We report the behaviour of thermoresponsive block copolymers of n-butyl acrylate and N-alkyl acrylamides in [C2mim][NTf2]. Poly(N-isopropylacrylamide) exhibits an upper critical solution temperature in [C2mim][NTf2] whereas poly(n-butyl acrylate) has a lower critical solution temperature. Consequently, these polymers exhibit double thermo-responsiveness correlated with the macromolecular structure. Moreover, a switching from micellar to reverse micellar structures was induced by a change in temperature. This property enables the development of reversible shuttles between ionic liquids and water.
RESUMEN
The synthesis of germanium nanoparticles has been carried out, thanks to the design of novel aminoiminate germanium(II) precursors: (ATI)GeZ (with Z = OMe, NPh2, and ATI = N,N'-diisopropyl-aminotroponiminate) and (Am)2Ge (Am = N,N'-bis(trimethylsilyl)phenyl amidinate). These complexes were fully characterized by spectroscopic techniques as well as single crystal X-ray diffraction. The thermolysis of both complexes yielded NPs which display similar features that are a Ge/GeO2 core/shell structure with a mean diameter close to 5 nm with a narrow size distribution (<15%). Whereas the high temperatures (>300 °C) classically reported in the literature for the preparation of germanium-based NPs were necessary for thermolysis of the complexes (ATI)GeZ, the use of amidinate-based precursors allows the preparation at an unprecedented low temperature (160 °C) for the thermolytic route. As suggested by a mechanistic study, the lower reactivity of (ATI)GeZ (for which the concomitant use of high temperature and acidic reagent is required) was explained in terms of lower ring strain compared to the case of (Am)2Ge.