Adhesive Performance of Pit and Fissure Sealants on Deproteinized Enamel with Different Proteolytic Agents: In Vitro Study.

The objective of this work was to assess the efficacy of different proteolytic agents on the bond strength of pit and fissure sealants to bovine enamel. Eighty-four bovine enamel specimens were randomly assigned in groups according to the pit and fissure sealant applied (HelioSeal F or Dyad Flow). Then, the specimens were subdivided according to the proteolytic agent used (n = 7): Group 1, distilled water (control); Group 2, 10 wt.% Tergazyme®; Group 3, 10 wt.% ZYME®; Group 4, 10% papain gel; Group 5, 10% bromelain gel; and Group 6, 5.25 wt.% sodium hypochlorite. The cell viability of the proteolytic solutions was assessed through the MTT assay. The proteolytic agents were applied on the enamel surface prior to the acid-etching procedure; then, the pit and fissure sealants were placed. The micro-shear bond strength was evaluated after 24 h or 6 months of water storing at 37 °C. Representative SEM images were taken for each experimental group. The bond strength data were statistically analyzed by a three-way ANOVA test using a significance level of α = 0.05. Bromelain and papain proteolytic solutions did not exert any cytotoxic effect on the human dental pulp cells. After 24 h and 6 months of aging, for both pit and fissure sealants, sodium hypochlorite, papain, bromelain, and Tergazyme® achieved statistically significant higher bond strength values (p < 0.05). Irrespective of the deproteinizing agent used, Dyad Flow resulted in a better bond strength after 6 months of aging. The type 1 etching pattern was identified for sodium hypochlorite, papain, and bromelain. Tergazyme®, papain, and bromelain demonstrated efficacy in deproteinizing enamel surfaces prior to acid etching, leading to the improved bond strength of pit and fissure sealants. Clinically, this suggests that these proteolytic agents can be considered viable alternatives to traditional methods for enhancing sealant retention and longevity. Utilizing these agents in dental practice could potentially reduce sealant failures.

Enhanced Antibacterial Properties of Titanium Surfaces through Diversified Ion Plating with Silver Atom Deposition.

In this study, we investigate the antibacterial effect of silver atoms implanted into a thin surface layer of titanium at low energies using an alternative ion plating technology called Diversified Ion Plating. Silver atoms were incorporated into titanium samples using reactive low-voltage ion plating at 2 keV and 4 keV. Surface modifications and morphology were evaluated using wettability, profilometry measurements, and energy-dispersive spectroscopy. For a precise determination of the quantity and depth of implanted silver atoms on titanium surfaces, a combination of experimental techniques such as Rutherford Backscattering Spectrometry along with Monte Carlo simulations were utilized. To assess the antibacterial effects of the silver atoms incorporated into pure titanium surfaces, bacterial suspension immersion tests were performed with a standard strain of Staphylococcus aureus (ATCC 12600). The outcomes indicate that titanium surfaces implanted with silver atoms were more effective in inhibiting the growth of Staphylococcus aureus than pure titanium surfaces. Better results were found when the deposition was performed at 4 keV, indicating that a deeper implantation of silver, spanning a few nanometers, can result in a longer and more effective release of silver atoms. These findings suggest the potential for the development of new, cost-effective biomaterials, paving the way for improved implant materials in various health-related applications.

In situ study of the effect of endogenous and exogenous agents on color stability, hardness, and surface roughness of an elastomer for facial prostheses.

