RESUMEN
Discoloration of non-vital teeth is an esthetic deficiency frequently requiring bleaching treatment. The purpose of this study was to evaluate in vitro the cervical base efficacy in order to prevent or to minimize the leakage along the root canal filling and into the dentinal tubules. Thirty-eight extracted single-root human teeth were used, which were biomechanically prepared, filled, and divided into three experimental groups: G1, a cervical base was applied (3 mm of thickness) below the cemento-enamel junction, with resin-modified glass-ionomer cement (Vitremer); G2, the base was done with glass-ionomer cement (Vidrion R); and G3 (Control), did not receive any material as base. A mixture of sodium perborate and hydrogen peroxide 30% was placed inside the pulp chamber for 3 days, and the access opening was sealed with Cimpat. This procedure was repeated thrice. Soon after this, a paste of calcium hydroxide was inserted into the pulp chamber for 14 days. All teeth were covered with two layers of sticky wax, except the access opening, and immersed in blue India Ink for 5 days. The results did not show statistically significant differences between the three groups concerning the leakage inside the dentinal tubules. Regarding the apical direction, a statistical difference (ANOVA P < 0.05) was observed among the experimental group G1 and control group G3. No statistically significant difference was observed between G2 and G3 groups. Therefore, the placement of a cervical base before internal bleaching procedures is still recommended.
Asunto(s)
Filtración Dental/prevención & control , Permeabilidad de la Dentina/efectos de los fármacos , Materiales de Obturación del Conducto Radicular/uso terapéutico , Blanqueamiento de Dientes/métodos , Cuello del Diente/efectos de los fármacos , Decoloración de Dientes/terapia , Análisis de Varianza , Boratos/uso terapéutico , Hidróxido de Calcio/uso terapéutico , Cementos Dentales/uso terapéutico , Cavidad Pulpar/efectos de los fármacos , Cementos de Ionómero Vítreo/uso terapéutico , Humanos , Peróxido de Hidrógeno/uso terapéutico , Técnicas In Vitro , Cementos de Resina/uso terapéutico , Tratamiento del Conducto Radicular/efectos adversos , Decoloración de Dientes/etiología , Diente no Vital/terapiaRESUMEN
O objetivo deste estudo foi avaliar o assentamento dos componentes protéticos do tipo Gold UCLA à plataforma do implante e UCLA em teflon fundidos em liga de níquel-crômio-titânio. Foram utilizados 10 componentes protéticos do tipo UCLA calcináveis, com hexágono, distribuídos em dois grupos. O grupo "T", de cinco UCLA foi fundido em titânio CP e o outro, grupo "N", de cinco, em níquel-crômio-titânio-molibdênio. Para o grupo controle, foram utilizados cinco intermediários Gold UCLA. Uma plataforma em aço inoxidável de forma poligonal de dois centímetros de altura recebeu, em seu centro, um implante de 3,75mm de diâmetro e 8mm de comprimento (da marca 3i Implant Innovations). Este estudo avaliou, com o auxílio de um Microscópio Comparador Olympus, as discrepâncias de assentamento dos componentes protéticos. Os dados numéricos foram submetidos à Análise de Variância (p<5) em parcelas subdivididas. De acordo com os resultados obtidos, pode-se concluir que o grupo fundido com níquel-crômio-titânio-molibdênio mostrou-se com melhores resultados de assentamento ao implante do que o grupo fundido com titânio CP, porém ambos foram inferiores ao grupo controle Gold UCLA
Asunto(s)
Aleaciones Dentales , Aleaciones de Oro , Implantes Dentales , TitanioRESUMEN
A finalidade deste estudo foi de avaliar as propriedades mecânicas de duas resinas compostas Charisma (Heraeus Kulzer, Alemanha) e Permalute (Ultradent Products Inc.) e verificar a influência da adição de uma fibra (Ribbond, Ribbond Inc.) na resistência à flexão das duas resinas. Foram preparados 52 corpos-de-prova num dispositivo de aço inoxidável com base retangular, sobre a qual é parafusada uma placa também em aço inoxidável com nove espaços usinados medindo 15mm de comprimento, 2mm de largura e 1mm de espessura, sobre os quais se aplicou as resinas compostas associadas ou não a fibras. Os corpos-de-prova foram divididos em quatro grupos (n=13), sendo o Grupo I somente de resina composta Charisma; Grupo II resina Charisma + Ribbond; Grupo III somente de resina Permalute e Grupo IV de resina Permalute + Ribbond. As amostras foram submetidas ao ensaio de compressão de três pontos para verificar a resisência flexural em um aparelho MTS-810 até à ruptura das mesmas e então avaliadas sob microscopia eletrônica de varredura. Os dados foram submetidos aos testes paramétricos 1-way ANOVA, análise de variância e de Comparação Múltipla de Tukey (5 por cento), após o teste de homogeneidade de variância, teste de Levene, sob nível de significância de 5 por cento. As amostras do Grupo I obtiveram média de 164,71 MPa (d.p. = 21,49 por cento); para o Grupo II, a média de ruptura foi de 292,28 MPa (d.p. = 34,24 por cento); para o Grupo III a média foi de 106,50 MPa (d.p. = 24,02 por cento) e para o Grupo IV os valores médios foram 61,70 MPa (d.p. = 24,92 por cento). Os resultados demonstram que a adição de fibras entrelaçadas aumentou consideravelmente a resistência à flexão, sendo melhor para Charisma + Ribbond do que Permalute + Ribbond. Entretanto, pela análise da região fraturada empregando-se o M.E.V., concluimos que não ocorreu reação química entre as resinas compostas e as fibras, embora não apresente completa separação entre a matriz e as fibras