RESUMEN
ABSTRACT Dentin hypersensitivity (DH) is characterized by rapid, acute pain arising from exposed dental tubules. Aim: the aim of this study was to evaluate the roughness, tubule occlusion, and permeability of eroded dentin brushed with different toothpastes. Materials and Method: ninety bovine teeth were cut into blocks. Thirty hemifaces were protected with varnish and the other sixty were submitted to permeability tests. Specimens were divided into groups according to the dentifrices: without fluoride (WF), sodium fluoride (NaF), and stannous fluoride (SnF2). The blocks were subjected to a 5-day erosive-abrasive protocol. Surface roughness and dentinal tubule occlusion (n=10) were assessed for both control and test hemifaces of the same sample along with permeability analysis (n=20). Two-way RM ANOVA and Tukey's post-hoc test were performed (p≤0.05). Results: NaF and SnF2 presented higher roughness than WF. The number of open tubules was higher in WF. Permeability was higher in SnF2, but there was no significant difference between WF and NaF. Conclusions: both fluoride toothpastes occluded dentinal tubules and increased roughness. NaF toothpaste promoted greater decrease in dentin permeability.
RESUMO A hipersensibilidade dentinária (HD) é caracterizada por dor rápida e aguda decorrente de túbulos dentais expostos. Objetivo: este estudo teve como objetivo avaliar a rugosidade, oclusão tubular e permeabilidade da dentina erodida escovada com diferentes dentifrícios. Materiais e Método: noventa dentes bovinos foram seccionados em blocos. Trinta hemifaces foram protegidas com verniz e outras sessenta foram submetidas à permeabilidade. Os espécimes foram divididos em grupos de acordo com os dentifrícios: sem flúor (SF), fluoreto de sódio (NaF) e fluoreto estanoso (SnF2). Em seguida, os blocos foram submetidos a um protocolo erosivo-abrasivo de 5 dias. A rugosidade da superfície e a oclusão do túbulo dentinário (n = 10) foram avaliadas para ambas as hemifaces de controle e teste da mesma amostra, também realizou-se a análise de permeabilidade (n = 20). Two-way RM ANOVA e pós-teste de Tukey foram realizados (p≤0,05). Resultados: NaF e SnF2 apresentaram rugosidade superior ao SF. O número de túbulos abertos foi maior em SF. Não encontramos diferenças significativas entre SF e NaF em relação à permeabilidade; entretanto, SnF2 apresentou maior permeabilidade. Conclusão: ambos os dentifrícios fluoretados foram capazes de ocluir os túbulos dentinários e aumentar a rugosidade. No entanto, o dentifrício NaF promoveu uma maior diminuição da permeabilidade dentinária.
RESUMEN
Dentin hypersensitivity (DH) is characterized by rapid, acute pain arising from exposed dental tubules. AIM: the aim of this study was to evaluate the roughness, tubule occlusion, and permeability of eroded dentin brushed with different toothpastes. MATERIALS AND METHOD: ninety bovine teeth were cut into blocks. Thirty hemifaces were protected with varnish and the other sixty were submitted to permeability tests. Specimens were divided into groups according to the dentifrices: without fluoride (WF), sodium fluoride (NaF), and stannous fluoride (SnF2). The blocks were subjected to a 5-day erosive-abrasive protocol. Surface roughness and dentinal tubule occlusion (n=10) were assessed for both control and test hemifaces of the same sample along with permeability analysis (n=20). Two-way RM ANOVA and Tukey's post-hoc test were performed (p≤0.05). RESULTS: NaF and SnF2 presented higher roughness than WF. The number of open tubules was higher in WF. Permeability was higher in SnF2, but there was no significant difference between WF and NaF. CONCLUSIONS: both fluoride toothpastes occluded dentinal tubules and increased roughness. NaF toothpaste promoted greater decrease in dentin permeability.
A hipersensibilidade dentinária (HD) é caracterizada por dor rápida e aguda decorrente de túbulos dentais expostos. Objetivo: este estudo teve como objetivo avaliar a rugosidade, oclusão tubular e permeabilidade da dentina erodida escovada com diferentes dentifrícios. Materiais e Método: noventa dentes bovinos foram seccionados em blocos. Trinta hemifaces foram protegidas com verniz e outras sessenta foram submetidas à permeabilidade. Os espécimes foram divididos em grupos de acordo com os dentifrícios: sem flúor (SF), fluoreto de sódio (NaF) e fluoreto estanoso (SnF2). Em seguida, os blocos foram submetidos a um protocolo erosivo-abrasivo de 5 dias. A rugosidade da superfície e a oclusão do túbulo dentinário (n = 10) foram avaliadas para ambas as hemifaces de controle e teste da mesma amostra, também realizou-se a análise de permeabilidade (n = 20). Two-way RM ANOVA e pós-teste de Tukey foram realizados (p≤0,05). Resultados: NaF e SnF2 apresentaram rugosidade superior ao SF. O número de túbulos abertos foi maior em SF. Não encontramos diferenças significativas entre SF e NaF em relação à permeabilidade; entretanto, SnF2 apresentou maior permeabilidade. Conclusão: ambos os dentifrícios fluoretados foram capazes de ocluir os túbulos dentinários e aumentar a rugosidade. No entanto, o dentifrício NaF promoveu uma maior diminuição da permeabilidade dentinária.
Asunto(s)
Sensibilidad de la Dentina , Pastas de Dientes , Animales , Bovinos , Pastas de Dientes/farmacología , Fluoruros/farmacología , Dentina , Fluoruro de Sodio/farmacología , Permeabilidad , Permeabilidad de la DentinaRESUMEN
AIM: To synthesize, characterize and evaluate the antimicrobial and antibiofilm activities of novel nanocomposites containing silver nanoparticles (AgNPs) associated or not to ß-calcium glycerophosphate. MATERIALS & METHODS: These nanocomposites were produced through a 'green' route using extracts of different parts of pomegranate. Antimicrobial and antibiofilm properties against Candida albicans and Streptococcus mutans were determined by the minimum bactericidal/fungicidal concentration and biofilm density after treatments. RESULTS: All extracts used were successful in producing AgNPs. Composites made with peel extracts showed the highest antimicrobial and antibiofilm activity against both microorganisms tested and performed similarly or even better than chlorhexidine. CONCLUSION: AgNPs associated or not to calcium glycerophosphate produced by a 'green' process may be a promising novel antimicrobial agent against oral microorganisms.