PURPOSE: To evaluate in situ the influence of sweat, oil, sunscreen, and disinfectant solution on the color stability, hardness, and roughness of elastomer for facial prostheses. MATERIALS AND METHODS: Standardized and intrinsically pigmented specimens remained in contact with human skin from the same person for 30 days, considering exposures (n = 36 per group), absent of exposition (Control, C); sweat and oiliness contact (SO); sweat and oiliness associated with sunscreen (SOS); 0.12% chlorhexidine digluconate immersion (CD0.12%); and all agents exposed (SOSCD). The main variables were color change (CIELab and National Standard Bureau system, NBS), Shore A hardness, and surface roughness, measured at baseline and 30 days. Qualitative analyses were performed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The data were analyzed by Kruskal-Wallis tests (color) and two-way ANOVA (hardness and roughness) with Sidak post-test (α = 0.05). RESULTS: CD0.12% (1.54 ± 0.49) and SOSCD (2.10 ± 1.03) had similar effects and caused the smallest color changes, considered mild and noticeable (NBS), respectively. SOS promoted the greatest color change (6.99 ± 1.43, NBS: large) and hardness (17.97 ± 0.56); SOS promoted intermediate roughness (3.48 ± 1.05) between SOSCD (2.25 ± 0.53), and two similar groups: C (4.46 ± 0.95), and CD0.12% (4.39 ± 1.26). The qualitative analysis showed an irregular, dense, dry, and whitish layer on the surface of the specimens exposed to sunscreen, which was reduced when in contact with 0.12% chlorhexidine digluconate. CONCLUSIONS: Endogenous and exogenous factors are capable of altering elastomer properties. The 0.12% chlorhexidine digluconate minimized the changes caused by sweat, oil, and sunscreen.

Evaluation of Antimicrobial Properties, Cell Viability, and Metalloproteinase Activity of Bioceramic Endodontic Materials Used in Vital Pulp Therapy.

This study aimed to evaluate the antimicrobial properties, cell viability, and matrix metalloproteinase (MMP) inhibition capacity of several endodontic materials aimed at vital pulp therapy: Pro Root MTA®, EndoSequence®, Biodentine®, MTA Angelus®, TheraCal LC®, and BioC Repair®. The materials were prepared according to the manufacturer's instructions. Antimicrobial tests were conducted using a microcosm biofilm model, cell viability was assessed using murine fibroblasts (L929), and MMP activity was analyzed through electrophoresis. The results showed that BioC Repair®, Biodentine®, and EndoSequence® exhibited similar antimicrobial properties, while MTA Angelus® and ProRoot MTA® had inferior results but were comparable to each other. In terms of cell viability, no significant differences were observed among the materials. EndoSequence® demonstrated the highest MMP inhibition capacity. In conclusion, BioC Repair®, Biodentine®, EndoSequence®, and TheraCal® showed better antimicrobial properties among the tested materials. The materials did not exhibit significant differences in terms of cytotoxicity. However, EndoSequence® displayed superior MMP inhibition capacity.

In vitro characterization of a novel resin-based restorative material containing alkaline fillers.

OBJECTIVE: In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials-a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)-were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity. METHODOLOGY: The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal-Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests. RESULTS: Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity. Conclusion: The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.

In vitro characterization of a novel resin-based restorative material containing alkaline fillers

Abstract Objective: In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials—a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)—were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity. Methodology: The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal-Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests. Results: Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity. Conclusion: The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.

Estabilidad dimensional de hidrocoloides irreversibles de vaciado convencional y de vaciado de tiempo extendido disponibles en el mercado uruguayo

Objetivo. Comparar la estabilidad dimensional de un hidrocoloide irreversible de vaciado convencional con hidrocoloides irreversibles de vaciado extendido. Metodología. Fueron evaluados cuatro productos con indicación de vaciado extendido: Jeltrate Plus (Denstply Sirona), Hydrogum 5 (Zhermack SpA), Algimax (Major), Kromopan (Lascod) y un producto de vaciado convencional (Tropicalgin; Zhermack SpA). Con cada producto se realizaron 10 impresiones y se vaciaron en yeso tipo III en cinco tiempos de almacenamiento diferentes (0, 24, 96, 120 y 168 horas). Un escáner para modelos tridimensionales se utilizó para digitalizar los modelos de yeso y realizar las mediciones correspondientes: sumatoria de las longitudes, variabilidad dimensional, porcentaje de variabilidad. Resultados. Las cinco marcas comerciales presentaron una sumatoria de longitudes mayor al grupo control (p<0,033). A las 0, 24 y 96h Tropicalgin e Hydrogum 5 presentaron significativamente menor variación dimensional en comparación con el modelo maestro (p<0,001). Los porcentajes de variabilidad oscilaron entre un 0.24 a 0.91%. Conclusiones. La estabilidad dimensional depende del producto utilizado. Almacenado correctamente, el hidrocoloide irreversible de vaciado convencional parece no sufrir alteraciones significativas hasta 96h, mientras que en el caso de Hydrogum 5 parece mantener su estabilidad dimensional hasta 168h.

