Formation of a U(VI)-Persulfide Complex during Environmentally Relevant Sulfidation of Iron (Oxyhydr)oxides.

Uranium is a risk-driving radionuclide in both radioactive waste disposal and contaminated land scenarios. In these environments, a range of biogeochemical processes can occur, including sulfate reduction, which can induce sulfidation of iron (oxyhydr)oxide mineral phases. During sulfidation, labile U(VI) is known to reduce to relatively immobile U(IV); however, the detailed mechanisms of the changes in U speciation during these biogeochemical reactions are poorly constrained. Here, we performed highly controlled sulfidation experiments at pH 7 and pH 9.5 on U(VI) adsorbed to ferrihydrite and investigated the system using geochemical analyses, X-ray absorption spectroscopy (XAS), and computational modeling. Analysis of the XAS data indicated the formation of a novel, transient U(VI)-persulfide complex as an intermediate species during the sulfidation reaction, concomitant with the transient release of uranium to the solution. Extended X-ray absorption fine structure (EXAFS) modeling showed that a persulfide ligand was coordinated in the equatorial plane of the uranyl moiety, and formation of this species was supported by computational modeling. The final speciation of U was nanoparticulate U(IV) uraninite, and this phase was evident at 2 days at pH 7 and 1 year at pH 9.5. Our identification of a new, labile U(VI)-persulfide species under environmentally relevant conditions may have implications for U mobility in sulfidic environments pertinent to radioactive waste disposal and contaminated land scenarios.

Formation of stable uranium(VI) colloidal nanoparticles in conditions relevant to radioactive waste disposal.

The favored pathway for disposal of higher activity radioactive wastes is via deep geological disposal. Many geological disposal facility designs include cement in their engineering design. Over the long term, interaction of groundwater with the cement and waste will form a plume of a hyperalkaline leachate (pH 10-13), and the behavior of radionuclides needs to be constrained under these extreme conditions to minimize the environmental hazard from the wastes. For uranium, a key component of many radioactive wastes, thermodynamic modeling predicts that, at high pH, U(VI) solubility will be very low (nM or lower) and controlled by equilibrium with solid phase alkali and alkaline-earth uranates. However, the formation of U(VI) colloids could potentially enhance the mobility of U(VI) under these conditions, and characterizing the potential for formation and medium-term stability of U(VI) colloids is important in underpinning our understanding of U behavior in waste disposal. Reflecting this, we applied conventional geochemical and microscopy techniques combined with synchrotron based in situ and ex situ X-ray techniques (small-angle X-ray scattering and X-ray adsorption spectroscopy (XAS)) to characterize colloidal U(VI) nanoparticles in a synthetic cement leachate (pH > 13) containing 4.2-252 µM U(VI). The results show that in cement leachates with 42 µM U(VI), colloids formed within hours and remained stable for several years. The colloids consisted of 1.5-1.8 nm nanoparticles with a proportion forming 20-60 nm aggregates. Using XAS and electron microscopy, we were able to determine that the colloidal nanoparticles had a clarkeite (sodium-uranate)-type crystallographic structure. The presented results have clear and hitherto unrecognized implications for the mobility of U(VI) in cementitious environments, in particular those associated with the geological disposal of nuclear waste.