RESUMEN
The influence of various process parameters on the deep drawing process is a current research topic in sheet metal forming technology. Starting from the application of the previously constructed original testing device, an original tribological model was developed based on the process of sheet metal strip sliding between flat contact surfaces under variable pressures. A complex experiment was executed using an Al alloy sheet, tool contact surfaces of different roughness, two types of lubricants and variable contact pressures. The procedure included analytically pre-defined contact pressure functions based on which, for each of the mentioned conditions, the dependencies of the drawing forces and friction coefficients were obtained. The pressure in function P1 constantly decreased from a high initial value until the minimum, while in function P3 the pressure increased until the minimum value at the halfway point of the stroke, after which it increased up to the initial value. On the other hand, the pressure in function P2 constantly increased from the initial minimum value until the maximum value, while in function P4 the pressure increased until reaching the maximum value at the halfway point of the stroke, after which it decreased to the minimum value. This enabled the determination of the influence of tribological factors on the process parameters of intensity of traction (deformation force) and coefficient of friction. The pressure functions starting with decreasing trends produced higher values for the traction forces and the friction coefficient. In addition, it was established that the roughness of the contact surfaces of the tool, especially those with titanium nitride coating, has a significant influence on the process parameters. For surfaces of lower roughness (polished), a tendency of the Al thin sheet to form a glued-on layer was noticed. This was especially prominent for lubrication with MoS2-based grease under conditions of high contact pressure (functions P1 and P4 at the beginning of the contact).
RESUMEN
Hard-facing as a type of the coating depositing is increasingly used today. Physical-chemical-metallurgical characteristics of contact layers in tribo-mechanical systems depend on the operating conditions and the conditions under which the work surfaces were created. That is the reason the influence of the processing procedures and regime, used in the contact surfaces formation, on development of the wear process of contact elements, is being considered ever more. To determine the influence of the hard-facing technology on characteristics of the gears' working surfaces, the experimental investigations were performed on samples hard-faced on the steel for cementation, by varying the filler metals (FM) and the hard-facing regimes. The samples tested were hard-faced by five "hard" and three "soft" filler metals. Experimental investigations included measuring the hard-faced layers' hardness and determination of their microstructure, as well as the wear resistance in the laboratory conditions, on tribometer and on a specially designed device for tests in the real operating conditions of gears. The wear intensity was monitored by the wear trace's width in the laboratory conditions and by the share of the teeth surfaces affected by the destructive pitting in the operating conditions. The results obtained were compared to results of the base metal (BM) tests, which provided the certain conclusions on which filler metal and which welding procedure are the optimal ones for regeneration of the worn teeth surfaces.
RESUMEN
Two aspects of various steels' weldability are considered in this article. The theoretical part presents general concepts related to steel's weldability and the application of the most important methods for its determination. In the experimental section, results of the hard-facing application to several samples are presented, and consist of hardness measurements in the different zones of the welded samples, with the evaluation of those zones' microstructures. The tested materials included two carbon steels and two alloyed steels, with hard-facing layers deposited by various filler metals. Experimental results were compared to results obtained by calculations; using both, authors were able to conclude which combination of filler metal, welding procedure and, if necessary, heat treatment, would achieve the optimal improvement of weldability in welding/hard-facing of each of the tested base metals.
RESUMEN
Numerous phenomena that occur during the process of machine parts' regeneration have a significant impact on the loss of their working ability. Therefore, the properties of the working surfaces of the teeth flanks of repaired gears were analyzed in this research. The hereditary properties of the gear teeth are expressed by the interdependence of their geometric and physical-mechanical-metallurgical parameters created during the technological operations of regeneration of worn teeth by welding/hard-facing. The hard-facing was executed with three filler metal types, namely: combination Inox 18/8/6 + EDur 600, Castolin 2 and UTP 670. The tested properties included geometrical accuracy, microstructure and microhardness. Evaluation of the executed regeneration procedures was done by comparing the mentioned parameters of the regenerated gears and the new ones. The tested gears were not withdrawn from production due to damage, but they were newly manufactured and intentionally damaged gears, made of the same materials, subjected to the same manufacturing process. In this way, all influences except for the considered filler metal type were eliminated. Based on results of the conducted experiments, it was possible to establish the influence of the filler metal type on the surface characteristics of the regenerated gears' teeth flanks.
RESUMEN
This paper presents the results of voluminous experimental investigations conducted to analyze the influence of the welding procedure on the performance of regenerated gears. Cylindrical spur gears were tested, both newly manufactured and regenerated, in two fundamentally different ways: by hard facing (surfacing) with the "hard" filler metal (DUR 600-IG) and with the "soft" filler metal (EVB2CrMo) with subsequent cementation and quenching. The regeneration procedures were defined and executed, while, subsequently, the microstructure and microhardness of the hard-faced layers were established and measured, followed by checking the durability of the hard-faced teeth flanks. Finally, techno-economic analysis was performed to establish the rationality of the conducted regenerations, i.e., the costs of regenerated and newly manufactured teeth were compared. Based on the results of the conducted investigations, it was possible to establish the influence of the welding type on the performance characteristics (primarily the service life) of the regenerated gears. For individual reparatory hard facing, the procedure with the "hard" filler metal exhibited better characteristics, while for batch reparation of numerous damaged gears, the reparation with the "soft" filler metal, followed by cementation and heat treatment, might be more convenient.