Objetivo. Comparar a estabilidade dimensional de um hidrocolóide irreversível de vazamento convencional com hidrocolóides irreversíveis de vazamento prolongado. Metodologia. Foram avaliados quatro produtos com indicação de vazamento estendido: Jeltrate Plus (Denstply Sirona), Hydrogum 5 (Zhermack SpA), Algimax (Major), Kromopan (Lascod) e um produto de vaziamento convencional (Tropicalgin; Zhermack SpA). Para cada produto foram feitas 10 impressões e vazadas em gesso tipo III em cinco tempos de armazenamento diferentes (0, 24, 96, 120 e 168 horas). Um scanner de modelos tridimensionais foi utilizado para digitalizar os modelos de gesso e fazer as medições correspondentes: soma dos comprimentos, variabilidade dimensional, percentagem de variabilidade. Resultados. As cinco marcas comerciais apresentaram somatório de comprimentos maior que o grupo controle (p<0,033). Nos tempos 0, 24 e 96h Tropicalgin e Hydrogum 5 apresentaram variação dimensional significativamente menor em comparação ao modelo Mestre (p<0,001). Os percentuais de variabilidade variaram de 0,24 a 0,91%. Conclusões. A estabilidade dimensional depende do produto utilizado. Armazenado corretamente, o hidrocolóide irreversível de vaziamento convencional convencionalmente parece não sofrer alterações significativas até 96h, enquanto no caso do Hydrogum 5 parece manter sua estabilidade dimensional até 168h.

Aim . Compare the dimensional stability of a conventional pouring irreversible hydrocolloid with extended pouring irreversible hydrocolloids. Methodology. Four products with extended emptying indication were evaluated: Jeltrate Plus (Denstply Sirona), Hydrogum 5 (Zhermack SpA), Algimax (Major), Kromopan (Lascod) and a conventional emptying product (Tropicalgin; Zhermack SpA). For each product, 10 impressions were made and cast in type III plaster at five different storage times (0, 24, 96, 120 and 168 hours). A three-dimensional model scanner was used to digitize the plaster models and make the corresponding measurements: sum of lengths, dimensional variability, percentage of variability. Results . The five commercial brands presented a greater sum of lengths than the control group (p<0,033). At 0, 24 and 96h Tropicalgin and Hydrogum 5 presented significantly less dimensional variation compared to the master model (p<0,001). The variability percentages ranged from 0.24 to 0.91%. Conclusions. Dimensional stability depends on the product used. Stored correctly, the conventionally cast irreversible hydrocolloid appears not to undergo significant alterations up to 96h, while in the case of Hydrogum 5 it appears to maintain its dimensional stability up to 168h.

Development of Lead-Free Radiation Shielding Material Utilizing Barium Sulfate and Magnesium Oxide as Fillers in Addition Cure Liquid Silicone Rubber.

The radiological protection has the purpose of safeguarding the physical well-being of the user, preventing exposure to detrimental levels of ionizing radiation. This study introduces a novel, cost-effective category of lead-free elastomeric material designed for radiation shielding. The filler compounds utilized are notably lighter than conventional lead-based materials, enhancing user ergonomics during application. They comprise of a blend of barium sulfate combined or not with magnesium oxide with addition-cure liquid silicone rubber. To ensure the effectiveness of the radiation shielding, X-ray transmission measurements were performed for the different thicknesses of the materials and the results compared with Monte Carlo simulations. Additionally, the physical properties of the new materials, such as density, homogeneity, tensile strength, viscosity, and wettability, were also evaluated. The findings indicate that both materials fulfill the requirement for application in radiation protection garments.

Antibacterial activity and physicochemical properties of a sealer containing copaiba oil.

This study aimed to evaluate the antimicrobial activity and physicochemical properties of a novel dual-cure endodontic sealer containing copaiba oil. The copaiba oil was obtained and characterized by gas chromatography (GC), and the minimum inhibitory concentration (MIC) was performed. The experimental sealers were formulated with copaiba oil concentrations of 0, 0.5, 1, and 2%, and the RealSeal™ (Sybron endo, Orange, USA) and AH Plus (Dentsply De Trey Gmbh, Konstanz, Germany) were used as the commercial references. The antimicrobial activity of the sealers was evaluated by the direct contact test for 1h and 24h. To evaluate the physicochemical properties of the sealers, the degree of conversion, setting time, film thickness, dimensional stability, and radiopacity tests were performed. The data were statistically analyzed by one-way ANOVA and Tukey's test (α = 0.05). Concerning the results, the sealers containing copaiba oil showed antimicrobial activity without harming the physicochemical properties.

