

Synthesis of Iron Oxide@Pt Core-Shell Nanoparticles for Reductive Conversion of Cr(VI) to Cr(III) and Antibacterial Studies.

Herein, we report the facile synthesis of Iron oxide@Pt core-shell nanoparticles (NPs) by facile two step synthesis process. The first step follows the growth of iron oxide nanoparticle by thermal decomposition process while the second step deals with the formation of iron oxide@Pt core-shell nanoparticles by the chemical reduction method. The synthesized core-shell nanoparticles were characterized by several techniques and used for the catalytic reductive translation of Cr(VI) to Cr(III) in the presence of formic acid by a UV-vis spectrophotometer. The UV photo-spectrometer analysis confirmed the conversion efficiency from 12% to as high as 98.8% at the end of 30 minutes. Thus, the presence of Iron oxide @Pt core-shell nanoparticles (NPs) can be effectively used as a catalyst for the reducion of Cr(VI) to Cr(III) ions. Additionally, antibacterial studies were performed for the prepared core-shell nanoparticles against two bacterial strains, i.e., gram (+ve) Staphylococcus Aureus (S. Aureus) and gram (-ve) Escherichia Coli (E. Coli).

Fabrication and characterization of porous scaffolds for bone replacements using gum tragacanth.

The practice of bone implants is the standard procedure for the treatment of skeletal fissures, or to substitute and re-establish lost bone. A perfect scaffold ought to be made of biomaterials that duplicate the structure and properties of natural bone. However, the production of living tissue constructs that are architecturally, functionally and mechanically comparable to natural bone is the major challenge in the treatment and regeneration of bone tissue in orthopaedics and in dentistry. In this work, we have employed a polymeric replication method to fabricate hydroxyapatite (HAP) scaffolds using gum tragacanth (GT) as a natural binder. GT is a natural gum collected from the dried sap of several species of Middle Eastern legumes of the genus Astragalus, possessing antibacterial and wound healing properties. The synthesized porous HAP scaffolds were analyzed structurally and characterized for their phase purity and mechanical properties. The biocompatibility of the porous HAP scaffold was confirmed by seeding the scaffold with Vero cells, and its bioactivity assessed by immersing the scaffold in simulated body fluid (SBF). Our characterization data showed that the biocompatible porous HAP scaffolds were composed of highly interconnecting pores with compressive strength ranging from 0.036 MPa to 2.954 MPa, comparable to that of spongy bone. These can be prepared in a controlled manner by using an appropriate binder concentration and sintering temperature. These HAP scaffolds have properties consistent with normal bone and should be further developed for potential application in bone implants.