RESUMEN
We investigate the magnetic interlayer coupling and domain structure of ultra-thin ferromagnetic (FM) cobalt (Co) layers embedded between a graphene (G) layer and a platinum (Pt) layer on a silicon carbide (SiC) substrate (G/Co/Pt on SiC). Experimentally, a combination of x-ray photoemission electron microscopy with x-ray magnetic circular dichroism has been carried out at the Co L-edge. Furthermore, structural and chemical properties of the system have been investigated using low energy electron diffraction (LEED) and x-ray photoelectron spectroscopy (XPS).In situLEED patterns revealed the crystalline structure of each layer within the system. Moreover, XPS confirmed the presence of quasi-freestanding graphene, the absence of cobalt silicide, and the appearance of two silicon carbide surface components due to Pt intercalation. Thus, the Pt-layer effectively functions as a diffusion barrier. The magnetic structure of the system was unaffected by the substrate's step structure. Furthermore, numerous vortices and anti-vortices were found in all samples, distributed all over the surfaces, indicating Dzyaloshinskii-Moriya interaction. Only regions with a locally increased Co-layer thickness showed no vortices. Moreover, unlike in similar systems, the magnetization was predominantly in-plane, so no perpendicular magnetic anisotropy was found.
RESUMEN
We report on a study of the Co intercalation process underneath the [Formula: see text] R30° reconstructed 6H-SiC(0001) surface for Co film-thicknesses in a range of 0.4-12 nm using a combination of surface sensitive imaging, diffractive, and spectroscopic methods. In situ photoemission electron microscopy reveals a dependence of the intercalation temperature on the Co film-thickness. Using low energy electron diffraction and photoemission spectroscopy (XPS), we find that the SiC surface reconstruction is partially lifted and transformed. We show that the [Formula: see text] R30° reconstruction does not prevent silicide formation for Co film-thicknesses ≥0.4 nm according to XPS and x-ray absorption spectra. Our results indicate that the silicide formation is self-limited to a thin interface region and is followed by Co intercalation between graphene and silicide. Furthermore, we analyze the magnetic properties using x-ray magnetic circular dichroism at the Co L-edge. In-plane magnetization is observed for all analyzed film-thicknesses. For ultra-thin Co films, self-assembled magnetic wires with a width of the order of 100 nm form at the step-edges.
RESUMEN
An ultra-high vacuum compatible multipurpose chamber for magneto-optical reflection and transmission experiments with polarization analysis on magnetic systems is introduced. It is applicable in a broad photon energy range from the visible to the soft x-ray regime and for a wide angular range from grazing to normal incidence. It exploits a novel magnetization device based on rotating permanent magnets, which generates tuneable magnetic fields up to 570 mT in longitudinal, transverse and polar geometry. The unique combination of these features enables the feasibility of all typical magneto-optical spectroscopy techniques as T-MOKE, L-MOKE, P-MOKE, x-ray magneto optical linear dichroism, x-ray magnetic circular dichroism in reflection and Kerr polarization-spectroscopy, which is demonstrated for Co with focus on the Co 3p edges.