Resistencia de unión al cizallamiento de diferentes agentes de fijación a aleaciones metálicas odontológicas / Shear bond strength of different bonding agents to dental metal alloys

Introducción: La fijación de las restauraciones indirectas es uno de los pasos más importantes, para conseguir una adecuada retención y sellado de la interfase entre el material restaurador y el diente. Objetivo: Evaluar la resistencia de unión al cizallamiento de diferentes agentes de fijación a dos aleaciones metálicas utilizadas en odontología. Métodos: Estudio experimental in vitro. Cien especímenes de aleaciones de metales base, 50 de níquel-cromo y 50 de níquel-cromo-titanio fueron preparados y divididos de manera aleatoria en 5 grupos. Esta división se realizó acorde con el agente de fijación utilizado: sistema autograbante de dos pasos (Clearfil SE Bond; CSB), sistema adhesivo universal (Single Bond Universal; SBU), cemento resinoso autoadhesivo (Maxcem Elite; ME), ionómero de vidrio (IV) y fosfato de zinc (ZnPO). Posteriormente a la aplicación de cada agente de fijación, los especímenes tratados fueron almacenados en agua destilada por 24 h a 37 ºC y sometidos a un ensayo de resistencia de unión al cizallamiento. Resultados: La resistencia de unión al cizallamiento fue influenciada significativamente por el tipo de agente de fijación (p = 0,002) y el tipo de aleación utilizada (p < 0,001). La resistencia de unión al cizallamiento fue mayor, al utilizar el sistema Clearfil SE Bond, seguida de Single Bond Universal; las diferencias entre Maxcem Elite y el Fosfato de zinc no fueron significativas. Finalmente, el IV no mostró adhesión a ninguna de las aleaciones metálicas utilizadas. Conclusiones: El uso de Clearfil SE Bond aumentó la resistencia de unión de los cementos resinosos a las aleaciones metálicas(AU)

Introduction: The bonding of indirect restorations is one of the most important steps, in order to achieve adequate retention and sealing of the interface between the restorative material and the tooth. Objective: To evaluate the shear bond strength of different bonding agents to two metal alloys used in dentistry. Methods: In vitro experimental study. One hundred specimens of base metal alloys, 50 nickel-chromium and 50 nickel-chromium-titanium were prepared and randomly divided into 5 groups. This division was made according to the bonding agent used: two-step self-etching system (Clearfil SE Bond; CSB), universal adhesive system (Single Bond Universal; SBU), self-adhesive resin cement (Maxcem Elite; ME), glass ionomer (IV) and zinc phosphate (ZnPO). After the application of each bonding agent, the treated specimens were stored in distilled water for 24 hr at 37 ºC and subjected to a shear bond strength test. Results: Shear bond strength was significantly influenced by the type of bonding agent (p = 0.002) and the type of alloy used (p < 0.001). Shear bond strength was highest when using the Clearfil SE Bond system, followed by Single Bond Universal; the differences between Maxcem Elite and Zinc Phosphate were not significant. Finally, IV did not show adhesion to any of the metal alloys used. Conclusions: The use of Clearfil SE Bond increased the bond strength of resinous cements to metallic alloys(AU)

LIGHT-CURED CALCIUM SILICATE BASED-CEMENTS AS PULP THERAPEUTIC AGENTS: A META-ANALYSIS OF CLINICAL STUDIES.

