RESUMEN
The evolution of local ferroelectric lattice distortions in multiferroic Ge1-x Mn x Te is studied by x-ray diffraction, x-ray absorption spectroscopy and density functional theory. We show that the anion/cation displacements smoothly decrease with increasing Mn content, thereby reducing the ferroelectric transition from 700 to 100 K at x = 0.5, where the ferromagnetic Curie temperature reaches its maximum. First principles calculations explain this quenching by different local bond contributions of the Mn 3d shell compared to the Ge 4s shell in excellent quantitative agreement with the experiments.
RESUMEN
Controlled wrinkling of single-layer graphene (1-LG) at nanometer scale was achieved by introducing monodisperse nanoparticles (NPs), with size comparable to the strain coherence length, underneath the 1-LG. Typical fingerprint of the delaminated fraction is identified as substantial contribution to the principal Raman modes of the 1-LG (G and G'). Correlation analysis of the Raman shift of the G and G' modes clearly resolved the 1-LG in contact and delaminated from the substrate, respectively. Intensity of Raman features of the delaminated 1-LG increases linearly with the amount of the wrinkles, as determined by advanced processing of atomic force microscopy data. Our study thus offers universal approach for both fine tuning and facile quantification of the graphene topography up to ~60% of wrinkling.