RESUMEN
Keratoprosthesis (KPro) implantation is frequently the only recourse for patients with severe corneal disease. However, problems arise due to inadequate biointegration of the KPro, particularly the PMMA optical cylinder, such as tissue detachment, tissue melting, or eye-threatening infection in the interface. Here, using the AuroKPro as a model prosthesis, a surface functionalization approachâcoating the optical cylinder with nanohydroxyapatite (nHAp)âwas trialed in rabbit eyes with and without a proceeding chemical injury. In chemically injured eyes, which simulated total limbal epithelial stem cell deficiency, clear benefits were conferred by the coating. The total modified Hackett-McDonald score and area of tissue apposition differences 12 weeks after implantation were 5.0 and 22.5%, respectively. Mechanical push-in tests revealed that 31.8% greater work was required to detach the tissues. These differences were less marked in uninjured eyes, which showed total score and tissue apposition differences of 2.5 and 11.5%, respectively, and a work difference of 23.5%. The improved biointegration could be contributed by the attenuated expression of fibronectin (p = 0.036), collagen 3A1 (p = 0.033), and α-smooth muscle actin (p = 0.045)âproteins typically upregulated during nonadherent fibrous capsule envelopment of bioinert materialâadjacent to the optical cylinders. The coating also appeared to induce a less immunogenic milieu in the ocular surface tissue, evidenced by the markedly lower expression of tear proteins associated with immune and stimulus responses. Collectively, the level of these tear proteins in eyes with coated prostheses was 1.1 ± 13.0% of naïve eyes: substantially lower than with noncoated KPros (246.5 ± 79.3% of naïve, p = 0.038). Together, our results indicated that nHAp coating may reduce the risk of prosthesis failure in severely injured eyes, which are representative of the cohort of KPro patients.