OBJECTIVES: To determine the clinical performance of light-cured calcium silicate-based cement for direct or indirect pulp capping. The research question was as follows: in teeth with deep caries lesions, does the use of resin-modified calcium silicate-containing composites improve the radiological success and prevent irreversible pulpitis and pulpal necrosis compared with other pulp-capping agents? MATERIALS AND METHODS: The following databases were screened until September 2021: PubMed, Web of Science, Scielo, Scopus, Embase, and The Cochrane Library. Randomized clinical trials reporting the clinical evaluation of a resin-modified calcium silicate material as an agent for pulp therapy were included. Meta-analysis was performed using the Rev Manager v5.4.1 software. The risk difference and 95% confidence interval of the dichotomous outcome (restoration failure or success) were calculated for comparison. RESULTS: Ten studies were considered for qualitative analysis and meta-analysis. Studies evaluating the performance of light-cured calcium silicate-based cement from 1 month to a maximum follow-up period of 36 months and comparing it with the performance of CaOH, mineral trioxide aggregate, or Biodentine were included. In the global analysis for direct pulp capping at 6-month follow-up, no statistical differences were observed between the experimental group using the light-cured calcium silicate-based cement and control group (P = .28). However, at 12-month follow-up, global analysis favored the control group (P < .001). For indirect pulp capping, at 6- and 24-month follow-ups, no statistically significant differences were observed between the experimental and control groups (P = .88; P = .21). CONCLUSIONS: Light-cured calcium silicate-based cement showed a limited clinical performance as a direct pulp capping agent, especially when evaluated in the long term. However, using it as an indirect pulp capping agent may be a reliable and easy-to-use option for restoring teeth with deep caries. CLINICAL SIGNIFICANCE: This systematic review provides evidence that supports the use of light-cured calcium silicate-based cement as an indirect pulp capping agent.

Self-Report of the perception of stress and signs of bruxism generated during the pandemic in student of the health area / Autoinforme de la percepción de estrés y signos de bruxismo derivados de la pandemia en estudiantes del área de la salud

Abstract Bruxism is the repetitive muscle-mandibular behavior characterized by clenching and/or grinding of the teeth, which reflects the presence of one or more underlying conditions or factors. The objective of this descriptive study was to determine the association between bruxism and stress self-perceived during the pandemic, as well as their frequency by gender and academic area. An interrogation and self-perceived stress scale PSS-14 were applied to students from the different areas of the Institute of Health Sciences (ICSa) to determine the presence or absence of stress and bruxism symptom, a Chi-square was used for the comparison between variables, considering a value of p0.005. ICSa students between 18 and 24 age perceive symptoms of bruxism and high levels of stress caused during the pandemic.

Resumen El bruxismo es el comportamiento músculo-mandibular repetitivo caracterizado por apretamiento y/o rechinamiento de los dientes, que refleja la presencia de una o varias condiciones o factores subyacentes. Se realizó un estudio descriptivo con el objetivo de determinar la asociación del nivel de estrés y síntomas de bruxismo autopercibidos durante la pandemia, así como su frecuencia por género y área académica. Se aplicó un interrogatorio y escala de estrés percibido PSS-14 a los estudiantes de las distintas áreas del Instituto de Ciencias de la Salud (ICSa) para determinar la presencia o ausencia de estrés y síntomas de bruxismo, se utilizó una Chi-cuadrada para la comparación entre variables, considerando significativo un valor de p0.0001. Los estudiantes de 18 a 24 años de edad del ICSa perciben síntomas de bruxismo y altos niveles de estrés originados durante la pandemia.

Development of functional fillers as a self-healing system for dental resin composite.

OBJECTIVES: To evaluate the incorporation of repairing capsules containing different monomers and polymerization modulators on the self-healing efficiency of an experimental photopolymerizable resin-based composite. METHODS: Self-healing capsules containing different monomers and polymerization modulators were prepared by emulsion polymerization: TCDHEPT (TEGDMA and DHEPT), BTCDHEPT (Bis-GMA, TEGDMA, and DHEPT), and BTCBPO (Bis-GMA, TEGDMA, and BPO). The capsules were analyzed through Fourier transform infrared spectroscopy and scanning electron microscopy. The capsules were added into experimental photopolymerizable resin composites establishing the following groups: ER (Control without capsules), ER+BPO, ER+BPO+TCDHEPT, and ER+BTCBPO+BTCDHEPT. Filtek Z350 resin composite (3 M ESPE) was used as a commercial reference. The materials were tested for degree of conversion (DC), flexural strength (σf), elastic modulus (Ef), fracture toughness (virgin KIC), self-healing efficiency (healed KIC), and roughness. For statistical analysis, the significance value was established at an a = 0.05 level. RESULTS: When compared to the control material, the incorporation of repairing capsules did not affect DC, σf, and Ef. Fracture toughness was statistically similar between the experimental groups (p ≤ 0.05). Healed KIC was statistically different between the groups ER+TCDHEP and ER+BTCBPO+BTCDHEPT; the self-healing efficiency was higher for ER+TCDHEPT. Surface roughness was statistically similar among all groups. CONCLUSIONS: The use of self-healing capsules promoted repair of the material. Studies with material aging after the self-healing process are necessary to better demonstrate the effectiveness of this system. CLINICAL SIGNIFICANCE: The self-healing system seemed to be a promising technology to be used in self-repaired restorative materials, which may prevent restoration fractures.

Effect of Different Desensitizers on Shear Bond Strength of Self-Adhesive Resin Cements to Dentin.

The sealing and bonding characteristics of luting cements may be affected by the application of desensitizers containing ingredients that induce chemical interaction with dentin organic matrix. This study evaluated the effect of different desensitizers on the immediate and long-term shear bond strength (SBS) of a self-adhesive resin cement (SARC) to dentin. Healthy bovine dentin specimens were used for the study. Gluma® Desensitizer, Desensibilize Nano P®, and Soothe® desensitizer were used in study groups, while the control group did not receive any treatment. Next, SARC (RelyXTM U200) in cylindrical mold was applied to the sample surface. All specimens were stored at 37 °C for 24 h or six months and tested for SBS. Additionally, water contact angle was measured using an optical tensiometer. Results were analyzed by analysis of variance and Student-t tests (p ˂ 0.05). Application of the different types of desensitizers had no significant influence on immediate or long-term SBS of SARC to dentin (p > 0.05). Differences for water contact angle were not statistically significant among the tested groups (p = 0.450). Within the limitations of the present study, it can be concluded that the application of the different types of desensitizers had no significant influence on the SBS of a SARC to dentin.

Effect of alpha-humulene incorporation on the properties of experimental light-cured periodontal dressings.

The objective of this study was to formulate an experimental light-cured periodontal dressing containing alpha-humulene and to compare its physical, antimicrobial, and cytotoxicity properties with commercial gold standards (Barricaid® and Periobond®). Two periodontal dressing formulations were developed (a and b). The formulations were divided into 5 groups according to the alpha-humulene concentration as follows: Ea - control group, Ea1 - 1%, Ea5 - 5%, Ea10 - 10%, and Ea20 - 20%; Eb - control group, Eb1 - 1%, Eb5 - 5%, Eb10 - 10%, and Eb20 - 20%. Materials characterization was performed using the degree of conversion, cohesive strength, sorption, and solubility assays. Antimicrobial assay was performed using the modified direct contact test against E. faecalis and S. aureus. Cytotoxicity was assessed by the cell viability experiment using L929 fibroblasts. In general, the cohesive strength values of materials decreased as the alpha-humulene concentration increased. All the experimental dressings showed antimicrobial activity against both bacteria tested. Cell viability results for the Ea, Ea1, Eb, and Eb1 groups showed moderate cytotoxic effect. The formulations containing alpha-humulene showed similar behavior to the commercial references. Thus, formulations containing alpha-humulene have potential to be used as periodontal dressing.

Evaluation of irradiance and radiant exposure on the polymerization and mechanical properties of a resin composite.

The objective of the present study was to evaluate the effect of irradiance and radiant exposure on the chemical-mechanical properties of a resin composite. A micro-hybrid resin composite (Clearfil AP-X, Kuraray) was investigated under two different irradiances: low (300 mW/cm2) and high (800 mW/cm2) and radiant exposures: 8 and 16 J/cm2. Four groups, named Low 8 J/cm2, High 8 J/cm2, Low 16 J/cm2, and High 16 J/cm2 were tested, and their flexural strengths, elastic moduli, depths of cure, and degrees of conversion were evaluated. Data were analyzed using two-way ANOVA and Tukey's test. A multiple linear regression model was used to correlate the irradiance and radiant exposure with dependent variables (α = 0.05). Irradiance and radiant exposure were found statistically significant for all dependent variables. The interaction between the factors was statistically significant only for the degree of conversion and elastic modulus. Group Low 16 J/cm2 exhibited a significantly superior performance in all the evaluated properties. Barring the degree of conversion, no significant differences were observed among the properties evaluated between the Low 8 J/cm2 and High 8 J/cm2 groups. The adjusted R2 values were high for the depth of cure and degree of conversion (0.58 and 0.96, respectively). Both irradiance and radiant exposure parameters play an important role in establishing the final properties of a micro-hybrid resin composite. Irradiance has a greater influence under higher radiant exposures.

Novel polymethyl methacrylate modified with metal methacrylate monomers: biological, physicomechanical, and optical properties.

This study sought to evaluate the physical and antimicrobial properties of a thermopolymerizable acrylic resin (PMMA) modified with metallic methacrylate monomers -zirconia (ZM), tin (TM), and di-n-butyl (DNTMB) methacrylates. Color stability was evaluated before and after immersion of samples in a staining solution by a digital spectrophotometer. The mechanical brushing test was evaluated by the roughness test. The flexural strength test used a mechanical testing machine. Human keratinocytes were used to assess cell viability and the biofilm formation assay was carried out for 5 days, in a microcosms model after one year of specimen storage. For statistical analysis, the method chosen was based on adherence to the normal distribution model and equality of variances (p < 0.05). The addition of DNTMB to PMMA promoted great antimicrobial action, acceptable cytocompatibility, without hampering the physical-mechanical properties of the commercial material. Therefore, the modified PMMA proved to be a promisor alternative to conventional resins.This study sought to evaluate the physical and antimicrobial properties of a thermopolymerizable acrylic resin (PMMA) modified with metallic methacrylate monomers -zirconia (ZM), tin (TM), and di-n-butyldimethacrylate-tin (DNTMB) methacrylates. Color stability was evaluated before and after immersion of samples in a staining solution using a digital spectrophotometer. The mechanical brushing test was evaluated by the roughness test. The flexural strength test used a mechanical testing machine. Human keratinocytes were used to assess cell viability and the biofilm formation assay was carried out for 5 days in a microcosm model after one year of specimen storage. For statistical analysis, the method chosen was based on adherence to the normal distribution model and equality of variances (p < 0.05). The addition of DNTMB to PMMA promoted great antimicrobial action, acceptable cytocompatibility, without hampering the physical-mechanical properties of the commercial material. Therefore, the modified PMMA proved to be a promising alternative to conventional denture base resins for dental use.

A multi-country survey on the impact of COVID-19 on dental practice and dentists' feelings in Latin America.

BACKGROUND: The COVID-19 pandemic has significantly influenced the routine of healthcare workers. This study investigated the impact of the pandemic on dental practice and dentists' feelings in Latin America. METHODS: A survey was conducted with dentists from 11 Spanish-speaking Latin American countries in September-December 2020. Professionals were invited by email and via an open campaign promoted on social media. The questions investigated dental care routines, practice changes, and feelings about the pandemic. Descriptive statistics were used to identify frequencies and distributions of variables. Proportions were compared using chi-square tests. RESULTS: A total of 2127 responses were collected from a sample with diverse demographic, sex, work, and education characteristics. The impact of COVID-19 was considered high/very high by 60% of respondents. The volume of patients assisted weekly was lower compared with the pre-pandemic period (mean reduction = 14 ± 15 patients). A high rate of fear to contracting the COVID-19 at work was observed (85%); 4.9% of participants had a positive COVID-19 test. The main professional challenges faced by respondents were reduction in the number of patients or financial gain (35%), fear of contracting COVID-19 (34%), and burden with or difficulty in purchasing new personal protective equipment (22%). The fear to contracting COVID-19 was influenced by the number of weekly appointments. A positive test by the dentists was associated with their reports of having assisted COVID-19 patients. The most cited feelings about the pandemic were uncertainty, fear, worry, anxiety, and stress. Negative feelings were more prevalent for professionals who did not receive training for COVID-19 preventive measures and those reporting higher levels of fear to contract the disease. CONCLUSION: This multi-country survey indicated a high impact of the pandemic on dental care routines in Latin America. A massive prevalence of bad feelings was associated with the pandemic.

Propiedades flexurales y estabilidad de color de materiales restauradores estéticos indirectos / Flexural properties and color stability of indirect esthetic restorative materials

Introducción: Las diferencias en las propiedades mecánicas de los materiales cerámicos y a base de resina plantean la interrogante sobre cuál puede tener un mejor desempeño a largo plazo. Objetivos: Evaluar la resistencia flexural y estabilidad de color de diferentes materiales restauradores estéticos indirectos. Métodos: Los materiales seleccionados fueron Filtek™ Z250 XT (3M ESPE), Ceramage (SHOFU Dental), VITA VM® LC y VITA ENAMIC® (VITA Zahnfabrik), IPS e.max® (Ivoclar-Vivadent) y Zolid FX (Amann Girrbach AG). El ensayo de resistencia flexural (n = 10) fue realizado en una máquina universal de ensayos mecánicos. Las lecturas de color (n = 5) se midieron en un espectrofotómetro VITA Easyshade V®. Resultados: Los materiales totalmente cerámicos mostraron un mejor desempeño mecánico (p < 0,001). Los resultados de estabilidad de color muestran que Ceramage, IPS e.max® y Zolid FX, mostraron una diferencia estadísticamente significativa (p ≤ 0,002) con Filtek Z250 XT, VITA VM® LC y VITA ENAMIC®. Conclusiones: Los materiales totalmente cerámicos presentaron una mayor resistencia flexural y estabilidad de color que los materiales de base polimérica. A pesar de ello, los materiales estéticos indirectos con polímeros en su composición, como Ceramage, se presentan como una alternativa válida, ya que además de tener propiedades mecánicas adecuadas, poseen una estabilidad de color semejante a los materiales cerámicos(AU)

Introduction: Differences in the mechanical properties of ceramic and resin-based materials pose the question of which of the two will perform better in the long run. Objectives: Evaluate the flexural resistance and color stability of different indirect esthetic restorative materials. Methods: The materials selected were Filtek™ Z250 XT (3M ESPE), Ceramage (SHOFU Dental), VITA VM® LC and VITA ENAMIC® (VITA Zahnfabrik), IPS e.max® (Ivoclar-Vivadent) and Zolid FX (Amann Girrbach AG). The flexural resistance assay (n = 10) was conducted in a universal mechanical testing machine. Color readings (n = 5) were taken with a VITA Easyshade V® spectrophotometer. Results: All-ceramic materials had better mechanical performance (p < 0.001). Color stability results show that Ceramage, IPS e.max® and Zolid FX displayed a statistically significant difference (p ≤ 0.002) with respect to Filtek Z250 XT, VITA VM® LC and VITA ENAMIC®. Conclusions: All-ceramic materials exhibited greater flexural resistance and color stability than polymer-based materials. However, indirect esthetic materials with polymers in their composition, such as Ceramage, are presented as a valid alternative, due to their appropriate mechanical properties and their color stability, which is similar to that of ceramic materials(AU)

Bond strength of self-adhesive flowable composite resins to dental tissues: A systematic review and meta-analysis of in vitro studies.

STATEMENT OF PROBLEM: Although the clinical use of self-adhesive flowable composite resins is convenient, the decision to use flowable or conventional composite resin remains controversial. PURPOSE: The purpose of this systematic review and meta-analysis was to assess the in vitro bond strength of self-adhesive flowable composite resins to enamel or dentin compared with conventional composite resins using etch-and-rinse or self-etch adhesive systems. MATERIAL AND METHODS: Two independent reviewers performed searches in the PubMed (MEDLINE), Cochrane Wiley, Web of Science, Scopus, and Google Scholar databases for studies reporting on the bond strength of self-adhesive flowable and conventional composite resins to enamel and dentin published from January 2010 up to September 2020. A meta-analysis software program was used for the meta-analysis. Comparisons were conducted using standardized mean differences considering the random-effects model (α=.05). RESULTS: Twenty-two studies were considered for the meta-analysis. Immediate and long-term bond strength to enamel was improved when a conventional composite resin was used in combination with an adhesive system (P<.001). Bond strength to dentin was improved by using an adhesive system in combination with a conventional composite resin (P<.001). CONCLUSIONS: The bond strength of self-adhesive flowable composite resins is lower than that of conventional composite resins, indicating limited ability to bond to enamel and dentin.